Hydrophilic polyester fiber containing coffee carbon and preparation method of hydrophilic polyester fiber

A technology of polyester fiber and coffee charcoal, applied in the direction of fiber chemical characteristics, single-component polyester rayon, rayon manufacturing, etc., to achieve the effect of rough surface, large structural voids, and high absorption efficiency

Active Publication Date: 2014-05-28
QUANZHOU HAITIAN MATERIAL TECH CORP
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no report on the use of sorbitol to prepare polyester for micro-modification.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophilic polyester fiber containing coffee carbon and preparation method of hydrophilic polyester fiber
  • Hydrophilic polyester fiber containing coffee carbon and preparation method of hydrophilic polyester fiber
  • Hydrophilic polyester fiber containing coffee carbon and preparation method of hydrophilic polyester fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A hydrophilic polyester fiber containing coffee charcoal, comprising a hydrophilic polyester fiber body and nanoscale coffee charcoal powder dispersed in the hydrophilic polyester fiber body. The content of nanoscale coffee charcoal powder is 0.5wt%, and its preparation method is:

[0044] (1) Preparation of hydrophilic polyester chips:

[0045]

[0046] Mix terephthalic acid and ethylene glycol in proportion to prepare slurry. The prepared slurry was mixed with the catalyst tetrabutyl titanate and then put into an esterification reactor for the first esterification reaction. The temperature of the first esterification reaction was 225° C., the reaction time was 4 hours, and the relative pressure of the reaction was 0 MPa. The by-product water is separated and collected by a fractionating tower, and the collection amount is measured with a graduated cylinder, and the theoretical value is calculated according to the reaction formula. When the collection amount of wat...

Embodiment 2

[0053] A hydrophilic polyester fiber containing coffee charcoal, comprising a hydrophilic polyester fiber body and nanoscale coffee charcoal powder dispersed in the hydrophilic polyester fiber body. The content of nanoscale coffee charcoal powder is 2wt%, and its preparation method is:

[0054] (1) Preparation of hydrophilic polyester chips:

[0055]

[0056] Mix terephthalic acid and ethylene glycol in proportion to prepare slurry. Mix the prepared slurry with ethylene glycol antimony, antioxidant 616, trimethyl phosphate and tris(nonylphenyl) phosphite in proportion and then add it to the esterification reactor for the first esterification reaction. The temperature of the esterification reaction is 230° C., the reaction time is 2.5 hours, and the relative pressure of the reaction is 0.25 MPa. The by-product water is separated and collected by a fractionating tower, and the collection amount is measured with a graduated cylinder, and the theoretical value is calculated a...

Embodiment 3

[0061] A hydrophilic polyester fiber containing coffee charcoal, comprising a hydrophilic polyester fiber body and nanoscale coffee charcoal powder dispersed in the hydrophilic polyester fiber body. The content of nanoscale coffee charcoal powder is 5wt%, and its preparation method is:

[0062] (1) Preparation of hydrophilic polyester chips:

[0063]

[0064] Mix terephthalic acid and ethylene glycol in proportion to prepare slurry. Mix the prepared slurry with antimony acetate, antioxidant 1010, antioxidant 168 and tris(nonylphenyl) phosphite in proportion and then add it to the esterification reaction kettle for the first esterification reaction. The first esterification reaction temperature is 230°C, the reaction time is 3h, and the relative pressure of the reaction is 0.35MPa. The by-product water is separated and collected by a fractionating tower, and the collection amount is measured with a graduated cylinder, and the theoretical value is calculated according to th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a hydrophilic polyester fiber containing coffee carbon and a preparation method of the hydrophilic polyester fiber. The hydrophilic polyester fiber containing coffee carbon is characterized by comprising a hydrophilic polyester fiber body and nanoscale coffee carbon powder scattered in the hydrophilic polyester fiber body. The hydrophilic polyester fiber containing coffee carbon is good in hydrophilicity, can be used for deodorizing, warming and is dried quickly, and brings touch sensation of enjoying refreshing and comfort to consumers.

Description

technical field [0001] The invention relates to a hydrophilic polyester fiber containing coffee charcoal and a preparation method thereof. Background technique [0002] Since polyester and polyester fiber entered large-scale industrialization in the 1970s, the development speed is much faster than other synthetic materials and synthetic fibers. In 2010, the output of polyester fiber in my country was 25.13 million tons, accounting for about 81% of my country's chemical fiber output; It accounts for about 70% of the world's polyester fiber production. In the next 10 years, the world's polyester and polyester fiber will still maintain a growth rate of more than 3%, and polyester fiber will account for more than 60% of the world's total fiber products. The physical and mechanical properties of polyester fibers such as strength, abrasion resistance, resilience and dimensional stability can better meet the needs of various uses. However, polyester fiber is a typical hydrophobic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10C08G63/672
Inventor 王朝生王华平张玉梅陈向玲王彪李建武
Owner QUANZHOU HAITIAN MATERIAL TECH CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com