Method for preparing precipitation-method white carbon black by utilizing organosilicon dust-containing tail gas hydrolysate

A technology of precipitation white carbon black and organic silicon, which is applied in the chemical industry, can solve the problems of organic silicon dust-containing tail gas hydrolyzate pollution and other problems, and achieve the effect of reducing environmental safety hazards, reducing the pressure of public opinion, and eliminating threats

Active Publication Date: 2014-05-21
浙江中天东方氟硅材料股份有限公司
View PDF8 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the defect that the organosilicon monomer factory adopts traditional accumulation, landfill and other treatment methods for the organic silicon dust-containing tail gas hydrolyzate to cause pollution, the invention provides a method for preparing precipitation method white carbon black by using the organosilicon dust-containing tail gas hydrolyzate method, this method prepares high value-added, better performance precipitated white carbon black by chemical precipitation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Put 100 parts of organic silicon dust-containing tail gas hydrolyzate and 10 parts of petroleum ether (boiling range 60~90°C) into the reactor, start stirring at a stirring speed of 450r / min, raise the temperature of the system to 80°C, stir at constant temperature for 1 hour, and then once Add 150 parts of caustic soda solution with a mass concentration of 30%, continue the reaction for 5 hours, then stop, let it stand for stratification, take the clear liquid layer and filter it, decolorize it with activated carbon of 1% of the total mass of sodium silicate solution at 60°C for 25 minutes, and get Colorless and clear sodium silicate solution; put the sodium silicate solution into the reactor, add sodium dodecyl sulfate with 2% of the total mass of the sodium silicate solution, and raise the temperature of the system to 60°C, at a stirring speed of 850r / min Add dilute hydrochloric acid with a mass concentration of 31% until the pH of the system is 7, stop adding dil...

Embodiment 2

[0030] Put 100 parts of organic silicon dust-containing tail gas hydrolyzate and 50 parts of petroleum ether (boiling range 60~90°C) into the reactor, start stirring at a stirring speed of 400r / min, raise the temperature of the system to 80°C, stir at constant temperature for 1 hour, and then once Add 200 parts of caustic soda solution with a mass concentration of 30%, continue the reaction for 5 hours, then stop, let it stand for stratification, take the clear liquid layer and filter, decolorize with activated carbon of 1% of the total mass of sodium silicate solution at 60°C for 30 minutes to obtain Colorless and clear sodium silicate solution; put the sodium silicate solution into the reactor, add polyethylene glycol with a total mass of 2% of the sodium silicate solution, raise the temperature of the system to 60°C, and add it at a stirring speed of 750r / min Concentrated sulfuric acid with a mass concentration of 86%, stop adding concentrated sulfuric acid until the pH ...

Embodiment 3

[0032]Put 100 parts of organic silicon dust-containing tail gas hydrolyzate and 30 parts of petroleum ether into the reactor, start stirring at a stirring speed of 350r / min, raise the temperature of the system to 80°C, stir at a constant temperature for 1 hour, and then add 100 parts at a time with a mass concentration of 30 % caustic soda solution, continue to react for 5 hours and then stop, let it stand for stratification, take the clear liquid layer and filter, decolorize with activated carbon of 1% of the total mass of sodium silicate solution at 60°C for 25 minutes to obtain a colorless and clear sodium silicate solution ;Put the sodium silicate solution into the reactor, add sodium tridecylsulfonate with a total mass of 2% of the sodium silicate solution, raise the temperature of the system to 60°C, and add trimethylchlorosilane at a stirring speed of 800r / min , stop adding trimethylchlorosilane until the pH of the system is 7, continue to stir for 1 hour, let it age for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing precipitation-method white carbon black by utilizing organosilicon dust-containing tail gas hydrolysate. The method comprises the following steps: a, mixing the organosilicon dust-containing tail gas hydrolysate with an dispersion aids at the mass ratio of 1:(0.1-0.5), wherein the dispersion aids are selected from low-carbon alkane, micromolecular alcohol or low-molecule aromatic hydrocarbon; b, adding caustic sodium solution into the mixture obtained in the step a under the stirring condition and mixing, after the reaction is finished, standing and layering, performing filtration and activated carbon decoloration to clear liquid in the middle layer, to obtain colorless clarified sodium silicate solution; c, adding surfactant into the sodium silicate solution, increasing the system temperature to be more than 60 DEG C, adding acid liquor while stirring until the pH value of a reaction system is equal to 7, stopping addition, standing and aging, filtering, performing azeotropy dewatering, and drying to obtain the product. The current organosilicone monomer plant always piles up or fills the organosilicon dust-containing tail gas hydrolysate, and the method can change wastes into valuables, and the organosilicon dust-containing tail gas hydrolysate can be converted into the white black carbon product.

Description

technical field [0001] The invention relates to a synthesis process of precipitated white carbon black, a product in the chemical industry, in particular to a method for preparing precipitated white carbon black by utilizing organic silicon dust-containing tail gas hydrolyzate. Background technique [0002] Dusty tail gas includes fluidized bed reactor venting air and silica powder conveying exhaust air. Usually, fluidized bed reactor venting air has a large dust content, high temperature, and a certain amount of methyl chlorosilane monomer , after being dedusted by the water washing tower, it is emptied, and the exhaust air of the silicon powder is conveyed through the bag filter and then washed and emptied. The emptied gas enters the pool and finally forms a polymer, that is, the dust-containing tail gas hydrolyzed polymer, referred to as the dust-containing tail gas hydrolyzate. [0003] The composition of organosilicon dust-containing tail gas hydrolyzate is complex, usu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/12B09B3/00
Inventor 周欣俊杨庆红孙刚吴连斌祝爱娟
Owner 浙江中天东方氟硅材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com