Composition for surface cleaning of platinum-osmium alloy

A surface cleaning and composition technology, which is applied in the field of metal material cleaning, can solve problems such as difficult processing, and achieve good cleaning effect and low solvent residue

Inactive Publication Date: 2014-12-17
JIANGSU KANG BAISI MECHANICAL TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Melting with argon protection in a high-frequency furnace, cold rolling after hot rolling, and alloys containing more than 10% osmium are difficult to process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The composition for cleaning the surface of platinum-osmium alloy is prepared by mixing the following components by weight: 10 parts of dimethylolbenzoic acid, 30 parts of diethylene glycol dimethyl ether, 5 parts of N-methylpyrrolidone, silicic acid 50 parts of aluminum, 20 parts of sodium dodecylsulfonate, 30 parts of 2-ethylhexanol, 20 parts of dimethylimidazole, 5 parts of quaternary ammonium salt, [Hmim][HSO 4 ] 100 copies.

[0021]

Embodiment 2

[0023] The composition for cleaning the surface of platinum-osmium alloy is prepared by mixing the following components by weight: 30 parts of dimethylol benzoic acid, 50 parts of diethylene glycol dimethyl ether, 10 parts of N-methylpyrrolidone, silicic acid 70 parts of aluminum, 30 parts of sodium lauryl sulfonate, 40 parts of 2-ethylhexanol, 30 parts of dimethylimidazole, 10 parts of stearic acid, [Bmim][Tf 2 N] 200 copies.

[0024]

Embodiment 3

[0026] The composition for cleaning the surface of platinum-osmium alloy consists of the following components by weight: 20 parts of dimethylol benzoic acid, 40 parts of diethylene glycol dimethyl ether, 8 parts of N-methylpyrrolidone, and 60 parts of aluminum silicate Parts, 25 parts of sodium dodecylsulfonate, 35 parts of 2-ethylhexanol, 25 parts of dimethylimidazole, 8 parts of sodium dodecylbenzenesulfonate, [Bmim][PF 6 ] 150 copies.

[0027]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

A composition for surface cleaning of a platinum-osmium alloy comprises the following ingredients by weight: 10-30 parts of dihydroxymethyl benzoic acid, 30-50 parts of diethylene glycol dimethyl ether, 5-10 parts of N-methyl pyrrolidone, 50-70 parts of aluminum silicate, 20-30 parts of sodium dodecyl sulfonate, 30-40 parts of 2-ethyl hexanol, 20-30 parts of dimethyl imidazole, 5-10 parts of a surface active agent and 100-200 parts of ionic liquid. Compared with the conventional cleaning agent, the composition for surface cleaning of the platinum-osmium alloy, provided by the invention, has a good cleaning effect on grease, ensures that the residual quantity of a solvent is lower than the conventional technical standard, doesn't produce poisonous and volatile ingredients, and cannot react with metal.

Description

[0001] technical field [0002] The invention belongs to the technical field of metal material cleaning, in particular to a composition for cleaning the surface of platinum-osmium alloy. [0003] Background technique [0004] Commonly used chemical cleaning agents can be classified in different ways. For example, according to its chemical composition, it can be divided into inorganic chemical cleaning agents and organic chemical cleaning agents; some cleaning agents may have different effects on different dirt, or have two or more effects on the same dirt, then They should be classified according to their main function under normal circumstances. The classification of cleaning agents is often classified according to the material: aluminum parts cleaning agent, steel cleaning agent, copper cleaning agent, plastic cleaning agent. Water and non-aqueous solvents: Dirt solvents refer to substances that can remove the dirt of the cleaning object in a dissolved or dispersed form...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G5/036
Inventor 陈凌王琰任琪程晓
Owner JIANGSU KANG BAISI MECHANICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products