Periclase-calcium-containing spinel brick for cement rotary kiln burning zone and preparation method thereof

A technology of cement rotary kiln and calcium spinel is applied in the field of periclase-calcium spinel bricks used in the firing zone of cement rotary kiln and its preparation, which can solve the problems of poor performance of sticking kiln skin and achieve good The effect of sticking kiln skin performance, improving service life and maintaining stable existence

Active Publication Date: 2015-01-21
WUHAN UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Magnesia spinel brick has the advantages of good thermal shock stability and corrosion resistance to alkali, chlorine and sulfur. The problem of poor performance of hanging kiln skin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The preparation method of the calcium-containing spinel is as follows: first co-grind 55-75wt% alumina raw material, 20-40wt% magnesia raw material and 1-10wt% raw dolomite, dry, knead, Extruded into a green body; then keep the green body at 110-200°C for 12-48 hours, put it into a high-temperature kiln, and calcinate it at 1600-1850°C, and then crush the calcined product to obtain calcium-containing tips spar.

[0016] Both the MgO content of the fused magnesia and the sintered magnesia are ≥95wt%.

Embodiment 1

[0018] A periclase-calcium-containing spinel brick for the firing zone of a cement rotary kiln and its preparation method: first, 60-70wt% of sintered magnesia and 30-40wt% of calcium-containing spinel are used as raw materials, mixed, Then add 2~4wt% pulp waste liquid of the above raw materials, knead, shape, bake, and then keep warm at 1500~1600°C for 2~4 hours to obtain the periclase-containing Calcium spinel bricks.

[0019] The particle gradation of sintered magnesia in this embodiment is: the particle size is 5-0.088mm, accounting for 25-32wt% of the raw material, and the particle size is less than 0.088mm, accounting for 35-38wt% of the raw material.

[0020] The gradation of calcium-containing spinel particles in this embodiment is: the particle size is 5-0.088 mm, accounting for 15-20 wt% of the raw material, and the particle size is less than 0.088 mm, accounting for 15-20 wt% of the raw material.

[0021] The forming in this embodiment is machine press forming, and...

Embodiment 2

[0024] A periclase-calcium-containing spinel brick for the firing zone of a cement rotary kiln and its preparation method: first, 70-80wt% fused magnesia and 20-30wt% calcium-containing spinel are used as raw materials, and mixed , and then add 3~5wt% pulp waste liquid of the raw material, knead, shape, bake, and then keep warm for 3~5 hours under the condition of 1600~1650°C to obtain periclase for cement rotary kiln firing belt- Calcium spinel bricks.

[0025] The particle gradation of the fused magnesia in this embodiment is: the particle size is 5-0.088 mm, accounting for 32-40 wt% of the raw material, and the particle size is less than 0.088 mm, accounting for 38-40 wt% of the raw material.

[0026] The gradation of calcium-containing spinel particles in this embodiment is: the particle size is 5-0.088 mm, accounting for 10-15 wt% of the raw material, and the particle size is less than 0.088 mm, accounting for 10-15 wt% of the raw material.

[0027] The forming in this e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention specifically relates to a periclase-calcium-containing spinel brick for a firing zone of a cement rotary kiln and a preparation method thereof. Its technical scheme is: firstly use 60-95wt% magnesia and 5-40wt% calcium-containing spinel as raw materials, mix them, and then add 2-5wt% pulp waste liquid of the raw materials, knead, shape, and bake Baked, and then kept at 1500-1800°C for 2-5 hours to obtain periclase-calcium-containing spinel bricks for the firing zone of cement rotary kiln. The preparation method of the calcium-containing spinel is: first co-grinding 55-75wt% alumina raw material, 20-40wt% magnesia raw material and 1-10wt% raw dolomite, drying, kneading, extruding Press into a green body; then keep the green body at 110~200°C for 12~48 hours, put it into a high-temperature kiln, and calcinate it at 1600~1850°C, and then crush the calcined product to obtain calcium-containing spinels stone. The periclase-calcium-containing spinel brick prepared by the invention has excellent performance of sticking to the kiln skin and improves the service life of the refractory material.

Description

technical field [0001] The invention belongs to the technical field of periclase-calcium-containing spinel bricks, and in particular relates to a periclase-calcium-containing spinel brick for a firing zone of a cement rotary kiln and a preparation method thereof. Background technique [0002] The sticking performance of the kiln skin is an important operational performance of the refractories used in the firing belt of the cement rotary kiln. The heat insulation effect brought by the kiln skin with an appropriate thickness on the surface of the refractory brick can effectively reduce the temperature gradient between the surface temperature of the refractory brick and the inside of the brick, and reduce the damage to the refractory brick caused by the thermal stress inside the brick. At the same time, the existence of the kiln skin can also effectively reduce the cement Chemical attack of clinker on refractory bricks. The stable adhesion of the kiln skin on the surface of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 顾华志罗琼孙光思
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com