High silicon molybdenum ductile iron material

A high-silicon molybdenum and ductile iron technology, applied in the field of ductile iron materials, can solve the problems of easy generation of fragmented graphite and graphite deterioration layer, difficult to meet the requirements of metallographic structure, high brittleness and other problems, and achieves elimination of graphite deterioration layer, uniform distribution, The effect of tensile strength improvement

Active Publication Date: 2017-10-27
CRRC CHANGZHOU AUTO PARTS CO LTD +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the biggest problem currently existing in high-silicon-molybdenum ductile iron is that due to the high content of silicon and molybdenum, it is brittle, prone to produce fragmented graphite and graphite deterioration layers, and prone to micro-shrinkage, which leads to metallographic Organizations Difficult to Meet
However, the addition of vanadium and chromium is easy to form carbides, making it more brittle and more likely to produce fragmented graphite and microscopic shrinkage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High silicon molybdenum ductile iron material
  • High silicon molybdenum ductile iron material
  • High silicon molybdenum ductile iron material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1)

[0025] The composition of the high-silicon-molybdenum ductile iron material in this embodiment is shown in Table 1.

[0026] Table 1

[0027] element

C / %

Si / %

Mo / %

Cr / %

V / %

Mn / %

Mg / %

P / %

S / %

Fe / %

content

3.13

4.57

0.63

0.44

0.34

0.22

0.057

0.022

0.006

margin

[0028] The mechanical properties of the high-silicon-molybdenum ductile iron material are shown in Table 2.

[0029] Table 2

[0030] Tensile strength / MPa

Yield strength / MPa

Elongation / %

Hardness / HBW5 / 750

740

520

11.5

252

[0031] The preparation method of the high silicon molybdenum ductile iron material has the following steps:

[0032] ① Weigh the charge according to the weight percentage in Table 3 for use, and the total weight of the charge is 3 tons.

[0033] table 3

[0034] raw material

pig iron

scrap steel

Return charge

Ferrosilicon

Ferrochrome

Ferr...

Embodiment 2~ Embodiment 4)

[0046] Each example is basically the same as Example 1, except that the composition and mechanical properties of the high-silicon-molybdenum ductile iron material are shown in Table 5.

Embodiment 5)

[0048] This example is basically the same as Example 1, except that: the composition and mechanical properties of the high-silicon-molybdenum ductile iron material, especially a small amount of Sn and Sb are added during the process of pouring molten iron into the ladle. The specific results are shown in Table 5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-silicon-molybdenum ductile iron material. The high-silicon-molybdenum ductile iron material contains: C: 2.90%-3.35%; Si: 4.40%-4.80%; Mo: 0.50%-0.75%; Cr: 0.30% to 0.50%; V: 0.20% to 0.45%; Mn: 0.10% to 0.30%; Mg: 0.04% to 0.07%; P: ≤0.07%; S: ≤0.02%; the rest is Fe. The tensile strength of the high-silicon-molybdenum ductile iron material is ≥710MPa, the yield strength is ≥500MPa, the elongation is ≥10%, and the hardness is 230-265HBW5 / 750. The high silicon molybdenum ductile iron material also contains trace amounts of Sn and Sb. The high-silicon-molybdenum ductile iron material of the present invention eliminates fragmented graphite and graphite deterioration layer, ensures the spheroidization level at different wall thicknesses, and simultaneously solves defects such as micro-shrinkage porosity.

Description

[0001] This application is a divisional application of the invention patent application with the application number 201210499812.6 and the application date is November 29, 2012, and the invention name is "high silicon molybdenum nodular iron material and its preparation method". technical field [0002] The invention relates to a ductile iron material, in particular to a high-silicon-molybdenum nodular iron material used for high-temperature-resistant parts of automobiles. Background technique [0003] High-silicon-molybdenum ductile iron is widely used in automotive high-temperature resistant parts such as exhaust pipes and turbine shells due to its high high-temperature strength, thermal fatigue resistance, excellent oxidation resistance, growth and good high-temperature creep resistance. . With the improvement of people's awareness of environmental protection and regulations, HT250 and even vermicular iron materials can no longer meet the performance requirements of engin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C37/10
Inventor 高顺程凤军宋彦丞唐中权
Owner CRRC CHANGZHOU AUTO PARTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products