Magnetic macroporous adsorption resin microspheres, and preparation method thereof

An adsorption resin and macroporous technology, applied in the field of polymer material preparation, can solve the problems of unmade microspheres and low cost, and achieve the effects of low cost, high product quality and wide application range

Inactive Publication Date: 2014-04-23
何小刚
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the problem that the magnetic macroporous adsorption ion exchange resin in the prior art is not made into a microsphere shape and is not suitable for application in the field of medicine, and provides a magnetic macroporous adsorption resin microsphere to make its application range wider wide, higher product quality, and lower cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A magnetic macroporous adsorption resin microsphere, comprising the following raw materials in parts by weight:

[0047] Oil phase:

[0048] 55% divinylbenzene 50 parts

[0049] Styrene 5 parts

[0050] 3 parts methyl acrylate

[0051] 200# gasoline 30 parts

[0052] 20 parts of toluene

[0053] 1 part dibenzoyl peroxide

[0054] Nano Fe 3 o 4 Particles 10 parts

[0055] water box:

[0056] 600 parts of deionized water

[0057] Sodium chloride 5 parts

[0058] 6 parts polyvinyl alcohol

[0059]2 parts gelatin.

Embodiment 2

[0061] A magnetic macroporous adsorption resin microsphere, comprising the following raw materials in parts by weight:

[0062] Oil phase:

[0063] 55% divinylbenzene 70 parts

[0064] Styrene 10 parts

[0065] 5 parts methyl acrylate

[0066] 50 parts of 200# gasoline

[0067] 40 parts of toluene

[0068] 2 parts dibenzoyl peroxide

[0069] Nano Fe 3 o 4 Particles 20 parts

[0070] water box:

[0071] 800 parts of deionized water

[0072] Sodium chloride 10 parts

[0073] 8 parts polyvinyl alcohol

[0074] 6 parts gelatin.

Embodiment 3

[0076] A magnetic macroporous adsorption resin microsphere, comprising the following raw materials in parts by weight:

[0077] Oil phase:

[0078] 55% divinylbenzene 60 parts

[0079] Styrene 7.5 parts

[0080] 4 parts methyl acrylate

[0081] 200# gasoline 40 parts

[0082] 30 parts of toluene

[0083] Dibenzoyl peroxide 1.5 parts

[0084] Nano Fe 3 o 4 Particles 15 parts

[0085] water box:

[0086] 700 parts of deionized water

[0087] Sodium chloride 7.5 parts

[0088] 7 parts polyvinyl alcohol

[0089] 4 parts gelatin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to magnetic macroporous adsorption resin microspheres, and a preparation method thereof. The magnetic macroporous adsorption resin microspheres comprise oil phase and water phase; the oil phase comprises following raw materials, by weight, 50 to 70 parts of 55% divinyl benzene, 5 to 10 parts of styrene, 3 to 5 parts of methyl acrylate, 30 to 50 parts of gasoline No.200, 20 to 40 parts of methylbenzene, 1 to 2 parts of dibenzoyl peroxide, and 10 to 20 parts of nano Fe3O4 particle; and the water phase comprises following raw materials, by weight, 600 to 800 parts of deionized water, 5 to 10 parts of sodium chloride, 6 to 8 parts of polyvinyl alcohol, and 2 to 6 parts of gelatin. The magnetic macroporous adsorption resin microspheres are capable of solving a problem of magnetic macroporous adsorption ion exchange resin prepared via existing technology that the magnetic macroporous adsorption ion exchange resin is not microspherical in shape, and is not suitable for applications in the field of medicine. Application range of the magnetic macroporous adsorption resin microspheres is wider, product quality is higher, and cost is relatively low.

Description

technical field [0001] The invention relates to a macroporous adsorption resin and a preparation method thereof. More specifically, the invention relates to a magnetic macroporous adsorption resin microsphere and a preparation method thereof, belonging to the technical field of polymer material preparation. Background technique [0002] Magnetic macroporous adsorption resin microspheres are composed of magnetic inorganic particles (iron, cobalt, nickel or their oxides, generally Fe) by polymerization or embedding. 3 o 4 Mostly) is a kind of high molecular polymer with special structure compounded with high molecular substances. The advantages of magnetic macroporous adsorption resin microspheres are that it is easy to separate under an external magnetic field, and can carry specific functional groups (such as -COOH, -NH) on the surface of magnetic polymer microspheres through copolymerization or surface modification. 2 , -SH, -OH, etc.), if the drug is immobilized on the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F212/36C08F212/08C08F220/14C08F2/44C08F2/20C08K3/22A61K47/32
Inventor 何小刚
Owner 何小刚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products