Manufacturing method for fiberboard
A manufacturing method and fiberboard technology, applied in the field of fiberboard manufacturing, can solve the problems of hard surface, poor water resistance, complicated process, etc.
Inactive Publication Date: 2015-03-11
胡一鸿
View PDF7 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The disadvantage of fiberboard is that the board is warped and deformed due to the difference in expansion force after moisture absorption; the surface of hard board is hard, it is difficult to nail, and the water resistance is poor
Along with the growth of demand for man-made fiber boards in the domestic construction and decoration market and furniture manufacturing industry, in order to improve the comprehensive performance of man-made fiber boards, many methods have also appeared. For example, Chinese patent CN2320409Y just provides a kind of fiberboard. A technical solution to improve the static bending strength and elastic modulus, but, as in the Chinese patent CN2320409Y, the existing technical solutions for improving man-made fiber boards are often made after the man-made fiber boards are manufactured, and the man-made fiber boards are used as raw materials for secondary processing to obtain the final product , so there are problems such as high production cost and complicated process
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0012] In order to have a clearer understanding of the technical features, objects and effects of the present invention, the specific embodiments of the present invention will now be described with reference to the accompanying drawings. Wherein, the same parts use the same reference numerals.
[0013] figure 1 Shown is a schematic structural diagram of a fiberboard manufactured by a method according to a specific embodiment of the present invention, see figure 1 As shown, the present invention provides a method for manufacturing a fiberboard, the fiberboard includes a first base material layer 1 and a second base material layer 2 integrally formed by hot pressing, the first base material layer 1 and the second base material layer 1 A reinforcing layer 3 is arranged between the base material layers 2, the first base material layer 1 and the second base material layer 2 are made of wood fibers or plant fibers, and the reinforcing layer 3 includes a conductive carbon fiber mesh...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides a manufacturing method for a fiberboard. The method comprises the following steps: step A, preparing a wood or plant raw material into dry fibers; step B, paving a first-layer board blank by use of the fiber material in the step A, then paving a conductive carbon fiber net-shaped fabric on the first-layer board blank, and paving a second-layer board blank on the conductive carbon fiber net-shaped fabric; step C, performing hot pressing on the overall board blank obtained in the step B, thereby finishing manufacturing of the fiberboard. According to the manufacturing method for the fiberboard, the overall performance of an artificial fiberboard is greatly improved and the production cost is reduced.
Description
technical field [0001] The present invention relates to a manufacturing method of artificial board, in particular to a manufacturing method of fiberboard. Background technique [0002] Fiberboard, also known as density board, is a man-made board made of wood fiber or other plant fiber as raw material and applying urea-formaldehyde resin or other suitable adhesives. The development of fiberboard production is an effective way of comprehensive utilization of wood resources. The disadvantage of fiberboard is that the sheet is warped and deformed due to the difference in expansion force after moisture absorption; the surface of the hard sheet is hard, it is difficult to nail, and the water resistance is poor. With the growing demand for man-made fiberboard in the domestic building decoration market and furniture manufacturing industry, in order to improve the comprehensive performance of man-made fiberboard, many methods have emerged. The technical scheme of improving the stat...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/06
CPCB27N3/06
Inventor 姚越凡胡成孟钟韦红林成官
Owner 胡一鸿