A kind of low hydroxyl yellow filter quartz tube and preparation method thereof

A quartz tube and low-hydroxyl technology, applied in the field of quartz tubes, can solve the problems of ultraviolet rays causing damage to the human body, accelerating the aging of automobile paint, and the transmittance can not be completely filtered out, etc., to ensure quality and performance, improve compressive strength, reduce damage effect

Active Publication Date: 2016-08-24
NANTONG HUITONG TEXTILE EQUIP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Since the current ordinary UV filter quartz glass tube has a transmittance of 200-320μM and cannot completely filter out, when it is made into a lamp, part of the ultraviolet rays that cannot be filtered out will cause harm to the human body and accelerate the aging of the car paint.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1, a kind of low hydroxyl yellow filter quartz tube, it is made of the raw material of following percentage by weight:

[0013] The weight percentage content is 99% of high-purity quartz sand, 0.1% of cobalt oxide, 0.1% of cerium oxide, 0.1% of europium oxide, 0.1% of aluminum oxide, 0.1% of titanium oxide, 0.1% of potassium oxide, and 0.1% of sodium oxide.

[0014] The steps of its preparation method are as follows: first weigh a certain amount of cobalt oxide, cerium oxide, europium oxide, aluminum oxide, titanium oxide, potassium oxide, and sodium oxide and dissolve them in nitric acid with a solubility of 65% for 15 minutes, and then Add the solution to 100 kg of high-purity quartz sand, then stir evenly in a mixer for 2 hours, wash the mixed solution, dry and cool it to room temperature, then put it into a continuous melting furnace, melt it at 1800°C, and draw it into The yellow quartz tube is finally subjected to high-temperature dehydroxylation in a d...

Embodiment 2

[0015] Embodiment 2, a kind of low hydroxyl yellow filter quartz tube, it is made of the raw material of following percentage by weight:

[0016] Weight percent high-purity quartz sand 97%, cobalt oxide 0.2%, cerium oxide 1%, europium oxide 0.3%, aluminum oxide 0.3%, titanium oxide 0.2%, potassium oxide 0.3%, sodium oxide 0.3%.

[0017] The steps of its preparation method are as follows: first weigh a certain amount of cobalt oxide, cerium oxide, europium oxide, aluminum oxide, titanium oxide, potassium oxide, and sodium oxide and dissolve them in nitric acid with a solubility of 65% for 15 minutes, and then Add the solution to 100 kg of high-purity quartz sand, then stir evenly in a mixer for 2 hours, wash the mixed solution, dry and cool it to room temperature, then put it into a continuous melting furnace, melt it at 2000°C, and draw it into The yellow quartz tube is finally subjected to high-temperature dehydroxylation in a dehydroxylation furnace at a temperature of 900°C...

Embodiment 3

[0018] Embodiment 3, a kind of low-hydroxyl yellow filter quartz tube, it is made of the raw material of following percentage by weight:

[0019] Weight percent high-purity quartz sand 94%, cobalt oxide 0.5%, cerium oxide 2%, europium oxide 0.5%, aluminum oxide 0.5%, titanium oxide 0.5%, potassium oxide 0.5%, sodium oxide 0.5%.

[0020] The steps of its preparation method are as follows: first weigh a certain amount of cobalt oxide, cerium oxide, europium oxide, aluminum oxide, titanium oxide, potassium oxide, and sodium oxide and dissolve them in nitric acid with a solubility of 65% for 15 minutes, and then Add the solution to 100 kg of high-purity quartz sand, then stir evenly in a mixer for 2 hours, wash the mixed solution, dry and cool it to room temperature, then put it into a continuous melting furnace, melt it at 2200 ° C, and draw it into The yellow quartz tube is finally subjected to high-temperature dehydroxylation in a dehydroxylation furnace at a temperature of 100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-hydroxyl yellow light-filtering quartz tube and a preparation method thereof. The low-hydroxyl yellow light-filtering quartz tube is prepared from the following raw materials by optimal weight percent: 94% to 99% of quartz sand with high purity, 0.1% to 0.5% of cobaltous oxide, 0.1% to 2% of ceric oxide, 0.1% to 0.5% of europium oxide, 0.1% to 0.5% of aluminum oxide, 0.1% to 0.5% of titanium oxide, 0.1% to 0.5% of potassium oxide and 0.1% to 0.5% of sodium oxide. The low-hydroxyl yellow light-filtering quartz tube also has the advantage of being more reasonable in formula matching besides having the advantages of the ordinary ultraviolet-filtering quartz glass tube. According to the testing of a conventional method, the compressive strength of the low-hydroxyl yellow light-filtering quartz tube is greatly improved while the damage of an automobile lamp to a baking varnish is greatly decreased due to the addition of multiple metal oxides and rare earth elements; the safety performance of the low-hydroxyl yellow light-filtering quartz tube is improved at the same time.

Description

technical field [0001] The invention relates to a quartz tube, in particular to a low-hydroxyl yellow filter quartz tube; the invention also relates to a preparation method of the low-hydroxyl yellow filter quartz tube. Background technique [0002] Since the current ordinary UV filter quartz glass tube has a transmittance of 200-320 μM and cannot completely filter out, when it is made into a lamp, part of the ultraviolet rays that cannot be filtered out will cause harm to the human body and accelerate the aging of the car paint. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a quartz tube with a more reasonable formula ratio and completely filter harmful ultraviolet rays below 320 μM in view of the deficiencies of the prior art. [0004] Another technical problem to be solved by the present invention is to provide a preparation method of the above-mentioned low hydroxyl yellow filter quartz tube. [0005] The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C4/08C03C3/06C03C4/02
Inventor 黄锋顾向军
Owner NANTONG HUITONG TEXTILE EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com