Anti-static polyvinyl chloride foamed shoe material and preparation method thereof

A polyvinyl chloride and antistatic technology, applied in the field of polyvinyl chloride foamed shoe material and its manufacturing, can solve the problems of inability to use antistatic, poor antistatic performance, and high surface resistance, and achieve improved antistatic performance, good resistance to Electrostatic properties, effects of improving wettability and adhesion

Inactive Publication Date: 2015-01-07
SUZHOU JINGRO TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, ordinary polyvinyl chloride foam shoe materials have high surface resistance and poor antistatic performance, so they cannot be used in antistatic situations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static polyvinyl chloride foamed shoe material and preparation method thereof
  • Anti-static polyvinyl chloride foamed shoe material and preparation method thereof
  • Anti-static polyvinyl chloride foamed shoe material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of antistatic polyvinyl chloride foam shoe material, its parts by weight consist of:

[0028]

[0029] Its manufacturing method comprises the following steps:

[0030] (1) adding the nano-nickel powder into the oleic acid solution, ultrasonically oscillating for 40 minutes, washing with absolute ethanol and deionized water to neutrality, and drying in a vacuum oven for 1 hour to obtain the modified nano-nickel powder;

[0031] (2) Add the modified nano-nickel powder obtained by other components and step (1) into a kneader for heating and kneading, and discharge after kneading for 2.5 hours;

[0032] (3) Add the kneaded mixture into a twin-roller plastic mixer to masticate the pull sheet, and the mastication temperature is 125° C. to obtain the sheet material;

[0033] (4) The sheet material is sent into a hot press machine for heating and plasticizing, foaming, cooling and shaping after foaming, and obtaining a blank after demoulding;

[0034] (5) Send the b...

Embodiment 2

[0037] A kind of antistatic polyvinyl chloride foam shoe material, its parts by weight consist of:

[0038]

[0039] Its manufacturing method comprises the following steps:

[0040] (1) adding the nano-nickel powder into the oleic acid solution, ultrasonically oscillating for 40 minutes, washing with absolute ethanol and deionized water to neutrality, and drying in a vacuum oven for 1 hour to obtain the modified nano-nickel powder;

[0041] (2) Add the modified nano-nickel powder obtained by other components and step (1) into a kneader for heating and kneading, and discharge after kneading for 2.5 hours;

[0042] (3) Add the kneaded mixture into a twin-roller plastic mixer to masticate the pull sheet, and the mastication temperature is 125° C. to obtain the sheet material;

[0043] (4) The sheet material is sent into a hot press machine for heating and plasticizing, foaming, cooling and shaping after foaming, and obtaining a blank after demoulding;

[0044] (5) Send the b...

Embodiment 3

[0047] A kind of antistatic polyvinyl chloride foam shoe material, its parts by weight consist of:

[0048]

[0049] Its manufacturing method comprises the following steps:

[0050] (1) adding the nano-nickel powder into the oleic acid solution, ultrasonically oscillating for 40 minutes, washing with absolute ethanol and deionized water to neutrality, and drying in a vacuum oven for 1 hour to obtain the modified nano-nickel powder;

[0051] (2) Add the modified nano-nickel powder obtained by other components and step (1) into a kneader for heating and kneading, and discharge after kneading for 2.5 hours;

[0052] (3) Add the kneaded mixture into a twin-roller plastic mixer to masticate the pull sheet, and the mastication temperature is 125° C. to obtain the sheet material;

[0053] (4) The sheet material is sent into a hot press machine for heating and plasticizing, foaming, cooling and shaping after foaming, and obtaining a blank after demoulding;

[0054] (5) Send the b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an anti-static polyvinyl chloride foamed shoe material, comprising the following components in parts by weight: 40-55 parts of polyvinyl chloride, 30-40 parts of a plasticizer, 1-2 parts of a foaming agent, 5-15 parts of nano nickel powder, 6-10 parts of packing, 1-3 parts of a stabilizer, 0.6-1 part of a lubricating agent and 1-5 parts of ACR. The invention also discloses a preparation method of the anti-static polyvinyl chloride foamed shoe material. The anti-static performance of the anti-static polyvinyl chloride foamed shoe material provided by the invention is relatively good.

Description

Technical field: [0001] The invention relates to a shoe material, in particular to an antistatic polyvinyl chloride foamed shoe material and a manufacturing method thereof. Background technique: [0002] At present, most shoe materials on the market are synthetic rubber, including polyvinyl chloride, polyvinyl chloride foam material, PU, ​​EVA and so on. Among them, the heat insulation, sound insulation effect, flame retardancy, chemical stability and weather resistance of polyvinyl chloride foamed shoe materials are all good. Compared with ordinary polyvinyl chloride shoe materials, they are lighter and more comfortable to wear. The performance in all aspects is close to PU shoe material, but the cost is greatly reduced, so it occupies a certain proportion in the shoe material market. However, ordinary polyvinyl chloride foamed shoe materials have high surface resistance and poor antistatic performance, so they cannot be used in antistatic applications. Invention content...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/04C08K3/08C08K5/12C08J9/10A43B13/04
CPCC08L27/06A43B13/04C08J9/103C08J2203/04C08J2327/06C08K2201/001C08K2201/003C08K2201/011C08L2201/04C08L2205/03
Inventor 黄超
Owner SUZHOU JINGRO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com