Manufacturing process of fluorine element release film

A fluorine release film and manufacturing process technology, applied in the field of release isolation materials, to achieve good isolation effect, good aging resistance effect, and stable release force

Active Publication Date: 2014-09-24
FOSHAN NANHAI DISTRICT XINYONGTAI ADHESIVE PROD CO LTD
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to incomplete statistics, the shipment of silicone protective tape reached 173 million square meters in 2012, including: 53 million square meters of protective film for plastic parts shipment, 64 million square meters of optical film cutting carrier film, and 18 million square meters of protective film for FPD shipment. 10,000 ㎡, functional protective film 38 million ㎡, and high temperature lamination protection has not yet been counted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] A manufacturing process of fluorine release film, characterized in that it comprises the following steps:

[0011] The first is to prepare the paint: mix the fluorine paint main agent and n-heptane solvent at a ratio of 1:6-1:8. The utensils used in the mixing must not be polluted. During the mixing process, the n-heptane solvent must be put first, and then slowly Add the main agent of fluorine paint at a speed of 100-150ml / min, stir for 10-15 minutes after adding, then add bridging agent and anchoring agent at a speed of 50-60ml / min, stir for 5-6 minutes after adding , and then add the catalyst at a speed of 30-40ml / min and stir for 3 minutes. During the stirring process, keep the temperature at 25-30°C and the relative humidity at 50-60%;

[0012] Next, prepare a fluorine release film: 1. Select a PET film, specifically a polyethylene terephthalate film, and corona treat the PET film so that its surface tension is above 56 Dahns to increase the surface area of ​​the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing process of a fluorine element release film, which comprises the following steps: 1) preparing a coating, that is, mixing a fluorine element coating main agent with a n-heptane solvent according to a ratio of 1:6-1:8, adding a bridging agent and an anchoring agent, then adding a catalyst and stirring; 2) preparing the fluorine element release film, that is, coating the above coating on a PET raw film in a precise coating manner, performing an curing reaction in an oven, then cooling and rolling to obtain the finished product. The PET film used in the invention is strict in material selection criterion; the selected main material is available on the market; the blending and preparation steps of the coating solution are strict; a precise coating mode is adopted to allow the coating of the whole film to be quite uniform; after curing and drying, the release force of the product is very stable; the product is good in aging resistance, is very suitable for all organic silica gel protection adhesive tapes, and can be used in high-temperature high-humidity environment with good isolation effect.

Description

technical field [0001] The invention relates to a novel release type isolation material of a silicone belt, in particular to a manufacturing process of a fluorine release film. Background technique [0002] At present, silicone release paper (membrane) is commonly used in the market, and silicone is used as a release agent. Therefore, silicone release paper (membrane) cannot be used as an isolation material on a silicone tape, because they belong to silicon series, usually such materials are imported from Japan, Taiwan, etc., which is not conducive to the development of our country in this field. According to Taiwan's Industrial Technology Research Institute, due to the rapid development of LED and OLED displays, touch-screen mobile phones, and large electronic blackboards, they are used in the production process, process transfer protection, product shipment surface protection, instrumentation surface protection, and high-temperature welding. Silicone tapes are widely used...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/06B32B27/36B32B33/00
Inventor 朱锦佐
Owner FOSHAN NANHAI DISTRICT XINYONGTAI ADHESIVE PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products