Heat-dissipation coating containing nanometer diatomite

A technology of nano-diatomite and heat-dissipating paint, applied in the direction of coating, can solve the problems of single function of heat-dissipating paint, lower system temperature, unable to meet various needs, etc. Effect

Active Publication Date: 2014-08-06
ANHUI MENGNIU COLOR PRINTING&PACKAGING
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Heat dissipation paint is a special paint that improves the heat dissipation efficiency of the surface of the object and reduces the temperature of the system. The existing heat dissipation paint has a single function and cannot meet people's various needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A kind of heat-dissipating paint containing nano diatomite, it is made by the raw material of following weight kg:

[0018] A material 50, B material 60;

[0019] Described A material is made by the raw material of following weight kg:

[0020] Keto-formaldehyde resin 50, diffusing agent NNO2, beryllium oxide 2, urotropine 0.5, nano-diatomaceous earth powder 2, di-tert-butyl peroxide 2, nano-titanium dioxide 2, zeolite powder 2, behenitol ester 1, di Methicone 3;

[0021] Described B material is made by the raw material of following weight kg:

[0022] . Chemical agent 1, epoxy linseed oil 1.5, antioxidant 1010 0.8, silane coupling agent KH560 3.5, propylene glycol 60, nano carbon 2;

[0023] The preparation method of the heat-dissipating coating containing nano diatomite comprises the following steps:

[0024] (1) Mix the raw materials of material A evenly, heat to 60°C, stir and react at a speed of 700r / min for 40 minutes, and get material A for later use;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat-dissipation coating containing nanometer diatomite. The heat-dissipation coating comprises the following raw materials in parts by weight: 40-50 parts of a material A and 50-60 parts of a material B, wherein the material A comprises the following raw materials in parts by weight: 40-50 parts of ketone-aldehyde resin, 1-2 parts of a diffusing agent NNO, 2-4 parts of beryllium oxide, 0.3-0.5 part of Urotropine, 1-2 parts of nanometer diatomite powder, 1-2 parts of di-t-butyl peroxide, 2-4 parts of nanometer titanium dioxide, 2-5 parts of zeolite powder, 1-2 parts of sorbitol ester and 3-5 parts of dimethicone. The heat-dissipation coating disclosed by the invention has the advantages of high cooling performance and convenience in application, and is used for decreasing the surface temperature of glass lamps and other objects to achieve the cooling effect, and a preferable protection effect is achieved by the reasonable combination and synergistic action of inorganic materials containing nanometer diatomite and the like and rest materials.

Description

technical field [0001] The invention relates to the field of heat-dissipating coatings, in particular to a heat-dissipating coating containing nano diatomite. Background technique [0002] Heat dissipation paint is a special paint that improves the heat dissipation efficiency of the surface of the object and reduces the temperature of the system. The existing heat dissipation paint has a single function and cannot meet the various needs of people. Contents of the invention [0003] The object of the present invention is to provide a heat dissipation coating containing nano diatomite. [0004] The above purpose is achieved through the following schemes: [0005] A heat-dissipating coating containing nano diatomite is characterized in that: it is made from the following raw materials in parts by weight: [0006] A material 40-50, B material 50-60; [0007] Described A material is made by the raw material of following weight portion: [0008] Ketoformaldehyde resin 40-50,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/06C09D7/12
Inventor 李峰郑志龙
Owner ANHUI MENGNIU COLOR PRINTING&PACKAGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap