Bamboo charcoal and shell carbon composite viscose

A technology of viscose fiber and fruit shell charcoal, which is applied in the fields of fruit shell charcoal composite viscose fiber, bamboo charcoal, and composite carbon viscose fiber. good affinity effect

Inactive Publication Date: 2014-02-05
YIBIN HIEST FIBER +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] The present invention aims to solve the problem that there is no viscose fiber product made by compounding various charcoals in the prior art, and the carbon slurry made of various charcoals cannot be mixed evenly, and provides a kind of bamboo charcoal, shell charcoal composite viscose fiber, It can reduce production costs and meet special product functional requirements, and various carbon pulps can be matched with each other, mixed evenly, and combined with viscose to make bamboo charcoal and fruit shell charcoal composite viscose fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0085] A bamboo charcoal, shell charcoal composite viscose fiber, using cellulose fiber pulp as raw material, making it into viscose, and then injecting bamboo charcoal pulp and shell charcoal pulp into the viscose by pre-spinning injection, passing through a static mixer Mixing, then wet spinning and post-processing to get the finished product;

[0086] Described finished product comprises following raw material in parts by weight:

[0087] Bamboo charcoal slurry 0.1 parts

[0088] 0.1 part of charcoal pulp of fruit shell

[0089] 85 parts of viscose;

[0090] Described bamboo charcoal slurry contains alkali 4%, and viscosity is 50 millipascal seconds;

[0091] Described fruit shell charcoal slurry contains alkali 4%, and viscosity is 50 millipascal seconds;

[0092] Described bamboo charcoal, shell charcoal composite viscose fiber finished product index are:

[0093] Air permeability ≥500mm / s

[0094] Carbon adsorption is ammonia absorption rate ≥ 50%

[0095] Color f...

Embodiment 2

[0098] A bamboo charcoal, shell charcoal composite viscose fiber, using cellulose fiber pulp as raw material, making it into viscose, and then injecting bamboo charcoal pulp and shell charcoal pulp into the viscose by pre-spinning injection, passing through a static mixer Mixing, then wet spinning and post-processing to get the finished product;

[0099]Described finished product comprises following raw material in parts by weight:

[0100] Bamboo charcoal paste 10 parts

[0101] 5 servings of charcoal pulp

[0102] 99.8 parts of viscose;

[0103] Described bamboo charcoal slurry contains alkali 9%, and viscosity is 40 millipascal seconds;

[0104] Described fruit shell charcoal slurry contains alkali 11%, and viscosity is 33 millipascal seconds;

[0105] Described bamboo charcoal, shell charcoal composite viscose fiber finished product index are:

[0106] Air permeability ≥500mm / s

[0107] Carbon adsorption is ammonia absorption rate ≥ 50%

[0108] Color fastness to wa...

Embodiment 3

[0111] A bamboo charcoal, shell charcoal composite viscose fiber, using cellulose fiber pulp as raw material, making it into viscose, and then injecting bamboo charcoal pulp and shell charcoal pulp into the viscose by pre-spinning injection, passing through a static mixer Mixing, then wet spinning and post-processing to get the finished product;

[0112] Described finished product comprises following raw material in parts by weight:

[0113] Bamboo charcoal pulp 5.1 parts

[0114] 2.55 parts of charcoal pulp

[0115] Viscose 92.4 parts;

[0116] Described bamboo charcoal slurry contains alkali 6.5%, and viscosity is 45 millipascal seconds;

[0117] Described fruit shell charcoal slurry contains alkali 7.5%, and viscosity is 41.5 millipascal seconds;

[0118] Described bamboo charcoal, shell charcoal composite viscose fiber finished product index are:

[0119] Air permeability ≥500mm / s

[0120] Carbon adsorption is ammonia absorption rate ≥ 50%

[0121] Color fastness to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Air permeabilityaaaaaaaaaa
Strongaaaaaaaaaa
Strongaaaaaaaaaa
Login to View More

Abstract

The invention relates to bamboo charcoal and shell carbon composite viscose, belonging to the technical field of viscose production. The composite viscose is prepared by the steps of using cellulose fiber pulp as a raw materials to prepare viscose, then adopting injection before spinning to inject bamboo charcoal pulp and shell carbon pulp into the viscose, mixing the pulp with a static mixer and then carrying out wet spinning and aftertreatment, thus obtaining the finished product. The invention provides the new carbon composite viscose product which can reduce the production cost and meet the special requirements of the product; the problem in the prior art that different kinds of carbon pulp can not be mixed uniformly is solved through selection of the index parameters of various carbon pulp in the raw materials and the carbon pulp can be mixed uniformly with the static mixer, thus improving the spinnability in the spinning process, avoiding affecting aftertreatment and ensuring the dyeing uniformity and color fastness during dyeing.

Description

technical field [0001] The invention relates to a composite carbon viscose fiber. More specifically, the invention relates to a bamboo charcoal and shell charcoal composite viscose fiber, which belongs to the technical field of viscose fiber production. Background technique [0002] Bamboo charcoal is a kind of charcoal made of three-year-old moso bamboo as raw material and fired at a high temperature of nearly 1,000 degrees. Bamboo charcoal has a porous structure, its molecules are fine and porous, and its quality is hard. It has strong adsorption capacity, can purify the air, eliminate peculiar smell, absorb moisture, prevent mildew, inhibit bacteria and repel insects. Contact with the human body can dehumidify and absorb sweat, promote human blood circulation and metabolism, and relieve fatigue. After being scientifically refined and processed, it has been widely used in daily life. [0003] In agriculture, bamboo charcoal can be used as a carrier of soil microorganism...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine