Waterproof coiled material having pre-laid anti-sticking function and preparation method thereof

A waterproof roll material, pre-paved anti-adhesive technology, applied in the field of chemical materials for construction, can solve the problems that the pre-paved anti-adhesive effect cannot be achieved, and achieve a wide temperature range, high tensile strength, and good tear resistance Effect

Active Publication Date: 2013-10-23
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
View PDF4 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiency that the asphalt-based self-adhesive film-type pre-paved waterproof membrane cannot achieve a real pre-paved anti-adhesive effect in the prior art, the present invention provides a polymer waterproof membrane with a multi-layer composite structure and its manufacturing process. With pre-laid anti-adhesive function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A plastic sheet with a width of 2.0m is made by extrusion blow molding. The plastic sheet is drawn and uniformly coated on its upper surface with a layer of hot melt pressure-sensitive adhesive with a thickness of 0.35mm and a width of 1.8m. The adhesive layer The surface is sprayed with a layer of acrylic protective coating with a thickness of 0.05mm after drying, and a layer of double-sided silicon-coated isolation film is covered on the top of the coating, and finally after trimming and bending, the two edges are each left with a 10cm non-adhesive layer area. waterproof materials.

Embodiment 2

[0049] Extrusion blow molding is used to make a plastic sheet with a width of 2.0m. The plastic sheet is drawn and uniformly coated on its upper surface with a layer of hot melt pressure-sensitive adhesive with a thickness of 0.30mm and a width of 1.9m. The adhesive layer The surface is sprayed with a layer of acrylic protective coating with a thickness of 0.08mm after drying, and a layer of double-sided silicon-coated isolation film is covered on the top of the coating, and finally after trimming and bending, the two edges are each left with a 5cm non-adhesive layer area. waterproof materials.

Embodiment 3

[0051] A plastic sheet with a width of 2.0m is made by extrusion blow molding. The plastic sheet is drawn and uniformly coated on its upper surface with a layer of hot melt pressure-sensitive adhesive with a thickness of 0.45mm and a width of 1.6m. The adhesive layer The surface is sprayed with a layer of acrylic protective coating with a thickness of 0.10mm after drying, and a layer of double-sided silicon-coated isolation film is covered on the top of the coating, and finally after trimming and bending, the two edges are each left with a 20cm non-adhesive area. waterproof materials.

[0052] For the products of the above three embodiments, the coiled material is laid on the surface during construction, and the overlapping edges are constructed by hot air double seam welding. After the paving is completed, the surface PET isolation film is removed, and then the steel bars are bound on the protective coating surface, and then the concrete is poured.

[0053] After the concrete was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof coiled material having a pre-laid anti-sticking function. A preparation method comprises the steps: with a plastic sheet material as a supporter, a hot melt pressure sensitive adhesive is blade-coated on the plastic sheet material, an acrylic acid isolating protection layer is spayed on the hot melt pressure sensitive adhesive layer, and a PET silicon-coated isolating film is coated on a topside layer. The waterproof coiled material disclosed by the invention has high tensile strength and good tear resistance, is non-toxic and odorless, is wide in adaptive temperature range, can be welded or be in self-adhesive lap joint, forms a full bonding with post-poured concrete, can be directly constructed while walking on the coiled material, and is suitable for waterproof of underground waterproof engineering, such as basements, artificial lakes, culverts, tunnels, subways and the like.

Description

Technical field [0001] The invention relates to a waterproof coiled material used for waterproofing or moisture-proofing and a manufacturing process thereof, and belongs to the field of building chemical materials. Background technique [0002] The waterproof board currently used for underground waterproofing works is separated from the concrete structure after the construction is completed. Once the waterproof board is damaged, water will directly act on the concrete structure and flow between the waterproof board and the concrete structure, so as to find the leakage point in the future. Repairs cause great inconvenience. [0003] In order to solve the problem of water channeling, a pre-laid anti-adhesive construction method has been developed in this field: the waterproof membrane covered with a self-adhesive film layer is laid on the base surface, and then the structural concrete is poured to make the concrete slurry and the membrane glue The film layers are tightly combined. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/08B32B7/12
Inventor 刘志维田凤兰段文锋
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com