Anti-dripping ceramic polyolefin composite material and preparation method thereof

A technology for ceramicized polyolefin and composite materials, which is applied in the field of anti-drip ceramicized polyolefin composite materials and its preparation, can solve the problems of ablation, dripping, and polyolefin composite materials cannot be prevented, and achieves good thermal shock resistance. Sexuality, huge economic profits and social benefits

Inactive Publication Date: 2014-06-18
NANJING UNIV OF TECH
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problem that the polyolefin composite material in the above-mentioned prior art cannot prevent it from dripping when burning and cannot withstand high temperature ablation, and provides an anti-drip ceramic polyolefin composite material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-dripping ceramic polyolefin composite material and preparation method thereof
  • Anti-dripping ceramic polyolefin composite material and preparation method thereof
  • Anti-dripping ceramic polyolefin composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Raw material weight ratio:

[0030]

[0031] First, add the above two glass powders and silane coupling agent into a high-speed mixer, mix at 60°C for 20 minutes, and then discharge, and then dry to obtain surface-treated glass powder. Then, the ethylene-vinyl acetate copolymer was poured into a two-roll open mill, and the temperature was kept at 110 °C for 2 minutes, so that the organic polymer could wrap the front roller; then glass frit 1 and low softening point were added respectively. The glass powder is mixed, and the general mixing time is 12 minutes. Finally, the blend was put into a flat vulcanizer, kept at 150°C and preheated for 5 minutes, then hot pressed at 10 MPa for 10 minutes, and then cold pressed at 5 MPa for 5 minutes to produce the sheet. The performance test results are shown in Table 1.

Embodiment 2

[0033] Raw material weight ratio:

[0034]

[0035] The preparation method is the same as that in Example 1, and the performance test results are shown in Table 1.

Embodiment 3

[0037] Raw material weight ratio:

[0038]

[0039]

[0040] The preparation method is the same as that in Example 1, and the performance test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-dripping ceramic polyolefin composite material and a preparation method thereof. The anti-dripping ceramic polyolefin composite material meets all requirements for mechanical performance in the fire protection field at the normal temperature; when being burnt, the composite materials is not caused to drip so that fire expansion can be prevented. The anti-dripping ceramic polyolefin composite material is prepared from the following raw materials in parts by weight: 30-60 parts of polyolefin, 20-40 parts of high-softening point glass powder, 20-40 parts of low-softening point glass powder, 0-15 parts of organic montmorillonite, 0.5-2.5 parts of coupling agent and 0-3 parts of compatilizer.

Description

technical field [0001] The invention relates to a polyolefin composite material and a preparation method thereof, in particular to a drip-proof ceramicized polyolefin composite material and a preparation method thereof. Background technique [0002] After entering the 21st century, with the improvement of people's living standards and fire safety awareness, as well as the continuous increase of high-rise buildings, hotels, supermarkets, hospitals, stations, airports, subways, and tunnels, the importance of fire safety has become prominent. This issue has attracted great attention. This requires us to develop a cheap, simple and practical refractory material. And the anti-drip ceramified polymer composites in this paper just meet this requirement. It can be applied in: household appliances, transportation, and power transmission. Typical functions of this material: ①When a fire occurs, some burning polymer composites will not drip, and the flame will spread to other places...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/12C08L23/08C08L23/14C08K9/06C08K9/04C08K3/34C08K3/38C08K3/32C08K3/22
CPCC08K3/346C08K3/40C08K9/06C08L23/0815C08L23/12C08L2201/08C08L23/0853C08L51/06
Inventor 王庭慰贡新浩曾浩
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.