Hot rolling lubricant for titanium and titanium alloy strips
A technology for titanium alloy plates and lubricants, applied in the directions of lubricating compositions, additives, petroleum industry, etc., can solve the problems of reduced processing performance, easy adhesion to rolls, pollution, etc., and achieve the effects of reduced cleaning performance and good cooling.
Active Publication Date: 2013-11-27
GUANGXI UNIV
View PDF4 Cites 8 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Titanium has two remarkable characteristics in rolling: one is that its chemical properties are relatively active, so that it is easy to react with the surrounding environment during the rolling process, especially in the hot rolling process, causing pollution and reducing processing performance; Extremely sticky roll
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] The following components are blended according to mass percentage:
[0019]
[0020] The sum of the above components is 100%.
Embodiment 2
[0022] The following components are blended according to mass percentage:
[0023]
[0024] The sum of the above components is 100%.
Embodiment 3
[0026] The following components are blended according to mass percentage:
[0027]
[0028] The sum of the above components is 100%.
[0029] The following are the main physical and chemical indicators of the product of embodiment 3:
[0030] project
[0031] Flash point (opening) °C, greater than
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a hot rolling lubricant for titanium and titanium alloy strips. The lubricant uses #150 total loss oil for a system as basic oil, and is matched with a plurality of composite additives. The lubricant comprises an antiwear agent, an oiliness agent, an antioxidant preservative, an antioxygen, an anti-foaming agent, a demulsifying compound, a clearing agent, a dispersant and the like. The lubricant has cooling, lubricating and cleaning properties, and can be used for reducing the extent of the roller adhered to titanium and reducing damage caused by adhesion on the surfaces of the plate and strip, and avoiding a possible melanism phenomenon of the lubricant.
Description
technical field [0001] The invention belongs to the field of hot-rolling lubricants for titanium and titanium alloy plates and strips. Background technique [0002] Titanium and titanium alloys have the characteristics of low density, high specific strength, and good corrosion resistance. Its plates are widely used in aviation, spaceflight, ships, chemical industry and other industries. Titanium and titanium alloy plates are processed by hot-rolling, cold-rolling, heat treatment, surface treatment and other processes on bare slabs with certain specifications, sizes and shapes after forging after melting and casting. Titanium has two remarkable characteristics in rolling: one is that its chemical properties are relatively active, so that it is easy to react with the surrounding environment during the rolling process, especially in the hot rolling process, causing pollution and reducing processing performance; Very easy to stick to the roll. In view of the fact that titaniu...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C10M167/00C10N40/24C10N30/06C10N30/04
Inventor 黄福川黄磊莫宇飞梁景粟满荣唐兴中唐彩珍蓝明新肖友程李胜梁慧田宗义李宏君赵钟兴廖丹葵刘琨黄旖瑶
Owner GUANGXI UNIV