Ceramic product, preparation method thereof, prepared inner container of drinking fountain and drinking fountain

A technology of ceramic products and drinking fountains, applied in the field of ceramics, can solve the problems of cleaning and inconvenient use, and achieve the effects of saving freight, adjusting metabolism, and easy source of raw materials

Inactive Publication Date: 2014-12-17
胡桂亮
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing water dispensers all use filter elements. If you need multiple minerals in the water or want to use alkaline water, you need to let the water pass through multiple filter elements, and you need to change the filter elements frequently, which is inconvenient to clean and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic product, preparation method thereof, prepared inner container of drinking fountain and drinking fountain

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] A method for preparing a ceramic product, comprising the steps of:

[0033] (1) Take each raw material according to the stated ratio, add it into a ball mill for ball milling for 18-22 hours to reach a fineness of 120 mesh, and obtain a mixed slurry;

[0034] (2) Pour the mixed slurry in step (1) into the prepared plaster mold, place it at 35 degrees for 1-2 hours and continue to place it for 3-5 days;

[0035] (3) Remove the dried green body from the mold, add water for 3-5 times, and polish the burrs to make the green body clean and smooth;

[0036] (4) Put the green body into the kiln, raise the temperature to 1200-1300 degrees within 3 hours, and fire for 8-10 hours. After the firing is completed, naturally cool to room temperature to obtain the finished product.

[0037] Fill the finished product with water and let it stand for 1-2 hours, collect the seepage water, and change weak alkaline or neutral water into weak alkaline water.

[0038] The present invention ...

Embodiment 1

[0046] Embodiment 1 Utilizes purple sand pottery of the present invention to prepare water dispenser liner

[0047] Take 10 parts of feldspar, 20 parts of purple sandstone, 15 parts of stick clay, 30 parts of quartz, 20 parts of clay, 15 parts of meteorite, 15 parts of medical stone and 10 parts of Nishan stone.

[0048] Its preparation method is as follows:

[0049] (1) Take each raw material according to the stated ratio, add it into a ball mill for ball milling for 22 hours to reach a fineness of 120 mesh, and obtain a mixed slurry;

[0050] (2) Pour the mixed slurry in step (1) into the plaster mold of the inner tank of the water dispenser, place it for 2 hours and then continue to place it for 5 days to dry at room temperature

[0051] (3) Remove the dried green body from the mold, replenish water 5 times, and polish the burrs to make the green body clean and smooth;

[0052] (4) Put the green body into the kiln, raise the temperature to 1260 degrees within 3 hours, and...

Embodiment 2

[0055] Embodiment 2 Utilizes purple sand pottery of the present invention to prepare teacup liner

[0056] Take 25 parts of feldspar, 10 parts of purple sandstone, 10 parts of stick clay, 15 parts of quartz, 15 parts of clay, 10 parts of meteorite, 30 parts of medical stone and 30 parts of Nishan stone.

[0057] Its preparation method is as follows:

[0058] (1) Take each raw material according to the stated ratio, add it into a ball mill for ball milling for 20 hours to reach a fineness of 120 mesh, and obtain a mixed slurry;

[0059] (2) Pour the mixed slurry in step (1) into the plaster mold of the prepared teacup liner, place it for 2 hours and then continue to place it for 4 days to dry at room temperature;

[0060](3) Remove the dried green body from the mold, add water 4 times, and polish the burrs to make the green body clean and smooth;

[0061] (4) Put the green body into the kiln, raise the temperature to 1230 degrees within 3 hours, and fire for 9 hours in total....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic product, a preparation method thereof, a prepared inner container of a drinking fountain and the drinking fountain. The ceramic product is prepared from the following raw materials in parts by weight: 10-25 parts of feldspar, 10-20 parts of purple sand, 10-15 parts of attapulgite, 15-30 parts of quartz, 10-25 parts of clay, 10-20 parts of stone needle, 15-30 parts of Maifan stone and 10-30 parts of Nishan stone. The ceramic product disclosed by the invention has the beneficial effects that the purple sand, the Maifan stone and broken powder from a variety of ore plants are taken as raw materials, and the purple sand, the Maifan stone, the stone needle and the Nishan stone contain trace elements which are beneficial to human bodies, so that the ceramic product can adsorb peculiar small in running water and poor-quality water, activate the running water and the poor-quality water into active mineralized water, increase the oxygen content in water, generate weak alkaline water with the pH value of 7.3-8.0, regulate the acid-base balance of the human body, realize an anti-oxidation effect, remove excess free radical rubbish in the human body, enable people to absorb more minerals by long-term drinking and adjust metabolism.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a ceramic product, a preparation method thereof, and a prepared water dispenser liner and water dispenser. [0002] Background technique [0003] With the improvement of living standards and the gradual seriousness of environmental pollution, people have higher and higher requirements for water quality. The pure water nutrients that people quote now are relatively simple. Mineral water dispensers or alkaline water dispensers also appear on the market at present. However, existing water dispensers all use filter elements. If there are multiple minerals in the water or if you want to use alkaline water, you need to let the water pass through multiple filter elements, and you need to change the filter elements frequently, which is inconvenient to clean and use. [0004] Contents of the invention [0005] In order to meet the needs of convenient use, the embodiment of the pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/22C04B33/24C04B35/18C04B35/622A47J31/44A47J31/00A47J31/54
Inventor 胡桂亮
Owner 胡桂亮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More