Yellow-gray quick-drying anti-corrosive paint for galvanized stainless pipe fitting and preparation method thereof

A technology of stainless steel and anti-corrosion paint, applied in anti-corrosion coatings, coatings, etc., can solve the problems of poor corrosion resistance, easy peeling of spray film and paint layer, poor adhesion, etc., to improve anti-corrosion performance, increase anti-rust and Corrosion resistance, the effect of increasing adhesion

Inactive Publication Date: 2014-09-10
SHANDONG RUIBANG COATING TECH
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional process uses electrostatic powder spraying and high-pollution environment painting to prevent the chemical change, damage and corrosion of the galvanized layer, but the sprayed film and paint layer are easy to fall off after the above process is used for a long time. Not good, poor corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Yellow-gray quick-drying anti-corrosive paint for galvanized stainless pipe fitting and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] A method for preparing a yellow-gray quick-drying anti-corrosion paint for galvanized stainless steel pipe fittings, comprising the following steps:

[0018] 1) Add the acrylic resin into the material preparation tank, and start the disperser to stir;

[0019] 2) Slowly add dispersant, titanium dioxide, medium chrome yellow, high-pigment carbon black and 1 / 3 xylene under stirring, and grind until the fineness is less than 20 μm after stirring evenly;

[0020] 3) Take it to the paint mixing tank, add modified resin, leveling agent, adhesion aid, preservative, butyl acetate and the remaining xylene, stir well, and it is ready.

[0021] In the following examples, the technical indicators of the acrylic resin used are as follows:

[0022] serial number

project

technical indicators

1

Exterior

clear transparent liquid

2

Viscosity (format tube) S

20-30

[0023] 3

Finenessum≤

15

4

Colorimetric...

Embodiment 1

[0028] The invention provides a yellow-gray quick-drying anti-corrosion paint for galvanized stainless steel pipe fittings, which is prepared from the following components in weight percentage: 39% of acrylic resin, 13% of modified resin, 11% of titanium dioxide, and 4% of medium chrome yellow %, high pigment carbon black 0.25%, dispersant 0.75%, leveling agent 0.4%, adhesion aid 1.4%, preservative 0.7%, butyl acetate 13% and xylene 16.5%.

[0029] The above-mentioned preparation method for the yellow-gray quick-drying anticorrosion paint for galvanized stainless steel pipe fittings comprises the following steps:

[0030] 1) Add the acrylic resin into the material preparation tank, and start the disperser to stir;

[0031] 2) Slowly add dispersant, titanium dioxide, medium chrome yellow, high-pigment carbon black and 1 / 3 xylene under stirring, and grind until the fineness is less than 20 μm after stirring evenly;

[0032] 3) Take it to the paint mixing tank, add modified resi...

Embodiment 2

[0034] This embodiment provides a yellow gray quick-drying anti-corrosion paint for galvanized stainless steel pipe fittings, which is made from the following components in percentage by weight: 38% acrylic resin, 14% modified resin, 10% titanium dioxide, medium chrome yellow 5%, high pigment carbon black 0.2%, dispersant 0.6%, leveling agent 0.2%, adhesion aid 1.5%, preservative 0.5%, butyl acetate 12% and xylene 18%.

[0035] The above-mentioned preparation method for the yellow-gray quick-drying anticorrosion paint for galvanized stainless steel pipe fittings comprises the following steps:

[0036] 1) Add the acrylic resin into the material preparation tank, and start the disperser to stir;

[0037] 2) Slowly add dispersant, titanium dioxide, medium chrome yellow, high-pigment carbon black and 1 / 3 xylene under stirring, and grind until the fineness is less than 20 μm after stirring evenly;

[0038] 3) Take it to the paint mixing tank, add modified resin, leveling agent, ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a yellow-gray quick-drying anti-corrosive paint for galvanized stainless pipe fittings. The yellow-gray quick-drying anti-corrosive paint is prepared from the following components in percentage by weight: 35%-45% of acrylic resin, 10%-15% of modified resin, 10%-12% of titanium dioxide, 3%-5% of medium chrome yellow, 0.2%-0.3% of high-pigment carbon black, 0.5%-1% of dispersing agents, 0.2%-0.5% of flatting agents, 1%-1.5% of adhesive force auxiliary agents, 0.5%-1% of anti-corrosion agents, 10%-15% of butyl acetate and 15%-20% of dimethyl benzene. The invention also provides a preparation method of the yellow-gray quick-drying anti-corrosive paint for the galvanized stainless pipe fittings. 10%-15% by weight of the modified resin, the adhesive force auxiliary agents and the anti-corrosion agents are additionally used for the formula of the yellow-gray quick-drying anti-corrosive paint, so that a composition formed by the components and other components is increased in adhesive force and improved in anti-corrosive property; the galvanized stainless pipe fittings show the yellow-gray and are attractive in appearance after being coated with the yellow-gray quick-drying anti-corrosive paint.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to a yellow-gray quick-drying anti-corrosion coating for galvanized stainless steel steel pipe fittings and a preparation method thereof. Background technique [0002] Galvanized stainless steel pipe is a welded steel pipe with a hot-dip or electro-galvanized layer on the surface. Galvanizing can increase the corrosion resistance of the steel pipe and prolong its service life. Galvanized pipes are widely used. In addition to being used as pipeline pipes for general low-pressure fluids such as water, gas, and oil, they are also used as oil well pipes and oil pipelines in the petroleum industry, especially offshore oil fields, and oil heaters and condensation pipes for chemical coking equipment. Pipes for coolers, coal distillation washing oil exchangers, trestle piles, and support pipes for mine tunnels, etc. [0003] For the galvanized layer, zinc is a relatively ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/08C09D7/12
Inventor 于龙涛盖成哲
Owner SHANDONG RUIBANG COATING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap