Waterborne matte velour-wetting treatment agent for synthetic leather and preparation method thereof

A technology of synthetic leather and treatment agent, applied in fiber processing, textiles and papermaking, etc., can solve the problems of poor hand feeling of synthetic leather, dissolution of the bottom layer of artificial leather, flammability, etc. good effect

Inactive Publication Date: 2013-05-15
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the field of synthetic leather, there are a variety of surface treatment technologies to form different surface styles, such as matte effect. It is a common method to make synthetic leather have a feel similar to genuine leather. However, the existing matte wet suede treatment agents for synthetic leather are mostly Solvent-based, which has the following disadvantages: the organic solvent in the solvent-based surface treatment agent will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather has a bad feel; The pollution is serious, and there are safety hazards such as flammability and explosion; the overall effect of treating synthetic leather is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The water-based matte surface wet velvet feeling treatment agent for synthetic leather consists of 25 parts by weight of water-based polyurethane resin varnish, 45 parts by weight of water, 1 part by weight of penetrating agent, 3 parts by weight of silica matting powder, 0.5 parts by weight of silicone leveling agent, It consists of 2 parts by weight of silicone defoamer and 0.5 part by weight of water-based polyurethane thickener.

[0025] The preparation method of the above-mentioned water-based matte surface wet suede treatment agent for synthetic leather is: 25 parts by weight of water-based polyurethane resin varnish, 3 parts by weight of silica matting powder, 1 part by weight of penetrating agent (EL-40), 2 parts by weight of organic Silicone defoamer, 0.5 parts by weight of silicone leveling agent and 45 parts by weight of water were mixed and stirred for 1 hour; the mixture obtained in the above steps was ground and filtered; finally, 0.5 parts by weight of wat...

Embodiment 2

[0028] The synthetic leather water-based matte surface wet velvet feeling treatment agent consists of 28 parts by weight of water-based polyurethane resin varnish, 50 parts by weight of water, 2 parts by weight of penetrating agent, 4 parts by weight of silica matting powder, 0.8 parts by weight of silicone leveling agent, 3 parts by weight of silicone defoamer and 1.5 parts by weight of water-based polyurethane thickener.

[0029] The preparation method of the above-mentioned synthetic leather water-based matte wet velvet treatment agent is: 28 parts by weight of water-based polyurethane resin varnish, 4 parts by weight of silica matting powder, 2 parts by weight of penetrating agent (EL-40), 3 parts by weight of organic Silicon defoamer, 0.8 parts by weight of silicone leveling agent and 50 parts by weight of water were mixed and stirred for 1.5 hours; the mixture obtained in the above steps was ground and filtered; finally, 1.5 parts by weight of water-based polyurethane thi...

Embodiment 3

[0032] The synthetic leather water-based matte surface wet velvet feeling treatment agent consists of 30 parts by weight of water-based polyurethane resin varnish, 55 parts by weight of water, 3 parts by weight of penetrating agent (EL-40), 5 parts by weight of silica matting powder, 1 part by weight of organic Silicon leveling agent, 5 parts by weight of silicone defoamer and 2 parts by weight of water-based polyurethane thickener.

[0033] The preparation method of the above-mentioned synthetic leather water-based matte wet suede treatment agent is: 30 parts by weight of water-based polyurethane resin varnish, 5 parts by weight of silica matting powder, 3 parts by weight of penetrating agent (EL-40), 5 parts by weight of organic Silicon defoamer, 1 weight part of silicone leveling agent and 55 weight parts of water were mixed and stirred for 2 hours; the mixture obtained in the above steps was ground and the resulting mixture was filtered; finally, 2 weight parts of water-bas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a waterborne matte velour-wetting treatment agent for synthetic leather. The waterborne matte velour-wetting treatment agent is composed of the following components: waterborne polyurethane resin varnish, water, penetrant, silica extinction powder, an organosilicone levelling agent, an organosilicone defoamer and a waterborne polyurethane thickener. The invention further relates to a preparation method of the waterborne matte velour-wetting treatment agent for the synthetic leather. The waterborne matte velour-wetting treatment agent for the synthetic leather has a good hand feel and a good comprehensive treatment effect and is environment-friendly; and the preparation method of the waterborne matte velour-wetting treatment agent is simple in process and dispenses with the change of production equipment and the increase of cost.

Description

technical field [0001] The invention relates to a surface treatment agent for synthetic leather, in particular to a water-based matte wet suede treatment agent for synthetic leather applied to the front-end process of synthetic leather, and to the preparation of the water-based matte wet suede treatment agent for synthetic leather method. Background technique [0002] The emergence of synthetic leather makes up for the lack of genuine leather resources, and compared with genuine leather, synthetic leather can meet people's requirements for various styles of surfaces. In the field of synthetic leather, there are a variety of surface treatment technologies to form different surface styles, such as matte effect. It is a common method to make synthetic leather feel like real leather. However, the existing matte wet suede treatment agents for synthetic leather are mostly Solvent-based, which has the following disadvantages: the organic solvent in the solvent-based surface treatm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M11/79D06M13/50D06N3/14
Inventor 齐春红
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap