Overpressure resistant PVC tubing

A PVC pipe, pressure-resistant technology, applied in the field of pipes, can solve the problems of low impact strength of rigid PVC pipes, prone to water leakage, water seepage, etc., and achieve the effect of enhancing processing fluidity, not easy to leak water, and resistant to chemical corrosion.

Inactive Publication Date: 2014-02-26
QINGDAO HUARUI RUBBER IND EQUIP
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies in the existing technology, the technical problem to be solved by the present invention is to provide a low-cost, high-strength and toughness, high-impact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Below in conjunction with specific embodiment the present invention is described in further detail;

[0016] A pressure-resistant PVC pipe, consisting of the following components by weight:

[0017] Polyvinyl chloride resin 50~70;

[0018] Plasticizer 3~5;

[0019] Lithopone 6~10;

[0020] Calcium carbonate 10-12;

[0021] Cadmium stearate 3~5;

[0022] Anti-impact agent 5~10;

[0023] Aluminum hydroxide 3-6;

[0024] Synthetic paraffin 5-10.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an overpressure resistant PVC tubing, which is composed of the following components by weight: 50-70 parts of PVC resin, 3-5 parts of plasticizer, 6-10 parts of lithopone, 10-12 parts of calcium carbonate, 3-5 parts of cadmium stearate, 5-10 parts of impact resistance agent, 3-6 parts of aluminium hydroxide, and 5-10 parts of synthesized paraffin. The impact resistance tubing has the advantages of good toughness and shock resistance, chemical corrosion resistance, improved tensile strength and fracture elongation rate, good toughness without water leakage, water seepage and rupture, and MBS resin is added into the PVC for promoting plasticizing, and enhancing inorganic substance dispersion and processing fluidity of PVC melt, and improving low temperature impact strength of the product.

Description

technical field [0001] The invention relates to a pipe material, in particular to a pressure-resistant PVC pipe material. Background technique [0002] The impact strength of rigid polyvinyl chloride products is not high. At present, it is mainly added by adding CPE (chlorinated polyethylene), MBS (butadiene and styrene, methyl methacrylate copolymer) or high impact ACR (acrylate copolymer) to improve the impact strength of the product. However, the impact resistance of CPE products is limited; high-impact ACR and MBS resins can maintain the product [0003] However, simply adding MBS or ACR cannot meet the requirements of high strength and high impact resistance of PVC-M pipes and fittings. Contents of the invention [0004] Aiming at the deficiencies in the existing technology, the technical problem to be solved by the present invention is to provide a low-cost, high-strength and toughness, high-impact resistance, which can effectively solve the problem of low impa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K13/02C08K3/30C08K3/26C08K5/098C08K3/22C08K5/01
Inventor 李金燕
Owner QINGDAO HUARUI RUBBER IND EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap