Salix mongolica regenerated cellulose and preparation method thereof
A technology of regenerated cellulose and Salix salix, applied to artificial filaments made of viscose, etc., to achieve the effects of increased utilization, low price, huge economic benefits and ecological benefits
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] (1) Preparation of salix wood powder: Peel and crush salix, pass through a 100-mesh sieve, dry at 80°C, cool, and put in a desiccator for later use;
[0020] (2) Preparation of salix fiber: add salix wood powder in step (1) to the autoclave, add anhydrous ethanol-nitric acid mixture, wherein the addition of nitric acid is 3%wt, and the solid-to-liquid ratio is 1:10 , heated to 120°C, stirred for 3 hours, cooled, filtered, washed with absolute ethanol for 5 times, rinsed repeatedly with deionized water, and dried;
[0021] (3) Preparation of salix pulp: use 10%wt NaOH to cook, the bath ratio is 1:10, the cooking temperature is 200°C, the time is 3h, and then 20%wt hydrogen peroxide is used for bleaching, the bleaching temperature is 100°C, and the bleaching time is 2h;
[0022] (4) Preparation of Salix salix spinning solution: Salix salix pulp is used as raw material, and the spinning solution is obtained through the steps of dipping, pressing, crushing, aging, yellowin...
Embodiment 2
[0026] (1) Preparation of salix wood powder: Peel and crush salix, pass through a 80-mesh sieve, dry at 90°C, cool, and put in a desiccator for later use;
[0027] (2) Preparation of salix fiber: add the salix wood powder in step (1) to the autoclave, add anhydrous ethanol-sulfuric acid mixture, the sulfuric acid addition is 4%wt, and the solid-to-liquid ratio is 1:5 , after heating to 120°C, stirring for 2 hours, cooling, filtering, washing with absolute ethanol for 3 times, then repeatedly rinsing with deionized water, and drying;
[0028] (3) Preparation of salix pulp: use 5%wt NaOH to cook, the liquor ratio is 1:5, the cooking temperature is 250°C, the time is 4h, and then bleached with 25%wt hydrogen peroxide, the bleaching temperature is 80°C, and the bleaching time is 1h;
[0029] (4) Preparation of Salix salix spinning solution: Salix salix pulp is used as raw material, and the spinning solution is obtained through the steps of dipping, pressing, crushing, aging, yell...
Embodiment 3
[0032] (1) Preparation of salix wood powder: Peel and crush salix, pass through a 60-mesh sieve, dry at 80°C, cool, and put in a desiccator for later use;
[0033] (2) Preparation of salix fiber: add salix wood powder in step (1) to the autoclave, add absolute ethanol-hydrochloric acid mixture, the solid-to-liquid ratio is 1:15, heat to 140°C, and stir for 3 hours , cooled, filtered, washed twice with absolute ethanol, rinsed repeatedly with deionized water, and dried;
[0034] (3) Preparation of salix pulp: use 15%wt NaOH to cook, the bath ratio is 1:10, the cooking temperature is 220°C, the time is 3h, and then 20%wt hydrogen peroxide is used for bleaching, the bleaching temperature is 80°C, and the bleaching time is 2h;
[0035] (4) Preparation of Salix salix spinning solution: Salix salix pulp is used as raw material, and the spinning solution is obtained through the steps of dipping, pressing, crushing, aging, yellowing, dissolving, degassing and filtering;
[0036] (5)...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap