Low-density and moderate-strength oil fracturing propping agent and preparing method thereof

A fracturing proppant, low-density technology, applied in chemical instruments and methods, earthwork drilling, and fluid production, can solve problems such as low production efficiency in shallow low-permeability oil and gas fields, achieve good appearance and prevent powder removal , The effect of high crush resistance

Active Publication Date: 2015-04-01
LUOYANG INST OF SCI & TECH +1
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problem of low production efficiency in the production of medium-shallow low-permeability oil and gas fields, the present invention provides a low-density, medium-strength petroleum fracturing proppant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] A low-density medium-strength petroleum fracturing proppant, made of powder and 4% silica sol by weight. According to the weight ratio, the powder is made of 85 parts of raw bauxite, 5 parts of molybdenum tailings, and 2 parts The bentonite is mixed with 2 parts of composite additives, in which the particle size of raw bauxite and molybdenum ore tailings is less than 0.044mm, and the fineness of bentonite is less than 0.074mm;

[0029] According to the weight ratio, the composite additive is composed of 1 part of manganese oxide powder and 1 part of nickel-iron slag powder, and the particle sizes of the manganese oxide powder and the nickel-iron slag powder are both less than 0.074 mm.

[0030] The preparation method of the aforementioned low-density medium-strength petroleum fracturing proppant includes the following steps:

[0031] 1) According to the above requirements, each material is weighed and pulverized to the corresponding particle size, and then th...

Example Embodiment

[0036] Example 2

[0037] A low-density medium-strength petroleum fracturing proppant, made of powder and 4% silica sol by weight. According to the weight ratio, the powder is made of 90 parts of raw bauxite, 8 parts of molybdenum tailings, and 3 parts The bentonite is mixed with 5 parts of composite additives, in which the particle size of raw bauxite and molybdenum ore tailings is less than 0.044mm, and the fineness of bentonite is less than 0.074mm;

[0038] According to the weight ratio, the composite additive is composed of 3 parts of manganese oxide powder and 2 parts of ferronickel slag powder, and the particle sizes of the manganese oxide powder and ferronickel slag powder are both less than 0.074 mm.

[0039] The preparation method of the aforementioned low-density medium-strength petroleum fracturing proppant includes the following steps:

[0040] 1) According to the above requirements, each material is weighed and pulverized to the corresponding particle size, and then the ...

Example Embodiment

[0045] Example 3

[0046] A low-density medium-strength petroleum fracturing proppant, which is made of powder and 4% silica sol by weight. According to the weight ratio, the powder is made of 87.5 parts of raw bauxite, 6.5 parts of molybdenum tailings, and 2.5 parts The bentonite is mixed with 3.5 parts of composite additives, wherein the particle size of raw bauxite and molybdenum ore tailings is less than 0.044mm, and the fineness of bentonite is less than 0.074mm;

[0047] According to the weight ratio, the composite additive is composed of 2 parts of manganese oxide powder and 1.5 parts of nickel-iron slag powder, and the particle sizes of the manganese oxide powder and the nickel-iron slag powder are both less than 0.074 mm.

[0048] The preparation method of the aforementioned low-density medium-strength petroleum fracturing proppant includes the following steps:

[0049] 1) According to the above requirements, each material is weighed and pulverized to the corresponding partic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Finenessaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a low-density and moderate-strength oil fracturing propping agent and a preparing method thereof, and belongs to the technical field of oil-gas well fracturing in oil production. The low-density and moderate-strength oil fracturing propping agent is made of powder and a silica solution accounting for four percent of the weight of the oil fracturing propping agent. The powder is formed by mixing, by weight, 85-90 parts of raw bauxite, 5-8 parts of molybdenum ore gangue, 2-3 parts of bentonite and 2-5 parts of composite additive. The molybdenum ore gangue and the composite additive composed of manganese oxide powder and ferronickel slag powder are added, good balance is obtained between obvious propping agent density reduction and certain strength keeping, the developed oil propping agent has good comprehensive performance, it is ensured that the propping agent has considerable strength, the firing temperature of the propping agent is reduced, the purposes of saving energy and reducing consumption are achieved, the wasted mineral is fully utilized, and waste resources are repeatedly utilized.

Description

technical field [0001] The invention relates to a solid proppant for oil and gas well fracturing technology, in particular to a low-density and medium-strength petroleum fracturing proppant and a preparation method thereof. Background technique [0002] Currently, the so-called hydraulic fracturing technology is widely used in deep well exploitation of oil and gas. This technology uses a high-pressure pump set on the ground to continuously inject high-viscosity fracturing fluid into the oil well through the wellbore, so that the lower part of the oil well forms a high pressure. With the continuous injection of fracturing fluid, the pressure also continues to rise. When the tensile strength and formation stress of the formation rock near the wellbore wall are less than the pressure formed by the fracturing fluid, fractures will occur in the formation near the bottom of the well. When the fracturing fluid carrying proppant continues to be injected, the fractures in the ro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K8/80
CPCC09K8/80
Inventor 廖桂华张国强李忠孝王黎张国弘
Owner LUOYANG INST OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap