Artificial stone and preparation method thereof

An artificial stone and formula technology, applied in the direction of manufacturing tools, supply devices, ceramic molding machines, etc., can solve the problems of poor anti-fouling, low stone strength, low gloss, etc., to improve strength, high simulation, and reduce porosity. Effect

Inactive Publication Date: 2014-06-18
广州渥图生物科技有限责任公司
View PDF7 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of this type of stone is that it does not contain volatile organic compounds that are harmful to the human body, and has stro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Artificial stone and preparation method thereof
  • Artificial stone and preparation method thereof
  • Artificial stone and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0082] refer to figure 1 as well as figure 2 , the embodiment of the present invention provides a kind of preparation method of artificial stone, comprising:

[0083] In S101, the matrix material and the active material are measured and proportioned, and the main material is obtained by mixing them thoroughly.

[0084] The formula of the base material in parts by mass is as follows:

[0085] Aggregate 150~800;

[0086] Preferably, the base material also includes an inorganic pigment, and its formula in parts by mass is as follows:

[0087] Inorganic pigment 0~30;

[0088] Further preferably, the formulation of the matrix material in parts by mass is as follows:

[0089] Aggregate 200~650

[0090] Inorganic pigment 0~25.

[0091] The formulation of the active material in parts by mass is as follows:

[0092] Cross-linking agent 200~800;

[0093] Preferably, the active material also includes magnesium chloride and / or silicon micropowder, and its formula in parts by mas...

Embodiment 1

[0127] Embodiment 1, the preparation of artificial marble I

[0128] Matrix material formula: 190 parts of quartz sand, 480 parts of stone powder, 0.02 parts of inorganic pigment.

[0129] Active material formula: 640 parts of high alumina cement, 90 parts of cement reinforcing agent.

[0130] Mix and stir the matrix material and the active material until they are uniform to obtain the main material, unload the main material from the mixer, and put them into multiple feeding hoppers of the distributing machine according to the different inorganic pigments added to the main material, and control the feeding through the gate under the feeding hopper. The feeding order and feeding amount of the hopper. Move the mold with the material to the vibrating table, vibrate for 5s at an amplitude of 0.2 mm and a frequency of 50 Hz, and then pressurize the material on a press to make the material reach a predetermined density to obtain a green body. The green body is soaked in the silica...

Embodiment 2

[0131] Embodiment 2, the preparation of artificial marble II

[0132] Matrix material formula: 200 parts of quartz sand, 180 parts of stone powder, 140 parts of tailings sand, 10 parts of inorganic pigment.

[0133] Active material formula: 450 parts of high alumina cement, 50 parts of Portland cement, 40 parts of magnesium chloride, and 20 parts of silica powder.

[0134] The matrix material and the active material are mixed and stirred until they are uniform to obtain the main material, and the main material is discharged from the mixer, and put into multiple feeding hoppers of the distributing machine according to the different inorganic pigments added to the main material, and the feeding hopper is controlled through the gate under the feeding hopper The feeding sequence and feeding amount. Move the mold with the material to the vibrating table, vibrate for 5s at an amplitude of 0.1 mm and a frequency of 500 Hz, and then pressurize the material on a press to make the mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Embodiments in the invention disclose an artificial stone. The artificial stone comprises a base material and an active material, wherein the base material comprises, by mass, 150 to 800 parts of aggregate, the active material comprises, by mass, 200 to 800 parts of a cross-linking agent, the aggregate is one selected from or a mixture of quartz sand, stone powder, tailing sand and glass powder, and the cross-linking agent is one selected from or a mixture of high-alumina cement, Portland cement and fly ash. The embodiments of the invention also disclose a preparation method for the artificial stone. The method comprises the following steps: weighing the base material and the active material in proportion and carrying out uniform mixing so as to obtain a main material; subjecting the main material to spreading in a mold with a spreading machine in the manner of mathematical modeling; vibrating and pressurizing the mold filled with the material so as to obtain a green body; soaking the green body in an induction solution; and subjecting the green body to maintenance, stacking and finishing so as to obtain the artificial stone. The prepared artificial stone has same appearance, structural configuration, physicochemical properties and the like compared with natural stone.

Description

technical field [0001] The invention relates to the field of artificial stone production, in particular to an artificial stone and a preparation method thereof. Background technique [0002] In the context of today's global economic integration, in the face of excessive exploitation of resources, as well as serious environmental pollution and environmental damage, low-carbon environmental protection is the key to sustainable development. At the same time, with the development of the national economy and the improvement of people's quality of life, the requirements for building decoration materials are also getting higher and higher. Among them, the application of stone is relatively extensive. Stone as a decorative material is generally divided into natural stone and artificial stone. At present, over-exploitation of natural stone has brought irreparable damage to the ecological environment, and high-grade natural stone is close to resource depletion, resulting in an extre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B28/06C04B28/00C04B28/30B28B1/08B28B13/02
Inventor 冯增萍黄能展
Owner 广州渥图生物科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap