Lubricating grease combination and preparing method of lubricating grease combination

A technology of grease composition and solid lubricant, which is applied in the field of grease, can solve problems such as reduced lubricating effect and paint failure of recliner, and achieves the effects of excellent extreme pressure performance, small operating torque at low temperature, and high transmission efficiency

Active Publication Date: 2014-11-12
CHINA PETROLEUM & CHEM CORP
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The grease composition uses polyalphaolefin as base oil, organically modified bentonite as thickener, antioxidant, rust inhibitor, corrosion inhibitor, extreme pressure antiwear agent and solid lubricant as additives, so that The obtained grease composition has good high and low temperature performance in a wide temperature range, and also has good extreme pressure and anti-wear performance. The loss will cause the recliner paint to fail; and during the welding process of the seat recliner, the loss of oil separation will reduce the lubrication effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lubricating grease combination and preparing method of lubricating grease combination

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The invention provides a kind of preparation method of lubricating grease composition, comprises the following steps:

[0027] mixing 40wt% to 50wt% of base oil, 2wt% to 10wt% of thickener and 35wt% to 40wt% of solid lubricant and performing homogenization treatment to obtain a grease composition precursor;

[0028] The grease composition precursor is mixed with 0.05wt%-0.50wt% structure stabilizer, 0.5wt%-2.0wt% metal deactivator, 2wt%-8wt% extreme pressure anti-wear agent and 0.2wt% ~2.0 wt% antioxidant was mixed to obtain a grease composition.

[0029] The present invention carries out homogenization treatment after mixing base oil, thickener and solid lubricant, and then mixes with described structural stabilizer, metal passivator, extreme pressure antiwear agent and antioxidant, and homogenization treatment makes each The components are uniformly dispersed, the solid-liquid phase is not separated, and a lubricating grease composition with a good colloidal structur...

Embodiment 1

[0062] Add 8kg of fluororesin to the base oil, the base oil includes 40kg of polyalphaolefin and 5kg of dipentaerythritol low carbonate, raise the temperature to 120°C, then add 35kg of calcium carbonate, stir for 30min, and use a colloid mill to cut the above materials circularly 2h, obtain the grease composition precursor;

[0063] Cool the grease composition precursor to 100°C, add 3kg molybdenum disulfide, 0.5kg polymethacrylate, 1.0kg N,N-disalicylidene propylenediamine, 3kg zinc dithiophosphate, 4kg molybdenum dithiophosphate and 0.5kg 2,6-di-tert-butylphenol, after stirring for 60min, take out the material from the colloid mill, grind the material twice with a three-wheel grinder, Obtain a grease composition;.

[0064] The present invention conducts a performance test on the obtained lubricating grease composition, and the test results are shown in Table 1. Table 1 shows the performance test results of the lubricating grease composition obtained in Examples 1-3 of the ...

Embodiment 2

[0066] Add 3kg of bentonite to the base oil, the base oil includes 30kg of polyalphaolefin and 20kg of hydrogenated base oil, raise the temperature to 160°C, add 40kg of melamine cyanurate, stir for 30min, and use a colloid mill to circulate and shear the above materials for 3h to obtain Grease composition precursors;

[0067] Cool the grease composition precursor to 80°C, add 0.5kg glycerin, 1.0kg N-N di-n-butylaminomethylene benzotriazole, 2kg dithiocarbamate, 3 kg of molybdenum dithiocarbamate and 0.5 kg of alkyl diphenylamine were stirred for 60 minutes, then the material was taken out from the colloid mill, and the material was ground 3 times with a three-wheel grinder to obtain a grease composition;

[0068] The present invention conducts a performance test on the obtained lubricating grease composition, and the test results are shown in Table 1. Table 1 shows the performance test results of the lubricating grease composition obtained in Examples 1-3 of the present inven...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparing method of a lubricating grease combination. The preparing method includes the steps that 40wt% to 50wt% of base grease, 2wt% to 10wt% of thickening agents and 35wt% to 40wt% of solid lubricants are mixed to be homogenized to obtain a lubricating grease combination precursor; the lubricating grease combination precursor is mixed with 0.05wt% to 0.50wt% of structure stabilizers, 0.5wt% to 2.0wt% of metal deactivators, 2wt% to 8wt% of extreme-pressure anti-wear agents and 0.2wt% to 2.0wt% of antioxidants to obtain the lubricating grease combination. By means of the preparing method, the base grease, the thickening agents and the solid lubricants are homogenized and then mixed with the structure stabilizers, the metal deactivators, the extreme-pressure anti-wear agents and the antioxidants; due to homogenizing, the components are evenly dispersed, solid-liquid phases are not separated, the lubricating grease combination of the good colloid structure is obtained, and the steel-net separated grease amount of the lubricating grease combination is small.

Description

technical field [0001] The invention relates to the technical field of lubricating grease, in particular to a lubricating grease composition and a preparation method thereof. Background technique [0002] Grease, commonly known as butter or tallow, is a stable solid or semi-solid product formed by dispersing a thickener in base oil. The types of grease are: calcium-based grease, sodium-based grease, calcium-sodium-based grease, general-purpose lithium-based grease, etc. Grease can be used on the friction part of mechanical parts to reduce the friction of the contact surface of mechanical parts, protect and seal the contact surface; it can also be used on the metal surface to form a protective layer on the metal surface to prevent the metal surface from rust and corrosion. With the development of industry, the requirements for the performance of lubricating grease in various fields are also increasing. [0003] The Chinese patent application number 201210413343.1 discloses...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M169/04C10N30/06C10N50/10
Inventor 欧阳秋康健卢现菊赵玉贞田忠利
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com