Hydrogel of composite semipermeable membrane and preparation method thereof
A composite semi-permeable membrane, hydrogel technology, applied in the fields of medical science, absorbent pads, layered products, etc., can solve the problems of residues, potential safety hazards, toxicity of small molecular initiators, etc., and achieve extended use time and high transparency. , the effect of expanding the use function and application scope
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032] Example 1
[0033] 8% by mass of polyvinylpyrrolidone and 2% carrageenan were prepared into an aqueous solution, after physical methods were preformed, it was coated with a polyurethane film using a coating process to form a coil, and then subjected to cobalt source radiation treatment with a radiation dose of 18kGy to obtain The hydrogel of the composite polyurethane film, when the material absorbs water up to a swelling rate of 500%, it still maintains the close combination of the hydrogel and the film.
Example Embodiment
[0034] Example 2
[0035] The polyacrylamide is soaked, and then formulated into an aqueous solution of 60% by mass. The foam is discharged at 0.08MPa, and then filled into a tray of a certain shape, covered with a polyethylene terephthalate film, and then treated with cobalt The source radiates 35kGy to form the hydrogel material of the composite polyethylene terephthalate film. When the swelling rate reaches 1400%, the hydrogel and the film are still tightly bonded.
Example Embodiment
[0036] Example 3
[0037] The mass percentage of 16% sodium alginate, 0.8% hyaluronic acid, 1% propylene glycol was prepared into an aqueous solution, and the crosslinking agent CaCl2 aqueous solution was added dropwise while stirring rapidly, and then coated on the low-density polyethylene film. Electron accelerated radiation of 42kGy to obtain a composite low-density polyethylene film hydrogel, which still maintains the close combination of the hydrogel and the film when the swelling rate reaches 1200%.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap