Polyurethane self-endothermic low-temperature filling material and preparation method thereof

A technology of filling material and polyurethane, which is applied in the field of polyurethane self-absorbing low-temperature filling material and its preparation, can solve problems such as insufficient storage stability, foam crisp temperature, and high corrosiveness of raw materials, and solve problems such as poor flame retardancy, Easy transportation and good fluidity

Active Publication Date: 2015-03-25
SHANDONG INOV NEW MATERIALS CO LTD
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a polyurethane self-absorbing heat-absorbing low-temperature filling material, which solves the problems of traditional filling materials such as high corrosiveness of raw materials, irrita

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane self-endothermic low-temperature filling material and preparation method thereof
  • Polyurethane self-endothermic low-temperature filling material and preparation method thereof
  • Polyurethane self-endothermic low-temperature filling material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] The described polyurethane self-endothermic low-temperature filling material is prepared from the following components according to the following steps:

[0027] (1) Prepare 100Kg of component A, weigh 24.6Kg of polyether polyol a (3 functionality, molecular weight 3500, EO accounts for 15%), polyether polyol b (ethylenediamine with 4 functionality, molecular weight 350) polyether polyol) 36.7Kg, foam stabilizer (L6950, Momentive) 1.2Kg, water 24.6Kg, pentamethyldiethylenetriamine 0.3Kg, dimethylaminoethoxyethanol 0.3Kg, water-soluble Flame retardant (FR425, Suzhou Anhongtai) 12.3Kg, put the weighed polyether polyol and water into the mixing kettle and stir, then add the weighed foam stabilizer, catalyst and flame retardant, and then add the reaction In the kettle, stir evenly at room temperature, and after passing the sampling test, it can be loaded into barrels.

[0028] (2) prepare 100Kg of component B material, put accurately metered polymethyle...

Example Embodiment

[0030] Example 2

[0031] The described polyurethane self-endothermic low-temperature filling material is prepared from the following components according to the following steps:

[0032] (1) Prepare 100Kg of component A, weigh 23.5Kg of polyether polyol a (3 functionality, molecular weight 6000, EO accounts for 25%), polyether polyol b (ethylenediamine with 4 functionality, molecular weight 430) base polyether polyol) 19.3Kg, foam stabilizer (B8532, Evonik Degussa) 0.8Kg, water 42.7Kg, pentamethyldiethylenetriamine 0.2Kg, trimethylenediamine 0.3Kg, dimethyl Aminoethoxyethanol 0.4Kg, water-soluble flame retardant (FR425, Suzhou Anhongtai) 12.8Kg, put the weighed polyether polyol and water into the mixing kettle and stir, and then add the weighed foam stabilizer , catalyst and flame retardant are added to the reaction kettle in turn, stirred evenly at room temperature, and can be loaded into barrels after passing the sampling test.

[0033] (2) Prepare 100Kg of component B, a...

Example Embodiment

[0035] Example 3

[0036] The described polyurethane self-endothermic low-temperature filling material is prepared from the following components according to the following steps:

[0037] (1) Prepare 100Kg of component A, weigh 24.5Kg of polyether polyol a (3 functionality, molecular weight 5000, EO accounts for 15%), polyether polyol b (ethylenediamine with 4 functionality, molecular weight 350) base polyether polyol) 24.5Kg, foam stabilizer (L6970, Momentive, USA) 1Kg, water 44.1Kg, dimethylaminoethoxyethanol 1Kg, water-soluble flame retardant (FR425, Suzhou Anhongtai) 4.9Kg, Put the weighed polyether polyol and water into the mixing kettle and stir, then add the weighed foam stabilizer, catalyst and flame retardant, add them to the reaction kettle in turn, stir evenly at room temperature, and after sampling and testing are qualified, Can be filled.

[0038] (2) prepare 100Kg of component B material, put accurately metered polymethylene polyphenyl polyisocyanate 44V20 (Bay...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of preparation of polyurethane materials, and particularly relates to a polyurethane self-endothermic low-temperature filling material and a preparation method thereof. The polyurethane self-endothermic low-temperature filling material consists of a component A and a component B, wherein the component A consists of polyol, water, an auxiliary agent and a fire retardant; the component B consists of polyisocyanate and a fire retardant. The polyol, the auxiliary agent, the fire retardant and the polyisocyanate are selected, a large amounts of water is added into a reaction system, and heat generated by the reaction system is taken away through evaporation of the unreacted water, so that the internal reaction temperature is not higher than 95 DEG C and the problem of poor fire retardance is solved at a time; the polyurethane self-endothermic low-temperature filling material is good in fire retardance, and liquid raw material is convenient to transport, low in viscosity, good in fluidity and good in storage stability; the raw material is environment-friendly and pollution-free, does not contain a volatile solvent, does not produce any toxic gas, and is harmless to a human body; the preparation method is simple and easy to implement.

Description

technical field [0001] The invention belongs to the technical field of polyurethane material preparation, and in particular relates to a polyurethane self-absorbing heat low-temperature filling material and a preparation method thereof. Background technique [0002] With the large-scale mining of coal mines in my country, it is often encountered that the roadway and the roof of the coal mining face are under high pressure, the top coal is broken, and the problem of collapse occurs during the excavation process, and then the filling material is injected into the upper cavity of the roof caving area, and then the roadway surrounding Grouting reinforcement, excavation and mining will be carried out after the roof of the roadway has fallen and the surrounding rock at the side is reinforced; on the other hand, the cavity in the goaf is likely to accumulate gas and cause explosion hazards, so the goaf needs to be filled. At present, phenolic materials, urea-formaldehyde materials o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/76C08G18/50C08G18/48C08K5/521C08G101/00
CPCC08G18/482C08G18/4829C08G18/5024C08G18/7664C08K5/521C08G2110/0083
Inventor 郝德开张丽唐国涛王超边宪磊
Owner SHANDONG INOV NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap