Method for preparing low-oxygen molybdenum and molybdenum alloy clad with Al4SiC4-HfC
A technology of al4sic4-hfc and molybdenum alloy, which is applied in the field of preparing low-oxygen metal alloys, can solve problems such as poor compatibility, shedding, coating cracking, etc., and achieve excellent hardness and wear resistance, excellent oxidation resistance, and high bonding strength Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1:
[0026] will Al 4 SiC 4 The powder and HfC powder are Al by mass fraction percentage 4 SiC 4 : HfC=55%: 45% mixed uniformly to obtain Al 4 SiC 4 -HfC powder, the Al 4 SiC 4 -HfC powder and composite binder are mixed in a volume ratio of 1:3, stirred evenly, and prepared into a viscous coating and filling slurry.
[0027] First, the coating filling slurry is used to spread evenly to the bottom of the cavity of the pressing mold, and the coating thickness of the coating filling slurry on the bottom of the cavity of the pressing mold is 1 mm. Then, a lightweight filling block is placed above the coating. The filling block is coaxial with the cavity of the pressing mold, so that the side of the filling block and the inner wall of the cavity of the pressing mold form a semi-closed trough with a side length of 1 mm. Fill the trough with the coating filling slurry by injection;
[0028] After the coating and filling slurry in the trough is solidified, remo...
Example Embodiment
[0031] Example 2:
[0032] will Al 4 SiC 4 The powder and HfC powder are Al by mass fraction percentage 4 SiC 4 : HfC=60%: 40% mixed uniformly to obtain Al 4SiC 4 -HfC powder, the Al 4 SiC 4 -HfC powder and composite binder are mixed in a volume ratio of 1:3, stirred evenly, and prepared into a viscous coating and filling slurry.
[0033] First, the coating filling slurry is used to spread evenly to the bottom of the cavity of the pressing mold, and the coating thickness of the coating filling slurry on the bottom of the cavity of the pressing mold is 2 mm. Then, a lightweight filling block is placed above the coating, and the filling block is coaxial with the cavity of the pressing mold, so that the side of the filling block and the inner wall of the cavity of the pressing mold form a semi-closed trough with a side length of 2 mm. Fill the trough with the coating filling slurry by injection;
[0034] After the coating and filling slurry in the trough is solidified, r...
Example Embodiment
[0036] Example 3:
[0037] will Al 4 SiC 4 The powder and HfC powder are Al by mass fraction percentage 4 SiC 4 : HfC=70%: 30% mixed uniformly to obtain Al 4 SiC 4 -HfC powder, the Al 4 SiC 4 -HfC powder and composite binder are mixed in a volume ratio of 1:2, stirred evenly, and prepared into a viscous coating and filling slurry.
[0038] First, the coating filling slurry is used to spread evenly to the bottom of the cavity of the pressing mold, and the coating thickness of the coating filling slurry on the bottom of the cavity of the pressing mold is 2 mm. Then, a lightweight filling block is placed above the coating, and the filling block is coaxial with the cavity of the pressing mold, so that the side of the filling block and the inner wall of the cavity of the pressing mold form a semi-closed trough with a side length of 2 mm. Fill the trough with the coating filling slurry by injection.
[0039] After the coating and filling slurry in the trough is solidified, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap