Liquid crystal composition and liquid crystal display device comprising same
A liquid crystal composition and liquid crystal display technology, which are applied in the directions of liquid crystal materials, instruments, chemical instruments and methods, can solve the problems of incomplete theoretical explanations and changes in the performance of conventional liquid crystal parameters, and achieve good UV resistance, suitable dual The effect of refractive index anisotropy, moderate optical anisotropy Δn
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0074] Example 1
[0075]
[0076] step one
[0077] Add 189g (0.58mol) 2',3,5-trifluoro-4"-propyl-1,1'; 4',1"-terphenyl, 1.7L tetrahydrofuran, N2 protection in a 3L three-necked flask, and cool to- 70°C. Add 256ml (0.64mol) butyllithium dropwise, dropwise time 0.5h, control the temperature between -65-75℃, finish the dripping, keep for 0.5h, control the temperature between -65-75℃; drip 73.5 g(0.7mol) trimethyl borate, dripping time 0.5h, temperature control between -65-75℃, after dripping, keep for 1h, control temperature between -65-75℃.
[0078] The temperature rises naturally to -20°C. Pour the material liquid into the aqueous hydrochloric acid solution to pH 2, stir for 5 min, separate the liquids, wash the aqueous phase with 500ml×2 ethyl acetate, combine the organic phases, wash the organic phase with 800ml×2 water, and dry with anhydrous sodium sulfate.
[0079] Concentrate the solvent, heat 600ML petroleum ether to dissolve the product, reduce to room temperature, filter...
Example Embodiment
[0098] Example 2
[0099]
[0100] step 1
[0101] Add 10g (0.03mol) 2',3,5-trifluoro-4"-propyl-1,1'; 4',1"-terphenyl, tetrahydrofuran 120ml, nitrogen protection, and cool to -70 in a 1L three-necked flask ℃.
[0102] Add 14.4ml (0.036mol) of butyllithium dropwise, keep for 30 minutes after adding, add 3.3g of DMF dropwise, keep for 1 hour. The temperature was raised to -40°C naturally, the reaction solution was poured into 20 g hydrochloric acid and 100 mL water, and the liquid was separated. The aqueous phase was extracted with ethyl acetate 100 mL×2, washed with 150 mL×2, dried with anhydrous sodium sulfate, and spin-dried 15 g.
[0103] Add 30 g of petroleum ether to dissolve the product and recrystallize at -20°C, and filter with suction to obtain 9.8 g of product (2-a).
[0104] Step 2
[0105]
[0106] Add 9.8 g (0.028 mol) (2-a), 150 mL of methanol, and 50 mL of water to a 500 ml three-necked flask, add 3 g of potassium borohydride in batches, and the reaction solution is heat...
Example Embodiment
[0114] Example 3
[0115]
[0116]
[0117] Δε[1KHz,20℃]: 9.2
[0118] Δn[589nm,20℃]: 0.099
[0119] Cp: 72°C
[0120] γ 1 [25℃]: 53mPa.s
[0121] This liquid crystal composition has a moderate Δε, a moderate Δn, and a very low γ 1 , Suitable for fast response TN, IPS, FFS-TFT display liquid crystal materials.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap