A white topcoat and glossy technology, applied in the field of topcoat, can solve problems such as difficult to achieve deep curing, weakened UV penetration, delamination, etc., and achieve the effect of good hardness, high fullness, and good scratch resistance

Inactive Publication Date: 2013-08-28
SHANGHAI CHANGRUNFA PAINT
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen that UV paint is suitable for industrialized high-efficiency production, is developing at a high speed, and has broad market application prospects. However, because UV paint is ultraviolet light penetrating radiation curing paint, the penetration of ultraviolet light in white products is obviously weakened, and it is difficult to achieve Deep curing can easily lead to paint defects such as pinholes, delamination, and yellowing by ultraviolet light

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] The UV bright white topcoat provided by the invention, in parts by weight, comprises:

[0077] 18 parts by weight of titanium dioxide paste;

[0078] 18 parts by weight of bisphenol A epoxy acrylic resin;

[0079] 15 parts by weight of epoxy-modified acrylate;

[0080] TPGDA 15 parts by weight;

[0081] TMPDA 20 parts by weight;

[0082] 7 parts by weight of unsaturated polyester acrylate;

[0083] Dispersant 0.1 parts by weight;

[0084] 0.5 parts by weight of anti-settling agent;

[0085] 0.3 parts by weight of defoamer;

[0086] Leveling agent 0.3 parts by weight;

[0087] Photoinitiator 1173 4 parts by weight;

[0088] TPO 1.5 parts by weight;

[0089] Among them, the production process of titanium white slurry is: disperse bisphenol A epoxy acrylic resin, titanium dioxide and dispersant to a fineness of less than 30 microns, and then grind to a fineness of 10-15 microns to obtain titanium white slurry, wherein, The weight ratio of bisphenol A epoxy acryli...

Embodiment 2

[0092] The UV bright white topcoat provided by the invention, in parts by weight, comprises:

[0093] 25 parts by weight of titanium dioxide paste;

[0094] 25 parts by weight of bisphenol A epoxy acrylic resin;

[0095] 20 parts by weight of epoxy-modified acrylate;

[0096] TPGDA 20 parts by weight;

[0097] TMPDA 25 parts by weight;

[0098] 12 parts by weight of unsaturated polyester acrylate;

[0099] Dispersant 0.1 parts by weight;

[0100] 0.5 parts by weight of anti-settling agent;

[0101] 0.3 parts by weight of defoamer;

[0102] Leveling agent 0.3 parts by weight;

[0103] Photoinitiator 1173 4 parts by weight;

[0104] TPO 2 parts by weight;

[0105] Among them, the production process of titanium white slurry is: disperse bisphenol A epoxy acrylic resin, titanium dioxide and dispersant to a fineness of less than 30 microns, and then grind to a fineness of 10-15 microns to obtain titanium white slurry, wherein, The weight ratio of bisphenol A epoxy acrylic...

Embodiment 3

[0108] The UV bright white topcoat provided by the invention, in parts by weight, comprises:

[0109] 20 parts by weight of titanium dioxide paste;

[0110] 20 parts by weight of bisphenol A epoxy acrylic resin;

[0111] 15 parts by weight of epoxy-modified acrylate;

[0112] TPGDA 15 parts by weight;

[0113] TMPDA 20 parts by weight;

[0114] 10 parts by weight of unsaturated polyester acrylate;

[0115] Dispersant 0.1 parts by weight;

[0116] 0.5 parts by weight of anti-settling agent;

[0117]0.3 parts by weight of defoamer;

[0118] Leveling agent 0.3 parts by weight;

[0119] Photoinitiator 1173 4 parts by weight;

[0120] TPO 1.5 parts by weight;

[0121] Among them, the production process of titanium white slurry is: disperse bisphenol A epoxy acrylic resin, titanium dioxide and dispersant to a fineness of less than 30 microns, and then grind to a fineness of 10-15 microns to obtain titanium white slurry, wherein, The weight ratio of bisphenol A epoxy acryli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
Login to view more

Abstract

The invention provides UV (Ultraviolet) light white finish. The UV light white finish comprises titanium white pulp, bisphenol A type epoxy acrylic resin, epoxy modified acrylic ester, UV monomer, unsaturated polyester acrylic ester, auxiliaries and auxiliaries, wherein the titanium white pulp is prepared by mixing the materials including bisphenol A type epoxy acrylic resin, titanium white pulp and dispersing agent. The UV light white finish can be used for effectively avoiding pin hole and de-lamination problems, can be used for achieving deep curing and has good yellowing resistance; a formed paint film has the excellent qualities including good leveling performance, high fullness, good hardness, high color and luster, good scratching resistance, good solution resistance and high adhesion force, and is suitable for a wood plate protecting and decorative painting system including wood floors, multi-layer floors, bamboo wood floors, consolidated composite floors, furniture and the like. Moreover, the economic benefits are good and the market prospect is broad.

Description

technical field [0001] The invention relates to a finish paint, in particular to a UV bright white finish paint. Background technique [0002] UV paint is the abbreviation of Ultraviolet Curing Paint (Ultraviolet Curing Paint), also known as photoinitiated coatings, photocured coatings, after being coated on the surface of the furniture board, the initiator is decomposed under the irradiation of ultraviolet light, generating free radicals, triggering Resin reaction, instant curing into film, is currently the most environmentally friendly paint, has the following advantages: (1) UV paint film has a three-dimensional structure, high hardness, good wear resistance, good transparency, and the product is scratch-resistant and friction-resistant. Can stand the test of time; (2) Mechanized equipment overcomes the human factors in manual operation, so that the color difference of the product is small and the quality is stable; (3) During the production process, the harmful substance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D167/06C09D7/12C09D17/00
Inventor 石天竖叶谦
Owner SHANGHAI CHANGRUNFA PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap