Preparation method for high-precision resister on LTCC base-plate surface

A substrate surface, high-precision technology, applied in the direction of resistance manufacturing, resistors, coating resistance materials, etc., can solve the problems of poor electrode solder resistance, low resistance value accuracy, film adhesion problems, etc., to achieve good solder resistance , High line precision, small line effect

Active Publication Date: 2014-12-17
NO 54 INST OF CHINA ELECTRONICS SCI & TECH GRP
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the surface resistance of existing LTCC substrates is usually prepared by screen printing and sintering, which has some disadvantages: (1) the resistance accuracy is low, generally 20% to 30%; (2) the adhesion of the film layer is limited. (3) Poor electrode solder resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] A method for preparing high-precision resistance on the surface of a LTCC substrate is specifically implemented as follows:

[0037] (1) Prepare a multilayer LTCC substrate, grind and polish the surface of the LTCC substrate with a grinder and a polishing machine;

[0038] (2) Soak the LTCC substrate treated in step (1) with acetone for 3 times, the total soaking time is not less than 30min, and ultrasonic treatment is performed in the first and last 1min to 3min of the first soaking process; the second and third soaking process Ultrasonic treatment is carried out in the last 1min to 3min of the process; the LTCC substrate is taken out from the acetone, and then immersed in ethanol for 2 times, the total soaking time is not less than 10min, and ultrasonic treatment is performed in the first 1min of each soaking process; Take it out, spray and clean it with deionized water; dry the LTCC substrate with nitrogen; place the LTCC substrate on a hot plate for drying;

[0039...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of manufacturing of LTCC, thin films and mixed base plates, and especially relates to a preparation method for a high-precision resister on LTCC base-plate surface. The preparation method mainly comprises grinding polishing of an LTCC base plate, cleaning, cavity filling, resistor figure making, electrode figure making, annealing and resistor resistance measuring. By employing the technical scheme, the resistance precision of the surface of the LTCC base plate can be improved from original 20%-30% to 5%-10%, the electrode soldering resistance and the film-layer adhesive force are effectively improved, and the line is relatively small, the line precision is relatively high and the application frequency is relatively high.

Description

technical field [0001] The invention relates to the field of manufacturing LTCC, thin films and mixed substrates, in particular to a method for preparing high-precision resistance on the surface of an LTCC substrate. Background technique [0002] Electronic equipment is gradually developing in the direction of miniaturization, light weight, high frequency and multi-function. LTCC (low temperature co-fired ceramic) technology has three-dimensional wiring and unlimited layers, fast signal transmission speed, low loss and reliable It has been widely used in many fields due to its technical advantages such as high performance and the ability to embed passive components and reserve cavities to realize chip embedment. However, the surface resistance of existing LTCC substrates is usually prepared by screen printing and sintering, which has some disadvantages: (1) the resistance accuracy is low, generally 20% to 30%; (2) the adhesion of the film layer is limited. (3) Poor electrod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01C17/00H01C17/075H01C17/12H01C17/28
Inventor 党元兰赵飞刘晓兰徐亚新梁广华唐小平严英占卢会湘朱二涛杨宗亮王康
Owner NO 54 INST OF CHINA ELECTRONICS SCI & TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap