Black table tennis racket inverted rubber composition with high viscosity and high elasticity

A table tennis racket, high-viscosity technology, applied in the field of rubber products and sports equipment manufacturing, can solve problems such as prolonging the service cycle, and achieve the effects of high manufacturing rotation efficiency, health protection, performance and appearance balance

Inactive Publication Date: 2013-08-14
BEIJING RES & DESIGN INST OF RUBBER IND
View PDF3 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention achieves high viscosity and high elasticity that can be maintained for a long time through the special rubber product composition independently developed to ensure that there is no bloomi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: a kind of black high-viscosity high-elasticity table tennis racket anti-adhesive rubber composition, its composition is made up of the material of following mass fraction: 80 parts of natural rubber; 20 parts of butadiene rubber; 2 parts of antioxidant 264; 10 parts of wear-resistant carbon black; 5 parts of zinc carbonate; 1 part of stearic acid; 1 part of 2-mercaptobenzothiazole; 0.7 parts of diphenylguanidine; 0.3 parts of tetramethylthiuram disulfide; 3 parts of insoluble sulfur ; 10 parts of liquid butadiene rubber.

Embodiment 2

[0029] Embodiment 2: a kind of black high-viscosity high-elasticity table tennis racket anti-adhesive rubber composition, its composition is made up of the material of following mass fraction: 60 parts of natural rubber; 40 parts of butadiene rubber; 2 parts of antioxidant 264; 5 parts of wear-resistant carbon black; 10 parts of zinc oxide; 2 parts of stearic acid; 2 parts of 2,2'-dithiodibenzothiazole; 0.8 part of diphenylguanidine; 0.2 part of tetramethylthiuram disulfide; 2 parts of insoluble sulfur; 30 parts of liquid butadiene rubber.

[0030] The above-mentioned embodiment adopts the black high-viscosity and high-elasticity table tennis racket anti-adhesive rubber that the rubber industry commonly used rubber mixing and vulcanization process makes, and process is simple and easy, and cost is low, and the vulcanization characteristic and physical performance of rubber are as follows:

[0031] Table 1 Comparison table of vulcanization characteristics and physical propertie...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a black table tennis racket inverted rubber composition with high viscosity and high elasticity. The composition comprises a matrix material composed of a blend of 50-100 parts by mass of a natural rubber and 0-50 parts by mass of a butadiene rubber, 1-3 parts by mass of an anti-aging agent, 1-10 parts by mass of a filler, 6-13 parts by mass of a vulcanizing activator, 1-5 parts by mass of a vulcanizing accelerator, 0.5-3.5 parts by mass of sulfur and 10-30 parts by mass of a tackifier. The composition is simple in preparation process and low in cost; the prepared table tennis racket inverted rubber has good rebound resilience and relatively high viscosity that can be kept for a long time, thereby guaranteeing fast tennis ball speed, high rotation ball-making efficiency and high control ability for the tennis balls; and at the same time, the rubber has smooth appearance without blooming phenomenon, so that the table tennis racket can be well balanced in both performance and appearance and be beneficial to athlete health.

Description

[0001] technical field [0002] The invention discloses a black anti-adhesive rubber composition for table tennis rackets with high viscosity and high elasticity. Fast return speed, strong rotation, easy to control the ball; at the same time ensure that the preparation process is simple, low cost, the surface of the rubber is smooth and flat, and there is no blooming phenomenon, so that the product has a good balance in performance and appearance, which is conducive to protecting athletes healthy. The invention relates to the technical field of manufacturing rubber products and sports equipment. technical background [0003] The anti-rubber rubber of table tennis rackets should have high resilience to ensure fast return speed. It is suitable for fast attack and fast loop ball. Generally, natural rubber is used and butadiene rubber with better elasticity is used as the base material. However, if the proportion of butadiene rubber is too large, the strength and elongation of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L9/00C08L23/20C08L9/02C08K13/02C08K3/06C08K3/26C08K3/22C08K5/09C08K3/04C08K5/13
Inventor 王雷吴文彪杨绪迎
Owner BEIJING RES & DESIGN INST OF RUBBER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap