Glaze of purple-sand tea sets and glazing technology

A glaze and tea set technology, which is applied in the field of purple sand, can solve the problems of high lead content, and achieve the effect of beautiful color, easy permanent preservation, and good hand feeling

Active Publication Date: 2014-08-27
卢群山
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the preparation technology of purple sand tea sets, for nearly a thousand years, in order to increase the smoo...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of glaze material of purple sand tea set, is made of the following components by weight,

[0025] 15 parts of cobalt oxide, 5 parts of zinc oxide, 30 parts of quartz, 15 parts of feldspar, 0.3 part of ferromolybdenum, 0.01 part of iron oxide, 0.02 part of lead oxide, 18 parts of dolomite, 10 parts of shell and 0.5 part of glass;

[0026] A kind of glazing process of purple sand tea set, comprising following process steps:

[0027] 1) Prepare the glaze according to the proportion, put it into a ball mill for grinding, the fineness reaches 450-500 mesh, and sieve to prepare the glaze for use;

[0028] 2) making the green body, using the purple sand in the Huainan area of ​​Anhui as the main material to make the green body, and drying it naturally at room temperature to prevent the green body from being deformed;

[0029] 3) Green body sintering: the first sintering in the kiln, using reducing flame sintering, rising to a temperature of 950-1050°C, and firing time ...

Embodiment 2

[0034] A kind of glaze material of purple sand tea set, is made of the following components by weight,

[0035] 14 parts of cobalt oxide, 6 parts of zinc oxide, 35 parts of quartz, 20 parts of feldspar, 0.2 part of ferromolybdenum, 0.02 part of iron oxide, 0.01 part of lead oxide, 20 parts of dolomite, 15 parts of shell and 0.3 part of glass;

[0036] A kind of glazing process of purple sand tea set, comprising following process steps:

[0037] 1) Prepare the glaze according to the proportion, put it into a ball mill for grinding, the fineness reaches 450-500 mesh, and sieve to prepare the glaze for use;

[0038] 2) making the green body, using the purple sand in the Huainan area of ​​Anhui as the main material to make the green body, and drying it naturally at room temperature to prevent the green body from being deformed;

[0039] 3) Green body sintering: the first sintering in the kiln, using reducing flame sintering, rising to a temperature of 950-1050°C, and firing time ...

Embodiment 3

[0044] A kind of glaze material of purple sand tea set, is made of the following components by weight,

[0045] 16 parts of cobalt oxide, 4 parts of zinc oxide, 25 parts of quartz, 10 parts of feldspar, 0.1 part of ferromolybdenum, 0.005 part of iron oxide, 0.01 part of lead oxide, 10 parts of dolomite, 5 parts of shell and 0.1 part of glass;

[0046] A kind of glazing process of purple sand tea set, comprising following process steps:

[0047] 1) Prepare the glaze according to the proportion, put it into a ball mill for grinding, the fineness reaches 450-500 mesh, and sieve to prepare the glaze for use;

[0048] 2) making the green body, using the purple sand in the Huainan area of ​​Anhui as the main material to make the green body, and drying it naturally at room temperature to prevent the green body from being deformed;

[0049] 3) Green body sintering: the first sintering in the kiln, using reducing flame sintering, rising to a temperature of 950-1050°C, and firing time ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A glazing technology for purple-sand tea sets relates to the technical field of purple sand and comprises the following technological steps: 1) preparing a green body, specifically taking purple sand at Huainan area of Anhui province of China as a main material to prepare the green body; 2) taking out the green body, baking to dry at a room-temperature environment, so as to prevent deformation of the green body; 3) sintering the green body, specifically for first sintering in a kiln, employing reduction flame for sintering, heating to 950-1050 DEG C, and sintering for 16-18 h, so as to mainly eliminate humidity and remove alkali in the green body; 4) keeping warm for 10-20 min, naturally cooling and discharging from the kiln; 5) uniformly glazing the surface of the green body; and 6) sintering the glazed green body, specifically for secondary sintering in a kiln, employing reduction flame for sintering, sintering at 130 DEG C for 20 h, keeping warm for 10-20 min, and naturally cooling and discharging out of the kiln. The technology is simple, and by adding compositions such as shells, bluestone and the like, the sintered tea set has spots on the surface and has beautiful color.

Description

technical field [0001] The invention relates to the technical field of purple sand, in particular to a glaze and a glazing process for a purple sand tea set. Background technique [0002] Zisha products, also known as Zisha ware and Zisha pottery, are ceramic products made of special clay, which can be made into various ceramic products commonly used in daily life. Zisha tea set is a kind of pottery tea set. It is dense and hard, with natural mud color. Most of them are purple sand, and there are also red sand and white sand. The fire temperature of finished pottery is 1100-1200 ℃, without water absorption, and the sound is rough and rhyme is long. It is cold-resistant and heat-resistant, making tea without the taste of cooked soup, and can keep the fragrance, and the heat transfer is slow, so it is not easy to scald your hands, and it will not burst when you use it to stew tea. Therefore, there was a saying in history that "a pot weighs no more than two, and the price wei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 卢群山卢涛张茜文
Owner 卢群山
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap