Manufacturing technology of PBT used for loose tube of optical cable

A production process and technology of loose tubes, applied in the field of PBT production process for optical cable loose tubes, can solve the problems that cannot meet the production requirements of large loose tubes, and achieve the effects of increasing flexibility, facilitating cable formation, and accelerating crystallization speed

Inactive Publication Date: 2014-10-22
YANGZHOU JINSEN OPTOELECTRONICS
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ribbon optical cable is a loose tube with several optical fibers in parallel. It requires a loose tube with a large diameter, a stable aperture, and appropriate rigidity and flexibility. Simply use ordinary PBT (polybutylence terephthalate, polyethylene terephthalate) butanediol ester) cannot meet the production requirements of large loose tubes, and this has become a technical problem to be solved urgently by those skilled in the art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The present invention processes according to the following steps:

[0014] 1) Preliminary treatment: take PBT for thickening;

[0015] 2) Stirring once: put the thickened PBT into a high-speed mixer, and add 5# white oil, the mass ratio of the white oil to the PBT is 1‰:1, and the stirring time is 10 minutes;

[0016] 3) Secondary stirring: put the polypropylene nucleating agent NA-11 into a high-speed mixer, the mass ratio of the polypropylene nucleating agent to the PBT is 1‰:1, and the stirring time is 15 minutes;

[0017] 4) Dust removal: Put the materials after secondary stirring into the vibrating screen for dust removal; complete.

Embodiment 2

[0019] The present invention processes according to the following steps:

[0020] 1) Preliminary treatment: take PBT for thickening;

[0021] 2) Stirring once: put the thickened PBT into a high-speed mixer, and add 5# white oil, the mass ratio of the white oil to the PBT is 3‰:1, and the stirring time is 5 minutes;

[0022] 3) Secondary stirring: put the polypropylene nucleating agent NA-11 into a high-speed mixer, the mass ratio of the polypropylene nucleating agent to the PBT is 11.5‰:1, and the stirring time is 8 minutes;

[0023] 4) Dust removal: Put the materials after secondary stirring into the vibrating screen for dust removal; complete.

Embodiment 3

[0025] The present invention processes according to the following steps:

[0026] 1) Preliminary treatment: take PBT for thickening;

[0027] 2) Stirring once: put the thickened PBT into a high-speed mixer, and add 5# white oil, the mass ratio of the white oil to the PBT is 2‰:1, and the stirring time is 8 minutes;

[0028] 3) Secondary stirring: put the polypropylene nucleating agent NA-11 into a high-speed mixer, the mass ratio of the polypropylene nucleating agent to the PBT is 1.25‰:1, and the stirring time is 12 minutes;

[0029] 4) Dust removal: Put the materials after secondary stirring into the vibrating screen for dust removal; complete.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A manufacturing technology of PBT used for a loose tube of an optical cable. The invention relates to the technical field of high molecular materials and provides a manufacturing technology of PBT used for a loose tube of an optical cable. The PBT is stable in shape, good in flexibility and high in processing efficiency. The manufacturing technology includes following steps: 1) preliminary treatment; 2) a primary stirring process; 3) a secondary stirring process; and 4) dust removal. According to the invention, a viscosity-increasing process is carried out to a PBT raw material and 5# white oil is added during the primary stirring process. By means of the white oil, flexibility of the material can be enhanced effectively, thereby increasing smoothness of a surface of the loose tube and being beneficial to cabling. A polypropylene nucleating agent is added during the secondary stirring process. By means of the polypropylene nucleating agent, a crystallization speed of the material can be effectively increased, thereby significantly reducing a production time of the material and improving a processing efficiency. The PBT material, after being processed, can satisfy a production requirement and a technical standard of the loose tube.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a production process of PBT for optical cable loose tubes [0002] improvement of. Background technique [0003] With the rapid development of the communication industry, the demand for ribbon optical cables has soared. Ribbon optical cable is a loose tube with several optical fibers in parallel. It requires a loose tube with a large diameter, a stable aperture, and appropriate rigidity and flexibility. Simply use ordinary PBT (polybutylence terephthalate, polyethylene terephthalate) Butanediol ester) can not meet the production requirements of large loose tubes, and this has become a technical problem to be solved urgently by those skilled in the art. Contents of the invention [0004] Aiming at the above problems, the present invention provides a PBT production process for optical cable loose tube with stable shape, good flexibility and high processing efficie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K5/01
Inventor 王君李兆顺
Owner YANGZHOU JINSEN OPTOELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com