Structure and cyclic olefin resin molded body

An olefin-based resin and structure technology, which is applied in the field of structures and cyclic olefin-based resin moldings, can solve problems such as discoloration and deformation of molded products, and achieve the effects of high transparency and improved printability.

Active Publication Date: 2013-08-28
POLYPLASTICS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is known that combustion treatment tends to cause deformation and discoloration of molded articles. Especially, cycloolefin-based resin molded articles are used in applications requiring transparency, so it is necessary to easily perform desired surface treatment by methods other than combustion treatment. technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Structure and cyclic olefin resin molded body
  • Structure and cyclic olefin resin molded body
  • Structure and cyclic olefin resin molded body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0101] Hereinafter, the present invention will be explained in further detail by enumerating examples, but the present invention is not limited to these examples.

[0102]

[0103] Cyclic olefin resin 1: Copolymer of ethylene and norbornene (manufactured by Topas Advanced Polymers, "TOPAS6013S-04", glass transition temperature: 138°C)

[0104] Cyclic olefin resin 2: Copolymer of ethylene and norbornene (manufactured by Topas Advanced Polymers. "TOPAS6015S-04", glass transition temperature: 158°C)

[0105]

[0106] Using the cyclic olefin resin 1 as a raw material, an injection molding machine was used to manufacture ISO178 bending test pieces under the conditions of a cylinder temperature of 280°C, a mold temperature of 110°C, an injection speed of 100 mm / s, and a holding pressure of 50 MPa. This test piece was used as a swelling test piece, and the mass before immersion was measured. It should be noted that the mass before immersion is taken as 100%, and the mass after immersion an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

Provided is a surface treatment technique for cyclic olefin resin molded bodies, which improves the printability of the surface of a cyclic olefin resin molded body and causes almost no problems such as discoloration that deteriorate transparency of the cyclic olefin resin molded body. Specifically provided is a structure which is provided with a cyclic olefin resin molded body that is at least partially subjected to a surface treatment and a print layer that is formed on the treated surface of the molded body. The surface treatment is carried out using a solvent that causes swelling of the cyclic olefin resin molded body. It is preferable that the solvent contains at least one substance that is selected from the group consisting of butyl acetate, methyl isobutyl ketone and liquid paraffins.

Description

Technical field [0001] The present invention relates to a structure and a cyclic olefin resin molded body. Background technique [0002] Cyclic olefin resin is a resin with a cyclic olefin skeleton in the main chain. It has high transparency, low birefringence, high heat distortion temperature, light weight, dimensional stability, low water absorption, hydrolysis resistance, and chemical resistance. A resin with many characteristics such as chemical properties, low dielectric constant, low dielectric loss, and no harmful substances to the environment. [0003] As described above, cyclic olefin-based resins are very excellent resins, and molded bodies formed by molding the resins are used in various fields. [0004] However, a printed layer may be formed on the surface of the resin molded body. For example, when the resin molded body is a container, a case where a printed layer on which information of the content is printed is formed. When forming a printed layer on a resin molded ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/02C08L45/00
CPCC08J7/02C08J2323/08
Inventor 小野寺章晃宫崎广隆
Owner POLYPLASTICS CO LTD