Ceramic glaze and preparation method thereof

A technology of ceramic glaze and fruit wood ash, which is applied in the preparation of ceramic glaze and the field of ceramic glaze to achieve the effects of simple production, expanded possibility, and convenient material acquisition

Active Publication Date: 2015-01-21
泉州德化县嘉欧利工艺品有限责任公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention proposes a ceramic glaze and a preparation method thereof, which solves or alleviates the problems mentioned above

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Adopt the disclosed content of the present invention, carry out following operation, at first, prepare lychee fruit wood ash:

[0041] (1) Collect and sort litchi fruit trees and branches and leaves, wherein the weight ratio of fruit trees and branches and leaves is 9:1;

[0042] (2) Cut the fruit trees and branches and leaves into small pieces and place them in a clear water pool, moisten the fruit trees and perform secondary sorting according to the density principle of different substances;

[0043] (3) After soaking for 2 days, pick up the fruit trees, branches and leaves and bake them in a gas oven at 160°C for 13 hours to avoid direct burning of the fruit trees by the open flame of the gas musket. Of course, they can also be placed in the sun according to the actual situation. Under the sun for 4-5 days;

[0044] (4) Put the dried fruit trees and branches and leaves into the fire pit in batches to burn. The fire pit can be a square fire pit with tiles and bricks ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides ceramic glaze. The ceramic glaze comprises the following components by weight percent: 34.8-35.3% of feldspar minerals, 5.5-6.5% of kaolin, 16.5-18.2% of quartz, 10.6-12.2% of dolomite, 5-6.3% of zinc oxide, 6.8-7.8% of titanium dioxide, 11.8-12.4% of calcium hydrophosphate, 4.4-4.7% of ferric oxide and 8.3-9.8% of fruit tree ashes. According to the ceramic glaze, natural mineral materials, which are used as solvents in the prior art, are replaced with the fruit tree ashes or reduced, so that the suspension property of the ceramic glaze can be improved, the function of presenting a crystal effect can be achieved, and the ceramic glaze is environment-friendly, and can be recycled. Besides, the invention further discloses a preparation method of the ceramic glaze.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to a ceramic glaze, and also relates to a preparation method of the ceramic glaze. Background technique [0002] In the existing ceramic firing process, the formula of ceramic glaze usually uses powder of natural minerals such as feldspar, quartz, limestone, calcium carbonate, lead as solvent or to increase the suspension of glaze. The formula is added in proportions ranging from 3% to 70%, but the use of traditional natural ores has a variety of factors that are unfavorable to long-term development and is contrary to the long-term scientific development of the industry. For example, natural minerals are non-renewable resources. Long-term large-scale mining is not conducive to the development of Changyu; at the same time, the distribution and quality of natural minerals are uneven across the country, and extensive development will also cause damage to the natural environment; if the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 蔡焕宜
Owner 泉州德化县嘉欧利工艺品有限责任公司