A kind of air-drying unsaturated polyester resin and its production method

A polyester resin and a production method technology, applied in the field of air-drying unsaturated polyester resin and its production, can solve the problems of poor air-drying, difficult to control, low amount of paraffin wax, etc., achieve convenient polishing, increase transparency, The effect of improving air dryness

Inactive Publication Date: 2016-04-13
ZHANGZHOU YABANG CHEM
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. The existing air-drying resin adjusts the air-drying property by adjusting the amount of paraffin, but the amount of paraffin used is small, and the air-drying property is poor; the amount of paraffin used is large, and the transparency of the cured product is not good, which is difficult to control
[0007] 2. The existing air-drying resin used as PE paint has high hardness and is difficult to polish
[0008] 3. The existing air-drying resin has a short storage time, and the general shelf life is only 6 months (below 25°C, keep away from light and seal)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of air-drying unsaturated polyester resin and its production method
  • A kind of air-drying unsaturated polyester resin and its production method
  • A kind of air-drying unsaturated polyester resin and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1 Take the production of air-drying unsaturated polyester resin with 3600 liters of reactor as an example

[0035] raw material

[0036] Reaction feed A

[0037]

[0038] Cooling, dilution step feeding B

[0039]

[0040] production steps

[0041] 1. Check equipment, pipelines, electrical appliances, instruments, and check the type and quantity of raw materials.

[0042] 2. Put the reaction materials A into the reaction kettle: glycol, dibasic acid (anhydride), triphenyl phosphite and QS-20, etc. Heat up, 10 degrees / hour, stir after 0.5 hours, when the material heats up When the temperature reaches 120°C, start the reaction stirrer and supply 4M nitrogen 3 / h and continue to heat up the reaction.

[0043] 3. When the temperature of the distillation head rises to 98-100°C, the vertical condenser is supplied with water, the temperature of the distillation head is controlled at 100-102°C, and the reaction is kept for 1 hour after the water is discharg...

Embodiment 2

[0061] Embodiment 2 Take the production of air-drying unsaturated polyester resin with 3600 liters of reactor as an example

[0062] raw material

[0063] Reaction feed A

[0064]

[0065] Cooling, dilution step feeding B

[0066]

[0067] production steps

[0068] 1. Check equipment, pipelines, electrical appliances, instruments, and check the type and quantity of raw materials.

[0069] 2. Put the reaction materials A into the reaction kettle: glycol, dibasic acid (anhydride), triphenyl phosphite and QS-20, etc. Heat up, stir after 0.5 hours, 10 degrees / hour, when the material heats up When the temperature reaches 120°C, start the reaction stirrer and supply 4M nitrogen 3 / h and continue to heat up the reaction.

[0070] 3. When the temperature of the distillation head rises to 98-100°C, the vertical condenser is supplied with water, the temperature of the distillation head is controlled at 100-102°C, and the reaction is kept for 1 hour after the water is discharged...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
storage stabilityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an air-drying unsaturated polyester resin and a production method thereof. According to the weight ratio, the raw materials include 200-220 parts of dimer acid; 1200-1300 parts of tetrahydrophthalic anhydride; 700-750 parts of maleic anhydride; propylene glycol 1150-1200 parts; neopentyl glycol 280-300 parts; triphenyl phosphite 1.150-1.25 parts; polymerization inhibitor QS-200.5-0.6 parts; styrene 1400-1500 parts; defoamer BYK-A5550.5- 1.5 parts and leveling agent BYK-3070.4-0.6 parts. The invention also discloses a production method of the resin.

Description

technical field [0001] The invention relates to a production method of polyester resin, in particular to a method of air-drying unsaturated polyester resin. Background technique [0002] Unsaturated polyester resin is the most commonly used type of thermosetting resin. It is generally a polycondensation of unsaturated dibasic acid diol or saturated dibasic acid unsaturated diol. It has ester bonds and unsaturated double bonds. type polymer compound. Usually, the polyester polycondensation reaction is carried out at 190-220°C until the desired acid value (or viscosity) is reached. After the polyester polycondensation reaction is completed, a certain amount of vinyl monomer is added while it is hot to form a viscous Such a polymer solution is called an unsaturated polyester resin. [0003] According to the structure of unsaturated polyester resin, it can be divided into ophthalmic type, m-benzene type, p-phenylene type, bisphenol A type, vinyl ester type, etc.; according to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/01C08G63/52C08G63/78
Inventor 蒋静史益文侯辉
Owner ZHANGZHOU YABANG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More