Coating process on impregnated and presseure-adheriing laminate flooring

A technology for strengthening the floor and coating process, which is applied to the surface coating liquid device, coating, polyester coating, etc., which can solve the problems of high cost, high price, and lack of layering of the pressed wood grain of the floor. Achieve the effects of reducing paint consumption, improving utilization rate, excellent visual effect and tactile feeling

Active Publication Date: 2014-06-11
JIANGSU HIMONIA TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing traditional reinforced flooring is basically made of impregnated reinforced paper and laminated with aluminum oxide-containing melamine film. However, although this type of product has good wear resistance, the pressed melamine film Relatively thin, high price, so that the laminated wood grain of the floor lacks a sense of hierarchy, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating process on impregnated and presseure-adheriing laminate flooring

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A coating process on the dipped and pressed reinforced flooring includes: dipping and pasting the reinforced base material on the reinforced floor to obtain a base material layer; coating the base material layer sequentially with UV-boil-resistant high-adhesion primer, UV -Tough sanding primer and flexible flow coat soft finish.

[0022] Components and weight proportions of the UV-high adhesion primer of the present embodiment are: 100% UV curing resin 45%; defoamer 0.1%; adhesion promoter 2.5%; dispersant 0.5% ; Thixotropic agent 0.5%; Photoinitiator 7%; Filling material 20%; The balance is monomer.

[0023] The components of the UV-flexible sanding primer of this embodiment and their weight proportions are: 100% UV curable resin 70%; defoamer 0.1%; leveling agent 0.05%; dispersant 1%; anti-settling agent 0.4%; photoinitiator 4%; filler 10%; the balance is monomer.

[0024] The components and weight proportions of the toughness flow coating soft finish paint of this ...

Embodiment 2

[0026] A coating process on the dipped and pressed reinforced flooring includes: dipping and pasting the reinforced base material on the reinforced floor to obtain a base material layer; coating the base material layer sequentially with UV-boil-resistant high-adhesion primer, UV -Tough sanding primer and flexible flow coat soft finish.

[0027] The components and weight proportions of a kind of boil-resistant UV-high adhesion primer of the present embodiment are: 100% UV curing resin 40%; defoamer 0.1%; adhesion promoter 1%; dispersant 0.5%; thixotropic agent 1%; photoinitiator 7%; filler 25%; the balance is monomer.

[0028] The components of the UV-flexible sanding primer of the present embodiment and their weight proportions are: 100% UV curable resin 75%; defoamer 0.2%; leveling agent 0.05%; dispersant 0.5%; anti-settling agent 0.5%; photoinitiator 5%; filler 5%; the balance is monomer.

[0029] The tenacity flow coating soft finish of the present embodiment is a high-gl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a coating process on impregnated and pressure-adhering laminate flooring. Since three kinds of UV (ultraviolet) coatings are adopted, work efficiency can be improved, space can be saved, emission can be reduced, surface properties of the impregnated and pressure-adhering laminate flooring by adopting the coatings can be more excellent, and the impregnated and pressure-adhering laminated flooring can be prevented from being delaminated after being boiled for three hours at the constant temperature of 70 DEG C and dried for three hours at the constant temperature of 70 DEG C. The three kinds of UV coatings refer to a UV-water-resistant high-adhesion base coating, a UV-toughness sanding base coating and a UV-flexible curtaining soft-light finishing coating. The coating process includes impregnating and pressure-adhering reinforcing base materials on laminate flooring to obtain a base material layer; coating the UV-water-resistant high-adhesion base coating, the UV-toughness sanding base coating and the UV-flexible curtaining soft-light finishing coating on the base material layer in sequence. By modifying coating formulas, the laminate flooring coated with modified coatings has good flexibility, fullness, adhesive force and comprehensive water resistance, and has special effects of moisture, soft light and glossiness. Besides, the glossiness of a coating film is above 75 degrees.

Description

technical field [0001] The invention relates to a coating process of UV coatings, in particular to a coating process on impregnated and pressed reinforced floors. Background technique [0002] UV is the English abbreviation of Ultraviolet (ultraviolet), and UV paint is ultraviolet light curing paint. The existing traditional reinforced flooring is basically made of impregnated reinforced paper and laminated with aluminum oxide-containing melamine film. However, although this type of product has good wear resistance, the pressed melamine film It is relatively thin and the price is high, so that the laminated wood grain of the floor lacks a sense of hierarchy, and the cost is high. Or some factories use UV coatings, and apply UV coatings after pressing and pasting impregnated wood grain paper on the laminate floor substrate. Many coatings can adhere well on the substrate, and the scratch resistance of coins is also good. It can be done very well, but there is almost no floor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B05D7/24C09D163/10C09D175/14C09D167/06C09D7/12
Inventor 江益新唐基红陈明贵吴志飞江科常红言
Owner JIANGSU HIMONIA TECH