A kind of modified calcium carbonate that can be used as sound-absorbing filler and preparation method thereof

A calcium carbonate, modified technology, applied in the direction of fibrous fillers, chemical instruments and methods, inorganic pigment treatment, etc., can solve problems such as defects, cracks, and the temperature window of nano-calcium carbonate becomes smaller, and achieve large specific surface area and increase The effect of dispersion performance and excellent sound absorption performance

Active Publication Date: 2016-01-06
广西贺州市科隆粉体有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of dispersants and surface modifiers greatly reduces the temperature window of nano-calcium carbonate, because commonly used dispersants and coupling agents are easy to decompose at high temperatures, causing bubbles, cracks, defects, deformation, etc., thus Affect the appearance, heat resistance and mechanical properties of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified calcium carbonate that can be used as sound-absorbing filler and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] specific implementation plan

[0013] The present invention will be described in detail below through specific examples.

[0014] A modified calcium carbonate that can be used as a sound-absorbing filler, prepared from the following raw materials in parts by weight (kg): calcium carbonate 90, nano hollow microspheres 4, aluminum silicate fiber cotton 3, wild rice straw powder 3, expanded pearls Rock 2, activated alumina 3, ammonium carbonate 2, polycarbonate 6, natural rubber latex 5, sodium α-alkenyl sulfonate 1, modified titanium dioxide 3;

[0015] The modified titanium dioxide is made of the following raw materials in parts by weight (kg): aluminum hydroxide 2, nano titanium dioxide 50, silicon carbide 4, methyl methacrylate 5, antimony trioxide 3, terephthalic acid 3, horse Dioctyl maleate 3, ethylene glycol 5, water 50; the preparation method is to first add methyl methacrylate, nano-titanium dioxide, aluminum hydroxide, ethylene glycol, and water and stir evenly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses modified calcium carbonate serving as a sound absorbing filler. The modified calcium carbonate is characterized by being prepared from the following raw materials in parts by weight: 90-95 parts of calcium carbonate, 4-6 parts of nanometer hollow microspheres, 3-5 parts of aluminum silicate fiber cotton, 3-4 parts of zizania aquatica straw powder, 2-4 parts of expanded perlite, 3-4 parts of activated aluminum oxide, 2-3 parts of ammonium carbonate, 6-8 parts of polycarbonate, 5-6 parts of natural latex, 1-2 parts of alpha-vinyl sodium sulfonate and 3-4 parts of modified titanium dioxide. The modified calcium carbonate disclosed by the invention has excellent sound absorption performance due to addition of the nanometer hollow microspheres and the aluminum silicate fiber cotton, has a large specific surface area as well as sound absorption and adsorption effects due to addition of plant fibers and natural substances, and has increased dispersion performance due to addition of the modified titanium dioxide, so the modified calcium carbonate is applicable to production of additives including sound absorbing bricks, sound absorbing plates, coatings and the like.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a modified calcium carbonate which can be used as a sound-absorbing filler and a preparation method thereof. Background technique [0002] Calcium carbonate is a very important functional inorganic filler, which is widely used in industrial fields such as plastics, rubber, coatings and papermaking. In the application field of calcium carbonate, most products belong to the category of polymers, such as plastics, rubber, adhesives, coatings, etc., and occupy an important market share. Modifiers play an important role in the performance and application of nano calcium carbonate. For example, the addition of dispersant can reduce the agglomeration of nanoparticles and improve the dispersion; the addition of surface modifier can improve the compatibility of nano-calcium carbonate in the polymer system. It can be seen that dispersants and surface modifiers are crucial for the applic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/02C09C3/06C09C3/10C09C3/08C09C1/36
Inventor 朱蕊许小林
Owner 广西贺州市科隆粉体有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com