Heat-resistant abrasion-resistant double-phase stainless steel casting alloy material

A technology of duplex stainless steel and casting alloy, applied in the field of steel alloy materials, can solve the problems of excessive corrosion, grate wear, grate fracture, etc. The effect of wear and corrosion resistance

Inactive Publication Date: 2015-03-25
XINGHUA SPECIAL STAINLESS STEEL INST OF SHANGHAI UNIV
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The grate in the grate incinerator technology is the main key vulnerable part of this technology. It has been in the environment of high temperature, erosion and high chloride ion corrosion for a long time. At present, quite a few manufacturers use heat-resistant austenitic materials. After a certain period of time Excessive wear and corrosion of the grate during operation will easily lead to the breakage of the grate, and failure to shut down in time will cause equipment accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistant abrasion-resistant double-phase stainless steel casting alloy material
  • Heat-resistant abrasion-resistant double-phase stainless steel casting alloy material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] In this embodiment, the composition and mass percentage of the heat-resistant and wear-resistant duplex stainless steel cast steel material are as follows:

[0018] Cr 27.0

[0019] Ni 4.8

[0020] Mo 0.70

[0021] C 0.35

[0022] Nb 0.30

[0023] Mn 0.51

[0024] V 0.05

[0025] Si 1.2

[0026] S 0.002

[0027] P 0.002

[0028] Fe balance

[0029] The traditional conventional smelting process method is adopted, after comprehensive measurement calculation and ingredient smelting, casting and molding, and finally duplex stainless steel castings are obtained. After solid solution at 1000-1200°C and aging treatment at 700-900°C, a good metallographic microstructure can be obtained. See for example figure 1 As shown, its tensile strength at room temperature is greater than 500 MPa, and its elongation is greater than 20%. The material has good wear resistance and corrosion resistance in the temperature range o...

Embodiment 2

[0031] In this embodiment, the composition and mass percentage of the heat-resistant and wear-resistant duplex stainless steel cast steel material are as follows:

[0032] Cr 25.5

[0033] Ni 4.3

[0034] Mo 0.60

[0035] C 0.25

[0036] Nb 0.50

[0037] Mn 0.82

[0038] V 0.10

[0039] N 0.15

[0040] Si 1.10

[0041] S 0.003

[0042] P 0.003

[0043] Fe balance

[0044] The traditional conventional smelting process method is adopted, after comprehensive measurement calculation and ingredient smelting, casting and molding, and finally duplex stainless steel castings are obtained. After solid solution at 1000-1200°C and aging treatment at 700-900°C, a good metallographic microstructure can be obtained. See for example figure 2 As shown, its tensile strength at room temperature is greater than 500 MPa, and its elongation is greater than 20%. The material has good wear resistance and corrosion resistance in the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Room temperature tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heat-resistant abrasion-resistant double-phase stainless steel casting alloy material, and belongs to the technical field of steel and iron alloy materials. The heat-resistant abrasion-resistant double-phase stainless steel casting alloy material comprises the following components in percentage by mass: 0.15-0.45% of C, 25.0-28.0% of Cr, 4.0-6.0% of Ni, 0.5-1.0% of Mo, 0.05-1.5% of Nb, less than or equal to 1.0% of Mn, less than or equal to 1.5% of Si, less than or equal to 0.03% of P, less than or equal to 0.03% of S, less than or equal to 0.5% of C+N, less than or equal to 1.5% of Nb+V, and the balance of Fe and inevitable impurities. A solid-solution structure of the steel in the component range comprises ferrite and austenite, wherein the austenite accounts for 40-60%, the room-temperature tensile strength is 500-700 MPa, and the elongation percentage is more than 20%. The alloy material is prepared by a conventional smelting process method comprising the following steps: smelting ingredients, performing cast molding, performing solid-solution treatment at 1000-1200 DEG C and aging treatment at 700-900 DEG C, and performing mechanical processing. The alloy material has very good abrasion resistance at 650-950 DEG C and is a relatively good candidate material for manufacturing a mechanical grate for a garbage power station.

Description

technical field [0001] The invention relates to a heat-resistant and wear-resistant duplex stainless steel casting alloy material, which belongs to the technical field of iron and steel alloy materials. Background technique [0002] Duplex stainless steel cast steel plays a very important role in the development and application of wear-resistant and corrosion-resistant cast steel, especially in the fields of petrochemical and marine engineering. [0003] As cities grow bigger and bigger, the disposal of domestic waste becomes increasingly serious. Currently, municipal solid waste is mainly disposed of by landfill and incineration for power generation. Waste incineration power generation is mainly divided into two technologies: circulating fluidized bed incinerator and grate incinerator according to different incinerator technologies. The grate furnace technology directly incinerates garbage, has low requirements on the quality and composition of garbage, simple pre-treatme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/48
Inventor 肖学山张娇娇李钧徐裕来冉庆选彭伟张华伟吉利文
Owner XINGHUA SPECIAL STAINLESS STEEL INST OF SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com