Liquid phase plasma surface cleaning method for tungsten-rhenium wire

A liquid-phase plasma and surface cleaning technology, applied in the field of metal cleaning, can solve the problems of environmental pollution, inability to clean the surface, bright and clean, etc., and achieve the effect of bright and clean surface, large cleaning volume and clean cleaning.

Inactive Publication Date: 2014-01-08
CHONGQING ACADEMY OF SCI & TECH
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Judging from the current domestic cleaning technology, pickling or alkaline cleaning is mainly used, coupled with ultrasonic composite cleaning. This cl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] Example 1

[0030] The liquid-phase plasma surface cleaning method of tungsten rhenium wire includes the following steps:

[0031] a. Dip the rolled tungsten rhenium wire directly as the anode into the neutral salt cleaning solution of the cleaning tank, and immerse the graphite as the cathode into the neutral salt cleaning solution of the cleaning tank; the neutral salt cleaning solution is the concentration It is a 3%-15% sodium bicarbonate solution. Preferably, the concentration of the sodium bicarbonate solution is 5%-10%.

[0032] b. The anode is connected to the negative electrode of the power supply, and the cathode is connected to the positive electrode of the power supply. The ultrasonic generator is synchronously turned on outside the cleaning tank to perform ultrasonic vibration in the cleaning tank for 5-30min; the power supply is output from the system and the power supply The control system is composed of, when cleaning, the power control system controls the out...

Example Embodiment

[0035] Example 2

[0036] The liquid-phase plasma surface cleaning method of tungsten rhenium wire includes the following steps:

[0037] a. Dip the rolled tungsten rhenium wire directly as the cathode into the neutral salt cleaning solution of the cleaning tank, and immerse the graphite as the anode into the neutral salt cleaning solution of the cleaning tank; the neutral salt cleaning solution is the concentration It is a 3%-15% sodium bicarbonate solution. Preferably, the concentration of the sodium bicarbonate solution is 5%-10%.

[0038] b. The anode is connected to the negative electrode of the power supply, and the cathode is connected to the positive electrode of the power supply. The ultrasonic generator is synchronously turned on outside the cleaning tank to perform ultrasonic vibration in the cleaning tank for 5-30min; the power supply is output from the system and the power supply The control system is composed of, when cleaning, the power control system controls the out...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a liquid phase plasma surface cleaning method for a tungsten-rhenium wire. Equipment comprises a control power supply, an output power supply, a cleaning tank, a first electrode and a second electrode. According to the liquid phase plasma surface cleaning method, the tungsten-rhenium wire is taken as the first electrode, the tungsten-rhenium wire is matched with the second electrode and a neutral salt cleaning solution, plasma can be produced on the surface of the tungsten-rhenium wire after electrification, ultrasonic oscillation is taken as assistance for removing greasy dirt and impurities on the surfaces of parts, and the liquid phase plasma surface cleaning method has the characteristics of thorough and complete cleaning and bright and tidy smooth; the cleaning solution selects a sodium bicarbonate solution which does not contain acid and alkali, the treatment of the waste solution is not required, and the harm to an environment can also be avoided; and the tungsten-rhenium wire is rolled up for batch cleaning, the cleaning quantity is large, and the cleaning efficiency is high.

Description

Technical field [0001] The invention belongs to the technical field of metal cleaning, and specifically relates to a liquid-phase plasma surface cleaning method of tungsten rhenium wire. Background technique [0002] As a commonly used electric light source, tungsten wire becomes very brittle after being recrystallized after high temperature use, and it is very easy to break under impact or vibration. In some electric light source products that require high reliability, in order to prevent the filament from breaking, rhenium is often added to the doped tungsten wire, called tungsten rhenium wire. The alloy contains 1% to 5% (mass) of rhenium. Add silicon, aluminum, and potassium to improve the high temperature performance of the material. It can reduce the brittle transition temperature of tungsten to room temperature or below. Tungsten rhenium wire is currently used mainly in the following areas: [0003] (1) Production of tungsten filament lamps and chromatographic heat sensit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G5/00
Inventor 刘林森王开阳
Owner CHONGQING ACADEMY OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap