Aluminum oxide pure black ceramic material and processing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of ceramic materials and processing methods, applied in the field of electronic ceramics, can solve the problems of high cost compliance, inconsistent inside and outside, high cobalt price, etc., and achieve the effects of good size consistency, good wear resistance, and good toughness.
Active Publication Date: 2014-03-05
XINHUA COUNTY XINTIAN ELECTRONICS CERAMICS
View PDF1 Cites 16 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In addition, a large amount of cobalt dioxide is also added on this basis, so that the price of cobalt is quite expensive, and the cost is greatly increased. Although the color is better than the original, it is blue-black, and the inside and outside are still inconsistent.
There are also some companies that directly purchase the black color base and add α-alumina to make products after grinding and mixing. The blackness of the product has improved, but it is not pure black, and the inside and outside are still inconsistent.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] This embodiment provides a pure black alumina ceramic material, which has the following components in weight percentage:
[0033] α-alumina 77.5~95.0wt%,
[0034] Ferric oxide 2.5~7.5wt%,
[0035] Manganese dioxide 2.0~10.0wt%,
[0036] Nickel oxide 0.5~5.0wt%.
[0037] Among them, the chemical molecular formula of α-alumina is α-Al 2 o 3 , mainly using 95-Al 2 o 3 ; The chemical molecular formula of ferric oxide is Fe 2 o 3 ; The chemical formula of manganese dioxide is MnO 2 ; The chemical formula of nickel oxide is NiO 2 .
[0038]
Embodiment 2
[0040] This embodiment provides a pure black alumina ceramic material, which has the following components in weight percentage:
[0041] α-alumina 86.5~92.5wt%,
[0042] Ferric oxide 3.5~5.5wt%,
[0043] Manganese dioxide 3.0~5.0wt%,
[0044] Nickel oxide 1.0~3.0wt%.
[0045]
Embodiment 3
[0047] This embodiment provides a pure black alumina ceramic material, which has the following components in weight percentage:
[0048] α-alumina 92.5wt%,
[0049] Ferric oxide 3.5wt%,
[0050] Manganese dioxide 3.0wt%,
[0051] Nickel oxide 1.0wt%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size (mesh)
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an aluminum oxide pure black ceramic material. The aluminum oxide pure black ceramic material comprises the following components in percentage by weight: 77.5 to 95.0 percent of alpha-aluminum oxide, 2.5 to 7.5 percent of ferric oxide, 2.0 to 10.0 percent of manganese dioxide and 0.5 to 5.0 percent of nickel oxide. The invention also discloses a formula and a processing method of the aluminum oxide pure black ceramic material. The ferric oxide, the manganese dioxide, the nickel oxide and the alpha-aluminum oxide are mixed according to the design ratio, so that the internal and external consistency of the ceramic material is greatly improved and the ceramic material is pure black. The sintered product has low shrinkage ratio and good consistency.
Description
technical field [0001] The invention relates to the technical field of electronic ceramics, in particular to a formula of alumina pure black ceramic material and a processing method thereof. [0002] Background technique [0003] In the electronic ceramics industry, electronic ceramics is a traditional name, but it should actually be called "oxide structure ceramics". This ceramic is a type of ceramic material that has been developed relatively early and is widely used. It generally refers to a type of ceramic material with a melting point higher than SiO 2 Various simple oxide ceramics with a crystalline melting point (1730 degrees). such as AL 2 o 3 , MgO, ZrO 2 , BeO, ThO 2 、TiO 2 , or composite oxide ceramics such as Al 6 Si 2 o 13 (mullite), MgAL 2 o 4 (spinel), cordierite, etc. [0004] Electronic ceramics are ceramics with new functions obtained through the control of surface, grain boundary and size structure. It can be widely used in energy, machinery, ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.