Preparation of nanometer graphene oxide modified cotton fibers and antibiosis product thereof

A technology of modified cotton and graphene, applied in fiber treatment, plant fiber, inorganic chemistry, etc., can solve the problem of weak killing effect, achieve good safety, excellent washing resistance and air permeability, broad-spectrum and high-efficiency antibacterial properties Effect

Inactive Publication Date: 2013-07-17
SUZHOU ZHENGYECHANG INTELLIGENT TECH
View PDF0 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Graphene oxide is less effective at killing Gram-negative bacteria due to the protection of the outer membrane in the structure of Gram-negative bacteria

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The preparation of a kind of nano-graphene oxide modified cotton fiber of the present invention and antibacterial product thereof is characterized in that the preparation method comprises the following steps:

[0014] (1) Add 20g of 50-mesh graphite powder, 10g of potassium persulfate and 10g of phosphorus pentoxide into concentrated sulfuric acid at 80°C, stir evenly, cool for 10h, wash until neutral, and dry. Add the dried sample to 230mL of concentrated sulfuric acid at 0°C, and then add 60g of potassium permanganate. The temperature of the mixture was kept at 10 °C, and after keeping in an oil bath at 30 °C for 2 h, 920 mL of deionized water was slowly added. After 10 minutes, add 2.8 L of deionized water (which contains 50 mL of 30% hydrogen peroxide), after which the color of the mixture turns bright yellow, and it is suction filtered while it is hot, and then washed with 5 L of 10% hydrochloric acid, suction filtered, Dry to obtain graphite oxide;

[0015] (2) ...

Embodiment 2

[0021] The preparation of a kind of nano-graphene oxide modified cotton fiber of the present invention and antibacterial product thereof is characterized in that the preparation method comprises the following steps:

[0022] (1) Add 20g of 50-mesh graphite powder, 10g of potassium persulfate and 10g of phosphorus pentoxide into concentrated sulfuric acid at 80°C, stir evenly, cool for 8h, wash until neutral, and dry. Add the dried sample to 230mL of concentrated sulfuric acid at 0°C, and then add 60g of potassium permanganate. The temperature of the mixture was kept at 20°C, and after being kept in an oil bath at 35°C for 3 h, 920 mL of deionized water was slowly added. After 20 minutes, add 2.8 L of deionized water (which contains 50 mL of 30% hydrogen peroxide), after which the color of the mixture turns bright yellow, and it is suction filtered while it is hot, and then washed with 5 L of 10% hydrochloric acid, suction filtered, Dry to obtain graphite oxide;

[0023] (2) ...

Embodiment 3

[0029] The preparation of a kind of nano-graphene oxide modified cotton fiber of the present invention and antibacterial product thereof is characterized in that the preparation method comprises the following steps:

[0030] (1) Add 20g of 50-mesh graphite powder, 10g of potassium persulfate and 10g of phosphorus pentoxide into concentrated sulfuric acid at 80°C, stir evenly, cool for 12h, wash until neutral, and dry. Add the dried sample to 230mL of concentrated sulfuric acid at 0°C, and then add 60g of potassium permanganate. The temperature of the mixture was kept at 20 °C, and after keeping in an oil bath at 40 °C for 3 h, 920 mL of deionized water was added slowly. After 20 minutes, add 2.8 L of deionized water (which contains 50 mL of 30% hydrogen peroxide), after which the color of the mixture turns bright yellow, and it is suction filtered while it is hot, and then washed with 5 L of 10% hydrochloric acid, suction filtered, Dry to obtain graphite oxide;

[0031] (2) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to preparation of nanometer graphene oxide modified cotton fibers and an antibiosis product thereof, wherein the preparation comprises that: (1) graphite oxide is prepared; (2) the graphite oxide and a cross-linking agent are put in a beaker, deionized water is added, and ultrasonic processing is performed to obtain a uniformly dispersed graphene oxide solution; and (3) preparation of an antibiosis product adopts a two dipping and two rolling technology. The nanometer graphene oxide modified cotton fibers and the antibiosis product thereof have characteristics of simple preparation, low cost, good security, broad-spectrum and high efficiency antibacterial property, excellent launderability and excellent permeability.

Description

technical field [0001] The invention belongs to the field of textiles, and in particular relates to a nanometer graphene oxide modified cotton fiber and the preparation of antibacterial products thereof. Background technique [0002] Although natural cotton products have the advantages of wearing comfort, reproducibility and biodegradability, but in the process of wearing, due to the large specific surface area and strong moisture absorption capacity of cotton fibers, cotton products are very easy to attach microorganisms and Create conditions for its reproduction and propagation, resulting in damage to fiber strength, stains and discoloration, unpleasant odors, and even the spread of diseases, affecting human health. Therefore, in the research of cotton fiber modification, an important research direction is to realize the antibacterial properties of cotton fiber and reduce the invasion of bacteria on the human body. [0003] There are usually two methods for the developmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/74D06M13/123D06M13/11C01B31/04D06M101/06C01B32/198
Inventor 赵兵
Owner SUZHOU ZHENGYECHANG INTELLIGENT TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com