Preparation method of antioxidant coating on surface of graphite

An anti-oxidation coating, graphite technology, applied in the field of materials, can solve the problems of unfavorable use, long cycle, control of auxiliary components and complicated preparation process, and achieve the effect of preventing oxidation and not easy to crack

Active Publication Date: 2013-12-11
QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The graphite anti-oxidation coating prepared by this method is complicated, the control of various additives and the preparation process are cumbersome and the cycle is long, which is not conducive to continuous production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of antioxidant coating on surface of graphite
  • Preparation method of antioxidant coating on surface of graphite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The embodiment of the present invention provides a method for preparing an anti-oxidation coating on the surface of graphite, which can be applied to the preparation of an anti-oxidation coating on the surface of graphite materials used in intermediate frequency induction heating equipment, such as the anti-oxidation coating of graphite materials used in amorphous strip production equipment. Oxidation coating preparation.

[0021] This preparation method comprises the steps:

[0022] Step 110, mix 30-45 parts by mass of SiC powder with 10-20 parts by mass of high-temperature glue, and mechanically stir evenly to obtain a SiC coating, and leave the stirred SiC coating for later use.

[0023] SiC powder is composed of β-SiC, a small amount of C, cristobalite and a small amount of ferrosilicon, in the form of powder, with a mesh number of 0-330 mesh and a density of 2.2g / cm 2 about. In a specific example, the composition of SiC powder is SiC≥90.0%, free C≤2.0%, Fe 2 o ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an antioxidant coating on the surface of graphite. The preparation method comprises the following steps: mixing SiC powder of 30-40 parts by mass and high-temperature glue of 10-20 parts by mass, and uniformly stirring to obtain a SiC coating, and standing the SiC coating for later use; polishing and burnishing a graphite material, placing the polished graphite material into anhydrous ethyl alcohol for ultrasonic cleaning, cleaning with deionized water, and drying for later use; uniformly applying the SiC coating on the surface of the cleaned graphite material to form a primary coating; keeping the thickness of the applied and flattened primary coating to be 0.3-0.5 mm; placing the graphite material applied with the primary coating in a 120 DEG C baking oven to be baked for 2 hours; uniformly coating the SiC coating on the surface of the baked graphite material to form a secondary coating; adhering the secondary coating to the primary coating and ensuring that the total thickness of the primary coating and the secondary coating is 3-10 mm; placing the graphite material coated with the secondary coating in the 120 DEG C baking oven to be baked for 6-8 hours.

Description

technical field [0001] The invention relates to the field of material technology, in particular to a method for preparing an anti-oxidation coating on a graphite surface. Background technique [0002] Amorphous alloy strip is molten steel with 10 6 The formed ribbon is cooled at a rate of °C / s. The alloy with a certain composition ratio is melted in the furnace, after being calmed and kept warm by the tundish, it flows into the preheated spray bag, passes through a narrow gap at the bottom of the spray bag, flows to the rapidly rotating cooling roller, and rapidly cools into a solid state flung out to form an amorphous ribbon. Among them, the molten steel temperature plays an extremely important role. The temperature of the molten steel flowing to the cooling roll is directly affected by the heat preservation during the preheating of the spray ladle and the spraying process. If the temperature is too high or too low, the quality and performance of the amorphous strip will...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/50
Inventor 庞靖张雪松王玲
Owner QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com