Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of anhydrous lithium iodide

A technology of lithium iodide and lithium hydroxide, applied in lithium halide and other directions, can solve the problems of easy deliquescence of lithium iodide, shorten the reaction time, difficult to produce large-scale, etc., and achieve the effects of short time consumption, high product purity and precise packaging.

Active Publication Date: 2016-02-24
HUBEI BAIJIERUI ADVANCED MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies in the prior art, the technical problem to be solved in the present invention is to overcome the time-consuming and high cost of existing anhydrous lithium iodide preparation methods, technical defects such as difficulty in large-scale production and packaging difficulties. Basically, the technological process is simplified, the reaction time is greatly shortened, the difficult problem that lithium iodide is easily deliquescent in the air is solved, and a method for preparing battery-grade anhydrous lithium iodide is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of anhydrous lithium iodide
  • A kind of preparation method of anhydrous lithium iodide
  • A kind of preparation method of anhydrous lithium iodide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation method for anhydrous lithium iodide, the steps are as follows:

[0028] (1) Add 8L of pure water into the reactor, then add 7.0Kg of iodine element, stir for 15 minutes to dissolve completely, then add 2.25Kg of recrystallized lithium hydroxide, stir for 5 minutes, slowly add 80wt% hydrazine hydrate into the reactor , until the solution just turns white (the amount of 80wt% hydrazine hydrate is about 0.8Kg), stabilize for 10 minutes, then add a small amount of iodine, until the solution just turns red, then add a small amount of 8wt% hydrazine hydrate to turn the color of the solution back to white , and then use recrystallized lithium hydroxide solid to adjust the pH value to 7.5, heat, evaporate and concentrate to 124 ° C, and the volume is concentrated to 1 / 2 of the original volume, then cooled to room temperature with cold water, and filtered to obtain the filtrate.

[0029] (2) Put the obtained filtrate into a reaction kettle, and evaporate and concen...

Embodiment 2

[0033] A preparation method for anhydrous lithium iodide, the steps are as follows:

[0034] (1) Add 9L of pure water into the reactor, then add 7.8Kg of iodine element, stir for 10 minutes to dissolve completely, then add 2.5Kg of recrystallized lithium hydroxide, stir for 5 minutes, slowly add 80wt% hydrazine hydrate into the reactor Just turn into white (the consumption of 80wt% hydrazine hydrate is about 0.89Kg) until solution, stabilize 10 minutes, then add a small amount of iodine, just all turn red to solution, add a small amount of 5wt% hydrazine hydrate to just adjust the solution color back to white, Then use recrystallized lithium hydroxide solid to adjust the pH value to 8.0, heat, evaporate and concentrate to 125°C, and the volume is concentrated to 1 / 2 of the original volume, then cooled to room temperature with cold water, and filtered to obtain the filtrate.

[0035] (2) Put the obtained filtrate into a reaction kettle, and evaporate and concentrate under stirr...

Embodiment 3

[0039] A preparation method for anhydrous lithium iodide, the steps are as follows:

[0040] (1) Add 12L of pure water into the reactor, then add 8.75Kg of iodine element, stir for 15 minutes to dissolve completely, then add 2.8Kg of recrystallized lithium hydroxide, stir for 5 minutes, slowly add 80wt% hydrazine hydrate into the reactor Just turn into white (the consumption of 80wt% hydrazine hydrate is about 0.10Kg) until solution, stabilize for 10 minutes, then add a small amount of iodine, just all turn red to solution, add a small amount of 10wt% hydrazine hydrate to just adjust the solution color back to white, Then use recrystallized lithium hydroxide solid to adjust the pH value to 8.0, heat, evaporate and concentrate to 127°C, and concentrate the volume to 3 / 5 of the original volume, then cool to room temperature with cold water, and filter to obtain the filtrate.

[0041] (2) Put the obtained filtrate into a reaction kettle, and evaporate and concentrate under stirri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of electrolyte preparation of lithium battery electrolytic liquids, and particularly relates to a preparation method of anhydrous lithium iodide. The preparation method of anhydrous lithium iodide comprises the following steps of reacting iodine, hydrazine hydrate and lithium hydroxide by using an aqueous liquid method, sequentially carrying out evaporation and concentration, filtration, and heated concentration on the obtained product, feeding inert gas into the obtained product to dehydrate, and packaging the obtained product under the protection of the inert gas. No organic solvent is added in the whole process; and the method is simple in technological process and short in time consumption, and solves the problems that traditional production methods are long in time consumption, iodide lithium packages are deliquescent, and the like.

Description

technical field [0001] The invention relates to the technical field of electrolyte preparation for lithium battery electrolyte, in particular to a method for preparing anhydrous lithium iodide. Background technique [0002] Lithium iodide is commonly used in the photographic industry and the pharmaceutical industry and in the synthesis of related artificial crystals, as well as the catalytic dehydrogenation of hydrocarbons, and is also used as an electrolyte for high-temperature resistant and long-life batteries. In the process of preparing anhydrous lithium iodide, since anhydrous lithium iodide is easy to deliquesce, and it is easy to precipitate iodine simple substance and turn yellow when it is exposed to light or exposed to air, and it is easy to be oxidized when heated in air, so the preparation of anhydrous iodine The lithium iodide raw material is relatively difficult, and the packaging for anhydrous lithium iodide is also a problem. [0003] At present, the methods...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01D15/04
Inventor 吴满梅徐涛纪东海
Owner HUBEI BAIJIERUI ADVANCED MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com