Castables for continuous casting machine tundish

Abstract

The invention relates to a high-strength castable for a continuous caster tundish, which is prepared from the following components in parts by weight: 20-30 parts of magnesite, 10-20 parts of dolomite, 10-20 parts of zircon, 10-20 parts of graphite, 5-10 parts of phenol formaldehyde resin, 10-20 parts of zirconium oxide fiber and 5-10 parts of yttrium oxide. The magnesite, dolomite, zircon and graphite are mixed to obtain 45-50 parts by weight of particles and 50-55 parts by weight of fine powder; and the zirconium oxide fiber, yttrium oxide and phenol formaldehyde resin are used as additives. The particle size of the particles is 1.2-1.8mm, and the particle size of the fine powder is 0.3-0.8mm.

Description

Technical field: [0001] The invention belongs to the technical field of refractory materials, and in particular relates to a casting material for a tundish of a continuous casting machine. Background technique: [0002] Compared with qualitative refractory products, unshaped refractory materials represented by refractory castables have the advantages of short process flow, low production energy consumption and cost, convenient use, wide application range, integrity and good use effect, so they are widely used in the world. It has developed rapidly, and its proportion in the whole refractory material is getting higher and higher. In some countries with advanced refractory technology, the output of unshaped refractories has approached or even exceeded the output of shaped products. For example, the current output of unshaped refractory materials in Japan accounts for about 60% of the total refractory materials; that of the United States is about 50%; and that of countries suc...

AI Technical Summary

Problems solved by technology

The tundish smear uses inorganic binders, but its service life is short, the amount of water added is not easy to control, the construction and baking are complicated and the cycle is long, it is difficult to turn over the tundish, the labor intensity of the workers is high and the working conditions are harsh, and what is more serious is that if the baking If the degree is not enough, the water cannot be fully discharged, which will easily make the submerged nozzle damp and loose or even cause cracks, which will affect the quality of the slab