Copper-based catalyst for synthesis of methanol in slurry bed, preparation method and application thereof

A copper-based catalyst, a technology for synthesizing methanol, applied in physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, chemical instruments and methods, etc., to achieve a wide selection range, enhanced synergy, and improved activity Effect

Inactive Publication Date: 2013-07-31
SHANXI LUAN ENVIRONMENTAL ENERGY DEV +1
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently, completely avoid the generation of Cu 2 (NO 3 )(OH) 3 The preparation method of the phase has not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] (1) Weigh 77.31g Cu(NO 3 ) 2 3H 2 O, 47.60g Zn (NO 3 ) 2 6H 2 O, 7.50g Al(NO 3 ) 3 9H 2 O, placed in a 250ml beaker, after adding distilled water to fully dissolve, constant volume with a 500ml volumetric flask, to prepare a mixed metal salt solution with a total metal ion concentration of 1.0 mol / L.

[0046] (2) Weigh 53.00g Na 2 CO 3 Put it in a 250ml beaker, add distilled water to fully dissolve it, and then use a 500ml volumetric flask to make up a 1.0 mol / L precipitant solution.

[0047] (3) Add 400ml metal salt solution to the anode pool, and add 480ml precipitant solution to the cathode pool at the same time, adjust the speed of both pools to 120 r / min, turn on the heating switch, and heat to 70°C.

[0048] (4) Turn on the electric field switch, adjust the electric field voltage U=20V, Cu 2+ , Zn 2+ 、Al 3+ Under the action of an external electric field, it moves directionally and passes through the Nafion cation exchange membrane of DuPont Comp...

Embodiment 2

[0052] (1) Weigh 77.31g Cu(NO 3 ) 2 3H 2 O, 47.60g Zn(NO 3 ) 2 6H 2 O, 7.50g Al(NO 3 ) 3 9H 2 O, put it in a 500ml beaker, add distilled water to fully dissolve it, then use a 1000ml volumetric flask to constant volume, and prepare a 0.5 mol / L mixed metal salt solution.

[0053] (2) Weigh 53.00g Na 2 CO 3 Put it in a 500ml beaker, add distilled water to fully dissolve it, and then use a 1000ml volumetric flask to make up a 0.5 mol / L precipitant solution.

[0054] (3) Add 800ml metal salt solution to the anode pool, and add 960ml precipitant solution to the cathode pool at the same time, adjust the speed of both pools to 120 r / min, turn on the heating switch, and heat to 70°C.

[0055] (4) Turn on the electric field switch, adjust the electric field voltage U=40V, Cu 2+ , Zn 2+ 、Al 3+ Under the action of an external electric field, it moves directionally and passes through the Nafion cation exchange membrane of DuPont Company of the United States to generate ...

Embodiment 3

[0059] (1) Weigh 54.36g Cu(NO 3 ) 2 3H 2 O, 66.94g Zn (NO 3 ) 2 6H 2 O, 18.76g Al(NO 3 ) 3 9H 2 O, placed in a 250ml beaker, after adding distilled water to fully dissolve, constant volume with a 500ml volumetric flask, to prepare a mixed metal salt solution with a total metal ion concentration of 1.0 mol / L.

[0060] (2) Weigh 53.00g Na 2 CO 3 Put it in a 250ml beaker, add distilled water to fully dissolve it, and then use a 500ml volumetric flask to make up a 1.0 mol / L precipitant solution.

[0061] (3) Add 500ml metal salt solution to the anode pool, and add 500ml precipitant solution to the cathode pool at the same time, adjust the speed of both pools to 120 r / min, turn on the heating switch, and heat to 60°C.

[0062] (4) Turn on the electric field switch, adjust the electric field voltage U=80V, Cu 2+ , Zn 2+ 、Al 3+ Under the action of an external electric field, it moves directionally and passes through the Nafion cation exchange membrane of DuPont Com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a copper-based catalyst for synthesis of methanol in a slurry bed. The catalyst is characterized in that it is composed of active component CuO, ZnO and a carrier. Specifically, the catalyst consists of 30.0-70.0wt% of CuO, 10.0-50.0wt% of ZnO, and 5.0-20.0wt% of the carrier. The catalyst provided in the invention has the advantages of high activity, good stability and long life.

Description

technical field [0001] The invention belongs to a catalyst, a preparation method and an application, and in particular relates to a slurry bed synthesis gas methanol copper-based catalyst, a preparation method and an application. Background technique [0002] Coal gasification to methanol is one of the effective ways for efficient and clean utilization of coal. The traditional industrial production of methanol adopts a fixed-bed reaction process, which has disadvantages such as difficult temperature control, large gas circulation ratio, low single-pass conversion rate, and poor economic efficiency. Chemical Systems Inc. of the United States proposed the gas-liquid-solid three-phase slurry bed methanol synthesis process (LPMeOH) in 1975, which has the advantages of uniform reaction temperature and easy control, high single-pass conversion rate of CO, high energy utilization rate and low cost. It is especially suitable for synthesizing methanol from CO-rich coal gasification ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/80C07C31/04C07C29/154
CPCY02P20/52
Inventor 郑华艳李忠武爱莲杨浩孟凡会
Owner SHANXI LUAN ENVIRONMENTAL ENERGY DEV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com