Elastic high-strength antistatic shoe sole material and preparation method thereof

A shoe sole material and anti-static technology, applied in the field of shoe sole materials, can solve the problems of shoe sole material elasticity decline and easy wear, and achieve the effects of reducing static electricity, preventing harm, and high tensile strength

Inactive Publication Date: 2017-10-20
HEFEI YUANKE GARMENT DESIGN CO LTD
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the soles on the market are modified to improve their antistatic properties, but the elasticity of the sole material is reduced and it is easy to wear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of elastic high-strength antistatic sole material of the present embodiment comprises the raw material of following weight portion:

[0035] 6 parts of organotin stabilizer, 7 parts of anti-slip agent, 2 parts of conductive filler, 25 parts of hydroxylated polypropylene, 50 parts of elastic filler, 4 parts of calcium carbonate, 5 parts of adhesive, 10 parts of reinforcing inorganic fiber, 1 part of antistatic agent parts, 3 parts of coupling agent, 10 parts of processing aid.

[0036] The organic tin stabilizer in this example is a mixture of dimethyl tin oxide and butyl tin sulfate in a weight ratio of 2:1.

[0037] The anti-slip agent in this embodiment is a mixture of silicon dioxide, attapulgite, and ceramic powder in a weight ratio of 2:3:5; the particle size of the anti-slip agent powder is between 100 mesh and 140 mesh.

[0038] The conductive filler in this embodiment is a mixture of carbon black, nano zinc oxide, and graphene in a weight ratio of 3:1:1;...

Embodiment 2

[0048] A kind of elastic high-strength antistatic sole material of the present embodiment comprises the raw material of following weight portion:

[0049] 10 parts of organic tin stabilizer, 9 parts of anti-slip agent, 4 parts of conductive filler, 35 parts of hydroxylated polypropylene, 60 parts of elastic filler, 8 parts of calcium carbonate, 7 parts of adhesive, 18 parts of reinforced inorganic fiber, 2 parts of antistatic agent parts, 5 parts of coupling agent, 12 parts of processing aid.

[0050] The organic tin stabilizer in this example is a mixture of dimethyl tin oxide and butyl tin sulfate in a weight ratio of 2:1.

[0051] The anti-slip agent in this embodiment is a mixture of silicon dioxide, attapulgite, and ceramic powder in a weight ratio of 2:3:5; the particle size of the anti-slip agent powder is between 100 mesh and 140 mesh.

[0052] The conductive filler in this embodiment is a mixture of carbon black, nano zinc oxide, and graphene in a weight ratio of 3:1...

Embodiment 3

[0062] A kind of elastic high-strength antistatic sole material of the present embodiment comprises the raw material of following weight portion:

[0063] 8 parts of organic tin stabilizer, 8 parts of anti-slip agent, 3 parts of conductive filler, 30 parts of hydroxylated polypropylene, 55 parts of elastic filler, 6 parts of calcium carbonate, 6 parts of adhesive, 14 parts of reinforced inorganic fiber, 1.5 parts of antistatic agent parts, 4 parts of coupling agent, 11 parts of processing aid.

[0064] The organic tin stabilizer in this example is a mixture of dimethyl tin oxide and butyl tin sulfate in a weight ratio of 2:1.

[0065] The anti-slip agent in this embodiment is a mixture of silicon dioxide, attapulgite, and ceramic powder in a weight ratio of 2:3:5; the particle size of the anti-slip agent powder is between 100 mesh and 140 mesh.

[0066] The conductive filler in this embodiment is a mixture of carbon black, nano zinc oxide, and graphene in a weight ratio of 3:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an elastic high-strength antistatic shoe sole material, which comprises the following raw materials in parts by weight: 6-10 parts of organotin stabilizer, 7-9 parts of anti-slip agent, 2-4 parts of conductive filler, and 25-35 parts of hydroxylated polypropylene 50-60 parts of elastic filler, 4-8 parts of calcium carbonate, 5-7 parts of binder, 10-18 parts of reinforced inorganic fiber, 1-2 parts of antistatic agent, 3-5 parts of coupling agent, processing aid Dose 10-12 parts. The sole material of the present invention has good elasticity and mechanical strength, good anti-slip effect, excellent antistatic performance, excellent heat resistance, weather resistance and impact resistance; meanwhile, the raw material components of the present invention are safe and reliable, and have no pollution to the environment, and the raw material It is easy to obtain, low in cost, simple in process, low-carbon, environmentally friendly and pollution-free, and has high practical value and good application prospect.

Description

technical field [0001] The invention relates to the technical field of shoe sole materials, in particular to an elastic high-strength antistatic shoe sole material and a preparation method thereof. Background technique [0002] Shoes are an essential item for people to travel. There are a wide variety of shoes for various people to choose from. People have different requirements for shoes, but anti-skid performance is a common requirement of people, because on snow-covered roads On slippery roads and rainy days, it is easy to fall when wearing non-slip shoes, and some people will fall because of this, especially the elderly and children are more likely to fall. The phenomenon of slipping occurs because the friction between the road surface and the sole is reduced to a minimum. The current anti-slip method is usually to suppress the texture on the sole, but the texture will be smoothed after wearing for a period of time, and the anti-skid effect is still not achieved. In add...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L23/26C08L23/08C08K13/06C08K3/36C08K3/34C08K3/04C08K7/10C08K7/14C08K5/526A43B13/04
CPCC08L75/04A43B13/04C08K2201/001C08K2201/011C08K2201/014C08L2201/02C08L2201/04C08L2201/08C08L2205/035
Inventor 张力
Owner HEFEI YUANKE GARMENT DESIGN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap