A kind of threaded steel bar for 785mpa high-strength prestressed structure and its preparation method

A technology of prestressed structure and threaded steel bar, which is applied in the field of metal material processing, can solve the problems of ferrite network structure in the core structure, unstable product performance, rapid change of hardness gradient, etc., and achieve the reduction of network ferrite structure. , The effect of significant grain refinement and slow change in hardness gradient

Active Publication Date: 2016-06-08
WUKUN STEEL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Micro-alloying + controlled cooling technology for the production of finished-rolled rebar. Due to the fact that there is no unified composition and process requirements in China, the hardness gradient of domestic finished-rolled rebar products changes rapidly, and the core tissue is prone to ferrite network structure, which leads to product damage. Unstable performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of threaded steel bar for 785mpa high-strength prestressed structure and its preparation method
  • A kind of threaded steel bar for 785mpa high-strength prestressed structure and its preparation method
  • A kind of threaded steel bar for 785mpa high-strength prestressed structure and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The preparation method of the 785MPa level high-strength prestressed structure threaded steel bar of the present invention comprises steel billet preparation, rolling, post-processing steps, specifically comprises:

[0018] A. Billet preparation:

[0019] 1) Melt iron converter smelting: chemical composition C3.8~4.8wt%, Si0.25~0.80wt%, Mn0.25~0.60wt%, P0.080~0.150wt%, S≤0.025wt%, the rest is Fe and unavoidable impurities of molten iron, chemical composition C0.15~0.30wt%, Si0.20~0.65wt%, Mn1.10~1.70wt%, P0.020~0.045wt%, S0.020~0.045wt% %, the rest is Fe and unavoidable impurities of steel scrap and chemical composition C3.2~3.8wt%, Si0.30~0.60wt%, Mn0.30~0.60wt%, P0.060~0.090wt%, S0 .020~0.035wt%, the rest is Fe and unavoidable impurities, and the pig iron is added to the LD converter for top-bottom compound blowing, and lime, dolomite, magnesite balls are added to make slag, and the amount of lime added is 30~40kg / t steel, the amount of dolomite added is 15~20kg / t ...

Embodiment 1

[0045] A, molten iron converter smelting: molten iron (chemical composition C3.8wt%, Si0.30wt%, Mn0.25wt%, P0.100wt%, S≤0.018wt%, the rest is Fe and unavoidable impurities), steel scrap (chemical composition C0.15wt%, Si0.20wt%, Mn1.10wt%, P0.020wt%, S0.020wt%, the rest is Fe and unavoidable impurities) and pig iron (chemical composition C3.2wt%, Si0 .35wt%, Mn0.30wt%, P0.050wt%, S0.020wt%, and the rest are Fe and unavoidable impurities) into the LD converter for conventional top-bottom composite blowing, adding conventional lime, dolomite, Magnesite ball slagging, the addition of lime is 30kg / t steel, the addition of dolomite is 15kg / t steel, the addition of magnesite balls is 4.0kg / t steel, the carbon content of the control end point is ≥0.10wt%, and the tapping temperature is 1610°C; before tapping, add active lime (activity degree ≥ 300ml) to the bottom of the ladle for slag washing, the amount of lime added is 2.0kg / t steel, the tapping process adopts the whole process of...

Embodiment 2

[0058] A, molten iron converter smelting: molten iron (chemical composition C4.3wt%, Si0.50wt%, Mn0.40wt%, P0.110wt%, S0.020wt%, the rest is Fe and unavoidable impurities), steel scrap ( Chemical composition C0.22wt%, Si0.41wt%, Mn1.40wt%, P0.032wt%, S0.030wt%, the rest is Fe and unavoidable impurities) and pig iron (chemical composition C3.5wt%, Si0. 50wt%, Mn0.45wt%, P0.075wt%, S0.027wt%, and the rest are Fe and unavoidable impurities) into the LD converter for conventional top-bottom compound blowing, adding conventional lime, dolomite, diamond Magnesium ball slagging, the addition of lime is 35kg / t of steel, the addition of dolomite is 17.5kg / t of steel, the addition of magnesite balls is 5.0kg / t of steel, the carbon content of the control end point is 0.14wt%, and the tapping temperature is 1620 ℃; Before tapping, add active lime (activity degree ≥ 300ml) to the bottom of the ladle for slag washing. The amount of lime added is 2.0kg / t steel. The tapping process adopts the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a twisted steel for a 785 MPa-level high-strength prestressed structure and a preparation method of the twisted steel. The twisted steel comprises following constituents in percentage by weight: 0.50-0.55% of C, 0.80-1.10% of Si, 1.00-1.30% of Mn, 0.060-0.12% of V, 0.60-0.95% of Cr, 0.0015-0.0040% of B, 0.010-0.025% of S, 0.010-0.025% of P, and the balance of Fe and unavoidable impurities. The preparation method comprises steps of billet preparation, rolling and after treatment. In the preparation process, when vanadium is utilized to conduct microalloying and reinforcement, the alloying element B is appropriately added to improve the steel hardenability, and the addition of the microalloying reinforcing elements is lowered. As the controlled rolling technology is combined and the cooling technology is applied, the grain refinement of steel structure is obvious, the net-like ferritic structure at the core of the steel is lowered, the steel strength is increased, the hardness gradient change is slow, and the stability of the precision rolled twisted steel is improved. The processed steel is stable in technologic and mechanical performances, and good in prestress relaxation performance.

Description

technical field [0001] The invention belongs to the technical field of metal material processing, and in particular relates to a threaded steel bar for 785MPa high-strength prestressed structures and a preparation method thereof. Background technique [0002] High-strength finish-rolled threaded steel bars for prestressed structures are referred to as finish-rolled threaded steel bars for short. It has the advantages of high strength, convenient and reliable connection, tensioning, and anchoring. It does not need cold drawing and welding during construction, and the construction is simple. Widely used in continuous beams and large frame structures of large-scale water conservancy, industrial and civil buildings, large and medium-span bridges for highways and railways, prestressed concrete structures such as nuclear power plants, and geotechnical anchorage projects. [0003] The traditional production process of finished rolled rebar usually adopts rolling + off-line heat tre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/32C22C33/04
CPCC22C33/04C22C38/02C22C38/04C22C38/12C22C38/18C22C38/32
Inventor 高勇张瑜王洁
Owner WUKUN STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More