Environmental protection type laser transfer composite aluminium foil paper and its preparation technology

A laser transfer, environmentally friendly technology, applied in papermaking, paper coatings, textiles and papermaking, etc., can solve problems such as pollution and many processes, and achieve the effects of improving environmental performance, saving energy, and good printability

Inactive Publication Date: 2006-01-25
张学毅
View PDF0 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the current laser transfer composite aluminum foil paper has the above advantages, the transfer coating used in its production process is still solvent-based, and there are still harmful substances in the coating, and the drying volatiles in the production process also pollute the environment. The transfer coating It is composed of a release material and a protective laser layer coating with a secondary coating process, and there are relatively many processes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1， Embodiment 1

[0007] Example 1, Example 1, extract raw materials according to the following weight ratio: 1-20 parts of water-soluble amino resin, 8-12 parts of water-soluble polyurethane resin, 8-12 parts of water-soluble alkyd resin, 26 parts of water-soluble acrylic resin -30 parts, 8-12 parts of cellulose resin, 8-10 parts of additives, 0-10 parts of colorants, 26-30 parts of co-solvents, 30-80 parts of water, made into water-based by synthesis, wetting and dispersing, and blending Laser transfer coating, which is suitable for transfer and compounding of paper, cardboard, fabric, leather and other substrates.

Embodiment 2

[0008] Example 2, raw materials are extracted according to the following weight ratio: 10 parts of water-soluble amino resin, 10 parts of water-soluble polyurethane resin, 5 parts of water-soluble alkyd resin, 30 parts of water-soluble acrylic resin, 10 parts of cellulose resin, auxiliary agent 10 parts, 2-10 parts of pigment, 30 parts of co-solvent, 30-80 parts of water, after synthesis, wetting and dispersing, blending to make water-based laser transfer coating, it is suitable for paper, cardboard, fabric, leather and other substrates transfer compound.

Embodiment 3

[0009] Example 3, the laser transfer coating made in Example 1 and Example 2 is used to be coated on the surface of the carrier film, such as PET, BOPP and PA, etc., dried and crosslinked by heating (80-120°C) After curing into a film, it is molded on a laser molding machine at a temperature of 80-120°C, and then aluminum-plated in a vacuum aluminum plating machine, and then compounded with various types of paper, cardboard, fabric, leather and other substrates. After the complex is dried, the carrier film is peeled off from the complex, and the carrier film can be returned to the previous first process to continue to be used as a carrier film repeatedly. After the carrier film is peeled off, the remaining complex is an environmentally friendly laser transfer compound. Aluminum foil paper, it has a strong metallic feeling, high gloss, strong adhesion to the aluminized layer, good surface wear resistance and reprinting performance, high binding force with ink, and the printed in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates an environmental protection laser transferred composite aluminum foil paper and the preparing technique, mainly solving the problems of the environment pollution and complicated technique caused by separant coating and laser layer protection coating of the existing commonly used solvent laser transferred composite aluminum foil paper. Its mixing proportion (by weight) of the raw materials is: water soluble amino resin 1-20 (or water soluble polyurethane resin 1-30, or water soluble alcohol acid resin 1-30, or water soluble acrylate resin 1-40, or cellulose resin 1-20), assistant 1-10, pigment 0-10, auxiliary solvent 1-30, and water 30-80, or their arbitrary combination, through synthesizing and wet-dispersing to mix into a water laser transfer coating, coating the transfer coating on a carrier thin film, drying, cross-linking curing, laser-mould pressing, and aluminizing to obtain the laser composite aluminum foil paper. It has the characters of improving environmental protection performance, simplifying producing process, saving energy sources, reducing production cost, stable production quality, etc.

Description

technical field [0001] The invention relates to a laser transfer composite aluminum foil paper coating and a preparation process thereof, in particular to an environment-friendly laser transfer composite aluminum foil paper and a preparation process thereof. Background technique [0002] In the early 1980s, the transfer composite aluminum foil paper invented abroad was used as a packaging material. Because of its superior performance such as environmental protection, energy saving, and economy, it gradually replaced pure aluminum foil paper and plastic aluminized film composite aluminum foil paper. It has also been promoted in China in recent years. With the development of science and technology, laser laser molding technology is combined to transfer composite aluminum foil paper, and laser transfer composite aluminum foil paper has been developed. Although the current laser transfer composite aluminum foil paper has the above advantages, the transfer coating used in its pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/24D21H21/14D21H19/44
Inventor 张学毅
Owner 张学毅
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap