Flame retardant acrylate adhesive
An acrylate and adhesive technology, applied in the direction of ester copolymer adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve problems such as hidden quality problems, adhesive layer burning, and debonding of load-bearing parts , to achieve the effect of increasing the flash point
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0020] Example 1:
[0021] Proportioning curing agent component main agent component
[0022] Methyl methacrylate 26%Wt 21%Wt
[0023] Hydroxyethyl methacrylate 22%Wt 40%Wt
[0024] Methacrylic acid 14%Wt 6%Wt
[0025] 2-hydroxyethyl methacrylate phosphate 5%Wt-
[0026] ABS 5.5%Wt 4.5%Wt
[0027] Nitrile rubber 12%Wt 12%Wt
[0028] Substituted thiourea 3%Wt-
[0029] Amine compounds 2.5%Wt-
[0030] 1,4-Hydroquinone-0.2%Wt
[0031] Flame retardant 10%Wt 10%Wt
[0032] Cumene Hydroperoxide-4.8%Wt
[0033] Benzoyl peroxide-1.5% Wt.
[0034] Preparation:
[0035] (1) Main agent: Put the monomethacrylate monomer and methacrylic acid into the reactor, add the elastomer, stir until the elastomer is completely dissolved, add epoxy resin and stabilizer, stir evenly, add cumene Mix hydrogen oxide and benzoyl peroxide evenly.
[0036] (2) Curing agent component: Put the monomethacrylate monomer and methacrylic acid into the reactor, add the elastomer, stir until the elastomer is completely dissolved,...
Example Embodiment
[0042] Example 2:
[0043] Proportioning curing agent component main agent component
[0044] Methyl methacrylate 23%Wt 20%Wt
[0045] Hydroxyethyl methacrylate 25%Wt 40%Wt
[0046] Methacrylic acid 11%Wt 5%Wt
[0047] 2-hydroxyethyl methacrylate phosphate 5%Wt-
[0048] ABS 5.5%Wt 4.5%Wt
[0049] Nitrile rubber 12%Wt 12%Wt
[0050] Substituted thiourea 3%Wt-
[0051] Amine compounds 2.5%Wt-
[0052] 1,4-Hydroquinone-0.2%Wt
[0053] Flame retardant 13%Wt 12%Wt
[0054] Cumene Hydroperoxide-4.8%Wt
[0055] Benzoyl peroxide-1.5% Wt.
[0056] The preparation method is the same as in Example 1.
[0057] The performance test is the same as in Example 1.
[0058] The test results are shown in Table 1.
Example Embodiment
[0059] Example 3:
[0060] Proportioning curing agent component main agent component
[0061] Methyl methacrylate 20%Wt 19%Wt
[0062] Hydroxyethyl methacrylate 28%Wt 41%Wt
[0063] Methacrylic acid 8%Wt 5%Wt
[0064] 2-hydroxyethyl methacrylate phosphate 5%Wt-
[0065] ABS 5.5%Wt 4.5%Wt
[0066] Nitrile rubber 12%Wt 12%Wt
[0067] Substituted thiourea 3.5%Wt-
[0068] Amine compound 3%Wt-
[0069] 1,4-Hydroquinone-0.2%Wt
[0070] Flame retardant 15%Wt 12%Wt
[0071] Cumene Hydroperoxide-4.8%Wt
[0072] Benzoyl peroxide-1.5% Wt.
[0073] The preparation method is the same as in Example 1.
[0074] The performance test is the same as in Example 1.
[0075] The test results are shown in Table 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2023 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap