Stiffener film substrate composition, stiffener film substrate as well as stiffener film and steel plate composite material

A technology of reinforcing film and composition, which is applied in the field of steel plate composite materials, and can solve the problems of low strength, low bonding force between reinforcing film and steel plate, etc.

Active Publication Date: 2014-01-15
BYD CO LTD
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the technical problems in the prior art that the bonding force between the reinforcing film and the steel plate is low, and the strength after curing is not high, the present invention provides a kind of steel sheet that can be prepared with goo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of the reinforced film of the present invention may be to attach the reinforcing layer on one surface of the reinforced film substrate of the present invention to obtain a reinforced film. It is also possible to compress the kneaded reinforced film matrix composition and the reinforcing layer together. It can also be that the release paper and the reinforcement layer are clamped and kneaded to form a reinforced film matrix composition, and then placed on a molding device to be pressed into a sheet. The invention is not limited.

[0027] The present invention also provides a steel plate composite material, which comprises a steel plate bonded together in sequence, a reinforcing film matrix and a reinforcement layer, and the reinforcing film matrix is ​​the above-mentioned reinforcing film matrix. Wherein, preferably, the thickness ratio of the steel plate, the reinforcing film substrate and the reinforcing layer may be 0.6-1.2:0.5-5:0.05-2. Where...

Embodiment 1

[0031] The reinforcing film matrix composition of this embodiment: 100 parts by weight of bisphenol A epoxy resin (Nanya Epoxy Resin Co., Ltd.) with an epoxy equivalent of 170-240 g / equivalent and a viscosity (25° C.) of 12000-15000 cps, acrylonitrile 30 parts by weight of nitrile rubber with a content of 30-50% by weight and a Mooney viscosity of 50-60 (manufactured by a Japanese company), styrene-butadiene rubber with a butadiene content of 50-70% by weight and a Mooney viscosity of 46-60 (Ji Chemical manufacturer) 35 parts by weight, tert-butyl phenolic resin (Dongxin chemical manufacturer) 20 parts by weight, particle size 10-75μm, density 0.1-0.3g / cm 3 35 parts by weight of hollow glass microspheres, 2 parts by weight of channel black with a particle size of 3-8 μm, 8 parts by weight of dicyandiamide with a particle size of 2-20 μm, 10 parts by weight of DOP, calcium carbonate and talc with a particle size of 2-13 μm 110 parts by weight of powder, 1 part by weight of dicu...

Embodiment 2

[0035] The automotive reinforcing film sample S2 was prepared in the same manner as in Example 1, except that the tackifier used in the reinforcing film matrix composition was octyl phenolic resin (Dongxin Chemical).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Epoxy equivalentaaaaaaaaaa
Viscosityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a stiffener film substrate composition, a stiffener film substrate, a stiffener film and a steel plate composite material comprising the stiffener film. The stiffener film substrate composition comprises epoxy resin, nitrile rubber, butadiene styrene rubber, a curing agent and a tackifier. The prepared stiffener film substrate has strong bonding force with a vehicle body steel plate, the strength of the cured stiffener film substrate is further improved, meanwhile, the vibration noise of a vehicle body can be reduced, and the NVH (Noise Vibration and Harshness) property of a vehicle can be enhanced.

Description

technical field [0001] The invention relates to a reinforced film matrix composition, a reinforced film matrix prepared from the composition, a reinforced film, and a steel plate composite material comprising the reinforced film. Background technique [0002] With the development of technology and the continuous improvement of automobile quality, automobiles are developing in the direction of high speed, light weight, energy saving and comfort. (Harshness)) requirements are also getting higher and higher. The current development trend of automobile lightweight makes the structure of automobile body change, such as thinning of outer panels, hollowing of structural parts, etc. This phenomenon will affect the NVH performance of automobiles. And its potential safety hazard will cause injury to the occupant. In order to solve this method of using thin steel plate as the body material to reduce the weight of the body in order to achieve the purpose of energy saving and consumptio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/00C09J109/02C09J109/06C09J11/04C09J7/04C09J7/02B32B7/12B32B15/092B32B15/18
Inventor 熊伟常德才曾永斌邵辉琳
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap